ASTM A335 P9 Alloy Steel Pipes

Our company stands tall among the eminent Manufacturers, Exporters and Suppliers of ASTM A335 P9 Alloy Steel Pipes. These are manufactured in compliance with set industrial norms. We maintain a large stock of the pipes in our spacious warehouse in order to meet the bulk and urgent requirements of the buyers.

Details :

ASTM A335 P9 is the part of ASTM A335, The pipe shall be suitable for bending, flanging, and similar forming operations, and for fusion welding. The steel material shall conform to chemical composition, tensile property, and hardness requirements.
Each length of pipe shall be subjected to the hydrostatic test. Also, each pipe shall be examined by a non-destructive examination method in accordance to the required practices.
The range of ASTM A335 P9 pipe sizes that may be examined by each method shall be subjected to the limitations in the scope of the respective practice.

The different mechanical test requirements for pipes, namely, transverse or longitudinal tension test, flattening test, and hardness or bend test are presented.Both ends of each crate will indicate the order no., heat no., dimensions, weight and bundles or as requested.
- Outer Dimensions : 19.05mm – 114.3mm
- Wall Thickness : 2.0mm – 14 mm
- Length : max 16000mm

Packing : Bare packing/bundle packing/crate packing/wooden protection at the both sides of tubes and suitably protected for sea-worthily delivery or as requested.

Inspection and Test : Chemical Composition Inspection, Mechanical Properties Test(Tensile Strength, Yield Strength, Elongation, Flaring, Flattening, Bending, Hardness, Impact Test), Surface and Dimension Test, No-destructive Test, Hydrostatic Test.

Surface treatment :
- Oil-dip, Varnish, Passivation, Phosphating, Shot Blasting.
- Both ends of each crate will indicate the order no., heat no., dimensions, weight and bundles or as requested.

Material & Manufacture : Pipe may be either hot finished or cold drawn with the finishing heat treatment noted below.
Heat Treatment
- A / N+T
- N+T / Q+T
- N+T
Mechanical Tests Specified :
- Transverse or Longitudinal Tension Test and Flattening Test, Hardness Test, or Bend Test
- For material heat treated in a batch-type furnace, tests shall be made on 5% of the pipe from each treated lot. For small lots, at least one pipe shall be tested.
- For material heat treated by the continuous process, tests shall be made on a sufficient number of pipe to constitute 5% of the lot, but in no case less than 2 pipe.

Notes for Bend Test :
- For pipe whose diameter exceeds NPS 25 and whose diameter to wall thickness ratio is 7.0 or less shall be subjected to the bend test instead of the flattening test.
- Other pipe whose diameter equals or exceeds NPS 10 may be given the bend test in place of the flattening test subject to the approval of the purchaser.
- The bend test specimens shall be bent at room temperature through 180 without cracking on the outside of the bent portion.

ASTM A335 P9 Chemical Compositions(%)

Compositions	Data
UNS Designation	K41545
Carbon(max.)	0.15
Manganese	0.30-0.60
Phosphorus(max.)	0.025
Silicon(max.)	0.50
Chromium	4.00-6.00
Molybdenum	0.45-0.65
Other Elements	…

Mechanical Properties for ASTM A335 P9

Properties	Data
Tensile strength, min, (MPa)	415 Mpa
Yield strength, min, (MPa)	205 Mpa
Elongation, min, (%), L/T	30/20

View Complete Details

Ask Latest Price & Details

ASTM A335 P11 Alloy Steel Pipes

We are counted among the successful Manufacturers, Exporters and Suppliers of ASTM A335 P11 Alloy Steel Pipes. These are suitable for bending, flanging, and similar forming operations, and for fusion welding. We hold the expertise to deliver bulk orders of these owing to our excellent logistics network.

Details :

ASTM A335 P5 is the part of ASTM A335, The pipe shall be suitable for The steel material shall conform to chemical composition, tensile property, and hardness requirements.
Each length of pipe shall be subjected to the hydrostatic test. Also, each pipe shall be examined by a non-destructive examination method in accordance to the required practices.
The range of ASTM A335 P5 pipe sizes that may be examined by each method shall be subjected to the limitations in the scope of the respective practice.

The different mechanical test requirements for pipes, namely, transverse or longitudinal tension test, flattening test, and hardness or bend test are presented.Both ends of each crate will indicate the order no., heat no., dimensions, weight and bundles or as requested.
- Outer Dimensions : 19.05mm – 114.3mm
- Wall Thickness : 2.0mm – 14 mm
- Length : max 16000mm
Packing : Bare packing/bundle packing/crate packing/wooden protection at the both sides of tubes and suitably protected for sea-worthily delivery or as requested.
Inspection and Test : Chemical Composition Inspection, Mechanical Properties Test(Tensile Strength, Yield Strength, Elongation, Flaring, Flattening, Bending, Hardness, Impact Test), Surface and Dimension Test, No-destructive Test, Hydrostatic Test.
Surface Treatment :
- Oil-dip, Varnish, Passivation, Phosphating, Shot Blasting.
- Both ends of each crate will indicate the order no., heat no., dimensions, weight and bundles or as requested.
Material & Manufacture : Pipe may be either hot finished or cold drawn with the finishing heat treatment noted below.
Heat Treatment
- A / N+T
- N+T / Q+T
- N+T
Mechanical Tests Specified :
- Transverse or Longitudinal Tension Test and Flattening Test, Hardness Test, or Bend Test
- For material heat treated in a batch-type furnace, tests shall be made on 5% of the pipe from each treated lot. For small lots, at least one pipe shall be tested.
- For material heat treated by the continuous process, tests shall be made on a sufficient number of pipe to constitute 5% of the lot, but in no case less than 2 pipe.
- Notes for Hardness Test : P11 shall not have a hardness not exceeding 250 HB/265 HV [25HRC].
Notes for Bend Test :
- For pipe whose diameter exceeds NPS 25 and whose diameter to wall thickness ratio is 7.0 or less shall be subjected to the bend test instead of the flattening test.
- Other pipe whose diameter equals or exceeds NPS 10 may be given the bend test in place of the flattening test subject to the approval of the purchaser.
- The bend test specimens shall be bent at room temperature through 180 without cracking on the outside of the bent portion.

ASTM A335 P11 Chemical Compositions(%)

Compositions	Data
UNS Designation	K11597
Carbon	0.05-0.60
Manganese	0.30-0.60
Phosphorus(max.)	0.025
Sulfur(max.)	0.025
Silicon	0.50-1.00
Nickel	…
Chromium	1.00-1.50
Molybdenum	0.44-0.65
Other Elements	…

Mechanical Properties for ASTM A335 P11

Properties	Data
Tensile strength, min, (MPa)	415 Mpa
Yield strength, min, (MPa)	205 Mpa
Elongation, min, (%), L/T	30/20

View Complete Details

Ask Latest Price & Details

ASTM A335 P22 Alloy Steel Pipes

We are enlisted among the reputed Manufacturers, Exporters and Suppliers of ASTM A335 P22 Alloy Steel Pipes. Our pipes are accredited for their excellent quality, long functional life and flawless performance. Buyers are free to place bulk orders of the pipes with us and we ensure their timely execution.

Details :

ASTM A335 P22 is the part of ASTM A335, The pipe shall be suitable for bending, flanging, and similar forming operations, and for fusion welding. The steel material shall conform to chemical composition, tensile property, and hardness requirements.
Each length of pipe shall be subjected to the hydrostatic test. Also, each pipe shall be examined by a non-destructive examination method in accordance to the required practices.
The range of ASTM A335 P22 pipe sizes that may be examined by each method shall be subjected to the limitations in the scope of the respective practice.

The different mechanical test requirements for pipes, namely, transverse or longitudinal tension test, flattening test, and hardness or bend test are presented.Both ends of each crate will indicate the order no., heat no., dimensions, weight and bundles or as requested.
- Outer Dimensions : 19.05mm – 114.3mm
- Wall Thickness : 2.0mm – 14 mm
- Length : Max 16000mm
Packing : Bare packing/bundle packing/crate packing/wooden protection at the both sides of tubes and suitably protected for sea-worthily delivery or as requested.
Inspection and Test : Chemical Composition Inspection, Mechanical Properties Test(Tensile Strength, Yield Strength, Elongation, Flaring, Flattening, Bending, Hardness, Impact Test), Surface and Dimension Test, No-destructive Test, Hydrostatic Test.
Surface Treatment :
- Oil-dip, Varnish, Passivation, Phosphating, Shot Blasting.
- Both ends of each crate will indicate the order no., heat no., dimensions, weight and bundles or as requested.
Material & Manufacture :Pipe may be either hot finished or cold drawn with the finishing heat treatment noted below.
Heat Treatment
- A / N+T
- N+T / Q+T
- N+T
Mechanical Tests Specified :
- Transverse or Longitudinal Tension Test and Flattening Test, Hardness Test, or Bend Test
- For material heat treated in a batch-type furnace, tests shall be made on 5% of the pipe from each treated lot. For small lots, at least one pipe shall be tested.
- For material heat treated by the continuous process, tests shall be made on a sufficient number of pipe to constitute 5% of the lot, but in no case less than 2 pipe.
Notes for Hardness Test : P11 shall not have a hardness not exceeding 250 HB/265 HV [25HRC].

Notes for Bend Test :
- For pipe whose diameter exceeds NPS 25 and whose diameter to wall thickness ratio is 7.0 or less shall be subjected to the bend test instead of the flattening test.
- Other pipe whose diameter equals or exceeds NPS 10 may be given the bend test in place of the flattening test subject to the approval of the purchaser.
- The bend test specimens shall be bent at room temperature through 180 without cracking on the outside of the bent portion.

ASTM A335 P11 Chemical Compositions(%)

Compositions	Data
UNS Designation	K21590
Carbon	0.05-0.15
Manganese	0.30-0.60
Phosphorus(max.)	0.025
Sulfur(max.)	0.025
Silicon	0.50-1.00
Nickel	…
Chromium	1.90-2.60
Molybdenum	0.87-1.13
Other Elements	…

Mechanical Properties For ASTM A335 P11

Properties	Data
Tensile strength, min, (MPa)	415 Mpa
Yield strength, min, (MPa)	205 Mpa
Elongation, min, (%), L/T	30/20

View Complete Details

Ask Latest Price & Details

ASTM A335 P12 Alloy Steel Pipes

Our company stands tall among the established Manufacturers, Exporters and Suppliers of ASTM A335 P12 Alloy Steel Pipes. These are manufactured in adherence with set industrial norms. The steel used to manufacture the pipes conform to chemical composition, tensile property, and hardness requirements. We offer the pipes at competitive rates.

Material & Manufacture :Pipe may be either hot finished or cold drawn with the finishing heat treatment noted below.
Heat Treatment
- A / N+T
- N+T / Q+T
- N+T
Mechanical Tests Specified of ASTM A335 P12
- Transverse or Longitudinal Tension Test and Flattening Test, Hardness Test, or Bend Test
- For material heat treated in a batch-type furnace, tests shall be made on 5% of the pipe from each treated lot. For small lots, at least one pipe shall be tested.
- For material heat treated by the continuous process, tests shall be made on a sufficient number of pipe to constitute 5% of the lot, but in no case less than 2 pipe.

Chemical Properties

UNS Designation	K11562
Carbon	0.05–0.15
Manganese	0.30–0.61
Phosphorus(max)	0.025
Sulfur(max)	0.025
Silicon	0.50 max
Chromium	0.80–1.25
Molybdenum	0.44–0.65
Others	. . .

Mechanical Properties

Tensile strength, min, (MPa)	585
Yield strength, min, (MPa)	415
Elongation, min, (%), L/T	20/…

View Complete Details

Ask Latest Price & Details

ASTM A335 P91 Alloy Steel Pipes

Our company is counted among the eminent Manufacturers, Exporters and Suppliers of ASTM A335 P91 Alloy Steel Pipes. We make use of excellent quality steel to manufacture the pipes, which conforms to chemical composition, tensile property, and hardness requirements. Bulk orders of these are processed by us as per the specific requirements of the buyers.

Details :

ASTM A335 P91 is the part of ASTM A335, The pipe shall be suitable for bending, flanging, and similar forming operations, and for fusion welding. The steel material shall conform to chemical composition, tensile property, and hardness requirements.
Each length of pipe shall be subjected to the hydrostatic test. Also, each pipe shall be examined by a non-destructive examination method in accordance to the required practices.
The range of ASTM A335 P91 pipe sizes that may be examined by each method shall be subjected to the limitations in the scope of the respective practice.

The different mechanical test requirements for pipes, namely, transverse or longitudinal tension test, flattening test, and hardness or bend test are presented.Both ends of each crate will indicate the order no., heat no., dimensions, weight and bundles or as requested.
- Outer Dimensions : 19.05mm – 114.3mm
- Wall Thickness : 2.0mm – 14 mm
- Length : max 16000mm
Packing : Bare packing/bundle packing/crate packing/wooden protection at the both sides of tubes and suitably protected for sea-worthily delivery or as requested.
Inspection and Test : Chemical Composition Inspection, Mechanical Properties Test(Tensile Strength, Yield Strength, Elongation, Flaring, Flattening, Bending, Hardness, Impact Test), Surface and Dimension Test, No-destructive Test, Hydrostatic Test.
Surface Treatment : Oil-dip, Varnish, Passivation, Phosphating, Shot Blasting.Both ends of each crate will indicate the order no., heat no., dimensions, weight and bundles or as requested.
Material & Manufacture :Pipe may be either hot finished or cold drawn with the finishing heat treatment noted below.
Heat Treatment
- A / N+T
- N+T / Q+T
- N+T
Mechanical Tests Specified :
- Transverse or Longitudinal Tension Test and Flattening Test, Hardness Test, or Bend Test
- For material heat treated in a batch-type furnace, tests shall be made on 5% of the pipe from each treated lot. For small lots, at least one pipe shall be tested.
- For material heat treated by the continuous process, tests shall be made on a sufficient number of pipe to constitute 5% of the lot, but in no case less than 2 pipe.
Notes for Bend Test :
- For pipe whose diameter exceeds NPS 25 and whose diameter to wall thickness ratio is 7.0 or less shall be subjected to the bend test instead of the flattening test.
- Other pipe whose diameter equals or exceeds NPS 10 may be given the bend test in place of the flattening test subject to the approval of the purchaser.
- The bend test specimens shall be bent at room temperature through 180 without cracking on the outside of the bent portion.

ASTM A335 P91 Chemical Compositions(%)

Compositions	Data
UNS Designation	K91560
Carbon(max.)	0.08-0.12
Manganese	0.30-0.60
Phosphorus(max.)	0.025
Silicon(max.)	0.50
Chromium	4.00-6.00
Molybdenum	0.45-0.65
Other Elements	…

Mechanical Properties for ASTM A335 P91

Properties	Data
Tensile strength, min, (MPa)	415 Mpa
Yield strength, min, (MPa)	205 Mpa
Elongation, min, (%), L/T	30/20

View Complete Details

Ask Latest Price & Details

ASTM A335 P5 Alloy Steel Pipes

We are reckoned among the reliable Manufacturers, Exporters and Suppliers of ASTM A335 P5 Alloy Steel Pipes. The Steel Pipes The pipes offered by us are undergo numerous tests based on parameters like longitudinal tension test, flattening test, and hardness or bend test before the final dispatch. One can obtain these at nominal rates.

Details :

ASTM A335 P5 is the part of ASTM A335, The pipe shall be suitable for bending, flanging, and similar forming operations, and for fusion welding. The steel material shall conform to chemical composition, tensile property, and hardness requirements.
Each length of pipe shall be subjected to the hydrostatic test. Also, each pipe shall be examined by a non-destructive examination method in accordance to the required practices.
The range of ASTM A335 P5 pipe sizes that may be examined by each method shall be subjected to the limitations in the scope of the respective practice.

The different mechanical test requirements for pipes, namely, transverse or longitudinal tension test, flattening test, and hardness or bend test are presented. Both ends of each crate will indicate the order no., heat no., dimensions, weight and bundles or as requested.
- Outer Dimensions : 19.05mm – 114.3mm
- Wall Thickness : 2.0mm – 14 mm
- Length : max 16000mm
Packing : Bare packing/bundle packing/crate packing/wooden protection at the both sides of tubes and suitably protected for sea-worthly delivery or as requested.
Inspection and Test : Chemical Composition Inspection, Mechanical Properties Test(Tensile Strength, Yield Strength, Elongation, Flaring, Flattening, Bending, Hardness, Impact Test), Surface and Dimension Test, No-destructive Test, Hydrostatic Test.
Surface Treatment :
- Oil-dip, Varnish, Passivation, Phosphating, Shot Blasting.
- Both ends of each crate will indicate the order no., heat no., dimensions, weight and bundles or as requested.

Material & Manufacture : Pipe may be either hot finished or cold drawn with the finishing heat treatment noted below.
Heat Treatment
- A / N+T
- N+T / Q+T
- N+T

Mechanical Tests Specified :
- Transverse or Longitudinal Tension Test and Flattening Test, Hardness Test, or Bend Test
- For material heat treated in a batch-type furnace, tests shall be made on 5% of the pipe from each treated lot. For small lots, at least one pipe shall be tested.
- For material heat treated by the continuous process, tests shall be made on a sufficient number of pipe to constitute 5% of the lot, but in no case less than 2 pipe.

Notes for Bend Test :
- For pipe whose diameter exceeds NPS 25 and whose diameter to wall thickness ratio is 7.0 or less shall be subjected to the bend test instead of the flattening test.
- Other pipe whose diameter equals or exceeds NPS 10 may be given the bend test in place of the flattening test subject to the approval of the purchaser.
- The bend test specimens shall be bent at room temperature through 180 without cracking on the outside of the bent portion.

ASTM A335 P5 Chemical Compositions(%)