Our Products
Mortar
2 Products availableMineral Ores
1 Products availableWe offer the best product range of Conventional Castables Whytheat K, Firecrete Normal (UE/FCN), Firecrete Super (UE/FCS), Whytheat C (UE/WC) and Conventional Castables Firecrete Normal.
TECHNICAL SPECIFICATIONS
Description | Units | UE/WK |
---|---|---|
Service Temp. | ˚C | 1550 |
Refractoriness | ˚C | 1800 |
D.C.B.D. | gm/cc | 2.2 |
Linear change % @1400˚C | 3 Hrs | ± 1.0 |
Alumina(Al₂O₃) | % | 60 |
Ferric(Fe₂O₃) | % | 2.0 |
Grain size | Mm | 0-5 |
*C.C.S.@110˚C | kg/cm² (Min) | 300 |
Water Reqd. | % @20˚C | 12-15 |
TECHNICAL SPECIFICATIONS
Description | UE/AC |
---|---|
Al₂O₃ % min | 45-50 |
Fe₂O₃ % max | 3-4 |
CaO % max | - |
*C.C.S Kg/cm² (Min) | - |
*D.C.B.D. gm/cc | - |
Ser. Temp. ˚C | 1700 |
Grade | Normal/Fine |
Additional Information:
Packaging Details : These castables come in packing of 50 kg bags with polythene liners.
Technical Specification
Description | Units | UE/FCN |
---|---|---|
Service Temp | oC | 1400 |
Refractoriness | oC | 1450 |
*D.C.B.D. | gm/cc | 2.1 |
Linear Change % @1400oC | 3-Hrs | ± 1.0 |
Alumina(Al2O3) | % | 45 |
Ferric(Fe2O3) | % | 3-5 |
Grain Size | Mm | 0-5 |
*C.C.S.@110oC | kg/cm2 (Min) | 250 |
Water Reqd. | % @20oC | 12-15 |
*D.C.B.D.-Dry Cast Bulk Density;*C.C.S-Cold Crushing Strength;*P.L.C-Permanent Linear Change Note : Above are average test data, subject to reasonable variation. Tailor made composition can be made on specific request to any specification. |
Technical Specification
Description | Units | UE/FCS |
---|---|---|
Service Temp | oC | 1450 |
Refractoriness | oC | 1500 |
*D.C.B.D. | gm/cc | 2.4 |
Linear Change % @1400oC | 3-Hrs | ±1.0 |
Alumina(Al2O3) | % | 60-65 |
Ferric(Fe2O3) | % | 3-5 |
Grain Size | Mm | 0-5 |
*C.C.S.@110oC | kg/cm2 (Min) | 300 |
Water Reqd. | % @20oC | 12-15 |
*D.C.B.D.-Dry Cast Bulk Density;*C.C.S-Cold Crushing Strength;*P.L.C-Permanent Linear Change Note : Above are average test data, subject to reasonable variation. Tailor made composition can be made on specific request to any specification. |
Technical Specification
Description | Units | UE/WC |
---|---|---|
Service Temp | oC | 1500 |
Refractoriness | oC | 1550 |
*D.C.B.D | gm/cc | 2.1 |
Linear Change % @1400oC | 3-Hrs | ± 1.0 |
Alumina(Al2O3) | % | 50 |
Ferric(Fe2O3) | % | 2.0 |
Grain Size | mm | 0-5 |
*C.C.S.@110oC | kg/cm2 (Min) | 300 |
Water Reqd. | %@20oC | 12-15 |
*D.C.B.D.-Dry Cast Bulk Density;*C.C.S-Cold Crushing Strength;*P.L.C-Permanent Linear Change Note : Above are average test data, subject to reasonable variation. Tailor made composition can be made on specific request to any specification. |
TECHNICAL SPECIFICATIONS
Description | Units | UE/FCN |
---|---|---|
Service Temp. | ˚C | 1400 |
Refractoriness | ˚C | 1450 |
D.C.B.D. | gm/cc | 2.1 |
Linear change % @1400˚C | 3 Hrs | ± 1.0 |
Alumina(Al₂O₃) | % | 45 |
Ferric(Fe₂O₃) | % | 3-5 |
Grain size | Mm | 0-5 |
*C.C.S.@110˚C | kg/cm² (Min) | 250 |
Water Reqd. | % @20˚C | 12-15 |
Technical Specification
Description | Units | UE/WA |
---|---|---|
Service Temp | oC | 1700 |
Refractoriness | oC | 1750 |
*D.C.B.D | gm/cc | 2.7 |
Linear Change % @1400oC | 3-Hrs | ± 1.0 |
Alumina(Al2O3) | % | 90 |
Ferric(Fe2O3) | % | 0.90 |
Grain Size | mm | 0-5 |
*C.C.S.@110oC | kg/cm2 (Min) | 600 |
Water Reqd. | %@20oC | 9-10 |
*D.C.B.D.-Dry Cast Bulk Density;*C.C.S-Cold Crushing Strength;*P.L.C-Permanent Linear Change Note : Above are average test data, subject to reasonable variation. Tailor made composition can be made on specific request to any specification. |
Technical Specification
Description | Units | UE/WK |
---|---|---|
Service Temp | oC | 1550 |
Refractoriness | oC | 1800 |
*D.C.B.D | gm/cc | 2.2 |
Linear Change % @1400oC | 3-Hrs | ± 1.0 |
Alumina(Al2O3) | % | 60 |
Ferric(Fe2O3) | % | 2.0 |
Grain Size | mm | 0-5 |
*C.C.S.@110oC | kg/cm2 (Min) | 300 |
Water Reqd. | %@20oC | 12-15 |
*D.C.B.D.-Dry Cast Bulk Density;*C.C.S-Cold Crushing Strength;*P.L.C-Permanent Linear Change Note : Above are average test data, subject to reasonable variation. Tailor made composition can be made on specific request to any specification. |