| Material | polypropylene(pp) | Color | White |
|---|---|---|---|
| Georgette Style | Non Woven | Length x Width | 2.1mtrX50mtr Meter (m) |
| Thickness | 5.5 Millimeter (mm) | Application | Typical applications Site : Roads RE Wall , Levelling and mechanical protection of the geomembrane; drainage of the accidental leaks below primary ; leachate and rain water collection above primary geomembrane; mechanical protection of the geomembranes when in contact with waste-materials and/or soil; drainage of liquids and gases present in the soil above and/or below the capping geomembrane. |
| In-situ soil passing | Permittivity, per sec ASTM D | Maximum Apparent Opening Size, mm as |
| 0.075 mm sieve(%) | 4491/ IS 14324 : 1995 | per ASTM D4751/ IS 14294 : 1995 |
|---|---|---|
| < 15 | 0.5 | 0.43 |
| 15 to 50 | 0.2 | 0.2 |
| > 50 | 0.1 | 0.22 |
| Property | Test method | Units | Minimum average Roll value |
| Tensile strength | EN ISO 10319 | kN/m | 16 |
|---|---|---|---|
| CBR Puncture Resistance | EN ISO 12236 | N | 3000 |
| Mass per unit area | EN ISO 9864 | g/m2 | 710 |
| Thickness of Composite | EN ISO 9863 | mm | 4.5 |
| In-plane permeability | |||
| (Hydraulic Gradient, i=1 at 100 kPa pressure) | EN ISO 12958 | l/m | 0.55 |
| Hydraulic Gradient, i=1 at 200 kPa pressure | EN ISO 12958 | l/m | 0.45 |
| Property | Particulars | Specification |
| Weight | 45-180 GSM | |
|---|---|---|
| Mesh Size | 2.5 x2.5 mm | |
| Density | (WARP/MD) (WEFT/CMD) |
10 10 |
| Breaking Strength ( N | (WARP/MD) (WEFT/CMD) |
700 700 |
| MassPerUnitArea(GSM) | 50 | |
| Length Per Roll Size ( mtr.) | 50 | |
| Standard Width ( mm ) | 1000 | |
| Coating | Acrylic | |
| Weave | Leno |
| SL. NO. | Characteristic | Unit | Specification |
|---|---|---|---|
| 1. | Tensile Strength | Kgf /cm2 | 300 min |
| 2. | Elongation at Break | % | 300 Min. |
| 3. | Carbon Black Content | % | 2.5±0.5 |
| 4. | Carbon Black dispersion | Dispersion analyzer | Satisfactory |
| 5. | Density | Gm/cc | 0.950±0.015 |
| 6. | Tear Resistance | N | 230 Min. |
| 7. | Punctual Resistance | N | 450 Min. |
| 8. | Chemical Resistance 30% H2so4for 7 days | ||
| A. | T .S. | % | ±241 |
| B. | E.B. | % | -25 |
| 9. | Ozone Resistance | visual | No Cracks |
| 10 | Water Absorption | % | 0.05 Max |
| SL. NO. | Characteristic | Unit | Specification |
|---|---|---|---|
| 1. | Tensile Strength | Kgf /cm2 | 140 min |
| 2. | Elongation at Break | % | 200 Min. |
| 3. | Dart Impact Load | Gf | 120 Min.(Normal) |
| 4. | Carbon Black dispersion | % | 20.5±0.5 |
| 5. | Carbon Black dispersion | Dispersion analyzer | No Crack |
| 6. | Density | Gm/cc | 0.992 to 0.937 |
| 7. | Tear Resistance | N/mm2 | 9.5 Min. |