1 Products availableLeading Manufacturer, Supplier & Retailer of 2024 T3 Aluminium Alloy Plate, 2024 T3 Aluminium Alloy Blocks, Aluminium Rectangular Bars, 7050 T7451 Aluminium Alloy Plates and tantalum plates.
With latest machines and technology, we ensure that the raw material used is as per the globally accepted standards and meet the international standards. We deliver the quality products that are manufactured using the best raw material. Owing to our wide distribution network and the fastest transit system, buyers can receive their orders on timely basis.
Alloy QQ-A-200/3 is supplied in a range of tempers :
Chemical Composition Of Aluminium Alloys 2024 Bare Sheet
Silicon | 0.5 |
---|---|
Iron | 0.5 |
Copper | 3.8-4.9 |
Manganese | 030.-0.9 |
Magnesium | 1.2-1.8 |
Chromium | 0.1 |
Zinc | 0.25 |
Mechanical Properties Of Aluminium Alloys 2024 Bare Sheet
Diameter (mm) | Proof Strength (Min) | Tensile Strength (Min) | Elongation % (Min) |
---|---|---|---|
Up to & incl. 6.25mm | 290 | 393 | 12 |
Over 6.3mm up to & incl. 19mm | 303 | 414 | 12 |
Over 19mm up to & incl. 38mm | 317 | 448 | 10 |
Over 38mm | 358 | 483 | 10 |
Physical Properties Of Aluminium Alloys 2024 Bare Sheet
Physical Property | Value |
---|---|
Density | 2.74 g/cm3 |
Melting Point | 640oC |
Thermal Expansion | 23.1 x10^-6 /K |
Modulus of Elasticity | 73 GPa |
Thermal Conductivity | 121 W/m.K |
Electrical Resistivity | 30 % IACS |
Owing to our wide distribution network and the fastest transit system, buyers can receive their orders on timely basis. Rest assured us for the quality of all products we deliver as the inputs used commensurate to international set standards and thus, the products are remarkable and meet your satisfaction level.
Available shapes : Flats, squares and rounds
Tempers : T351, T3511 & T4
Specifications : ASTM B211, AMS 4120, AMS 4339, AMS-QQ-A-225/6, ASTM B221, AMS 4152, AMS 4164, AMS 4165, AMS-QQ-A-200/3
Typical Chemical Composition %
Weight % | Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti | Each | Total |
---|---|---|---|---|---|---|---|---|---|---|
Minimum | - | - | 3.8 | 1.2 | 0.3 | - | - | - | - | - |
Maximum | 0.5 | 0.5 | 4.9 | 1.8 | 0.9 | 0.1 | 0.25 | 0.15 | 0.05 | 0.15 |
Typical Mechanical Properties
Temper | Tensile | Hardness | ||||
Ultimate | Yield | Elongation | Brinell | |||
KSI | MPA | KSI | MPA | % | ||
T4, T351 | 68 | 469 | 47 | 324 | 19 | 120 |
Sourced from trustworthy vendors, our entire lot of raw materials has been cross checked against varied quality parameters before using them in the production process. We efficiently cater to the varied demands of the clients and offer them personalized packaging options as well. We ensure that the products are packed sternly using quality packaging material to evade loss.
Main applications : high resistance structural parts for mechanical industry, aviation, military, motorbike and automotive.
According to EU directives : 2000/53/CE (ELV) - 2011/65/EU (RoHS II)
Properties :
Additional Information:
Delivery Time : 5 Days
Production Program
Unit: mm | Round | Squere | Rectangular |
---|---|---|---|
Drawn | 25 ÷ 76,2 | - | |
Extruded | 30 ÷ 254 | 50 ÷ 165 | Thick 30 ÷ 127 |
Chemical Composition
Si | < 0,40 |
---|---|
Fe | < 0,50 |
Cu | 1,20 ÷ 2,00 |
Mn | < 0,30 |
Mg | 2,10 ÷ 2,90 |
Cr | 0,18 ÷ 0,28 |
Ni | - |
Zn | 5,10 ÷ 6,10 |
Ti | < 0,20 |
Pb | - |
Bi | - |
Others | Each 0,05 Total 0,15 |
Al | Remainder |
Physical Properties
Density | Kg / dm3 | 2,80 |
---|---|---|
Modulus of elasticity | MPa | 72 |
Coefïcient of thermal expansion | X10-6 / oC | 23,5 |
Thermal conductivity at 20oC | W / mk | 130 |
Typical electrical resistivity at 20oC | Ω mm2 / m | 52 |
Mechanical Properties
Temper | Diam. mm | Rm MPa | Rp0, MPa | A% | HBW Typical | |
---|---|---|---|---|---|---|
Drawn | T6 | ≤ 80 | 540 | 485 | 7 | 150 |
T651 | ≤ 80 | 540 | 485 | 5 | 150 | |
T73 | ≤ 80 | 455 | 385 | 10 | 135 | |
T7351 | ≤ 80 | 455 | 385 | 8 | 135 | |
Extruded | T6, T6510, T6511 | ≤ 100 | 560 | 500 | 7 | 150 |
T6, T6510, T6511 | 100 < D ≤ 150 | 550 | 440 | 5 | 150 | |
T6, T6510, T6511 | 150 < D ≤ 200 | 440 | 400 | 5 | 150 | |
T73, T73510, T73511 | ≤ 75 | 475 | 405 | 7 | 135 | |
T73, T73510, T7351 | 75 < D ≤ 100 | 470 | 390 | 6 | 135 | |
T73, T73510, T7351 | 100 < D ≤ 150 | 440 | 360 | 6 | 135 |
We are instrumental in offering the exceptional assortment of product that are deigned and manufactured only after complete examination of the raw materials and inputs used. Being a quality-conscious firm, we ensure that the offered products comply with the laid industry standards and are of supreme quality.
Subcategory : 7000 Series Aluminum Alloy; Aluminum Alloy; Metal; Nonferrous Metal Composition Notes : Aluminum content reported is calculated as remainder. Composition information provided by the Aluminum Association and is not for design.
Key Words : AA7050-T7451; AA7070-T73651, UNS A97050; ISO AlZn6CuMgZr; Aluminium 7050-T7451; Aluminium 7070-T73651
Specification
Component | Wt. % | Component | Wt. % | Component | Wt. % |
---|---|---|---|---|---|
Al | 87.3 - 90.3 | Si | Max 0.12 | Mg | 1.9 - 2.6 |
Cr | Max 0.04 | Ti | Max 0.06 | Mn | Max 0.1 |
Cu | 38750 | Zn | 5.7 - 6.7 | Other, each | Max 0.05 |
Fe | Max 0.15 | Zr | 0.08 - 0.15 | Other, total | Max 0.15 |
Technical Specification
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 2.83g/cc | 0.102lb/in3 | AA; Typical |
Mechanical Properties
Hardness, Brinell | 140 | 140 | 500 kg load with 10 mm ball. Calculated value. |
---|---|---|---|
Hardness, Knoop | 177 | 177 | Converted from Brinell Hardness Value |
Hardness, Rockwell A | 51.6 | 51.6 | Converted from Brinell Hardness Value |
Hardness, Rockwell B | 84 | 84 | Converted from Brinell Hardness Value |
Hardness, Vickers | 162 | 162 | Converted from Brinell Hardness Value |
Ultimate Tensile Strength | 524MPa | 76000psi | AA; Typical |
Tensile Yield Strength | 469MPa | 68000psi | AA; Typical |
Elongation at Break | 0.11 | 0.11 | AA; Typical; 1/2 in. (12.7 mm) Diameter |
Modulus of Elasticity | 71.7GPa | 10400ksi | AA; Typical; Average of tension and compression. Compression modulus is about 2% greater than tensile modulus. |
Poisson's Ratio | 0.33 | 0.33 | |
Fracture Toughness | 28MPa-m1/2 | 25.5ksi-in1/2 | K(IC) in S-L Direction |
Fracture Toughness | 31MPa-m1/2 | 28.2ksi-in1/2 | K(IC) in T-L Direction |
Fracture Toughness | 35MPa-m1/2 | 31.9ksi-in1/2 | K(IC) in L-T Direction |
Shear Modulus | 26.9GPa | 3900ksi | |
Shear Strength | 303MPa | 44000psi | AA; Typical |
Electrical Properties
Electrical Resistivity | 4.3e-006 ohm-c m | 4.3e-006ohm-cm |
Thermal Properties
CTE, linear 68oF | 23µm/m-oC | 12.8µin/in-oF | AA; Typical; Average over 68-212oF range. |
---|---|---|---|
CTE, linear 250oC | 25.4µm/m-oC | 14.1µin/in-oF | Average over the range 20-30oC |
Specific Heat Capacity | 0.86J/g-oC | 0.206BTU/lb-oF | - |
Thermal Conductivity | 157W/m-K | 1090BTU-in/hr-ft²-oF | - |
Melting Point | 488 - 629oC | 910 - 1165oF | AA; Typical range based on typical composition for wrought products 1/4 inch thickness or greater |
Solidus | 488oC | 910oF | AA; Typical |
Liquidus | 629oC | 1165oF | AA; Typical |
Processing Properties
Annealing Temperature | 413oC | 775oF |
---|---|---|
Solution Temperature | 477oC | 890oF |
Aging Temperature | 121 - 177oC | 250 - 350oF |