1 Products availableWe offer a complete product range of Aluminium Sheets, 5754 H111H22h32O Aluminium Alloy Temper Sheets and 2024T3 Aluminum Alloy Sheets
we make available, high-quality aluminium sheets, which are dimensionally stable and have a high tensile strength. these aluminium sheets are commonly used from industrial applications and can be availed in different shapes and sizes.
aluminium alloys 7075 bare plates specifications : uns a97075, aluminum 7075, 7075 alloy, 7075 aluminum alloy, aa7075 aluminium alloys 7075 bare plates
available forms : 7075 aluminum sheet, 7075 aluminum plate, 7075
aluminum bar temper : 7075-0, 2014-t6, 7075-t73, 7075-t76, 7075-t651, 7075-t7351, 7075-t7651
Additional Information:
Payment Terms : L/C, T/T
Delivery Time : 5 Days
Chemical Element
Chemical Element | % Present |
---|---|
Silicon (Si) | 0.0 - 0.40 |
Iron (Fe) | 0.0 - 0.50 |
Copper (Cu) | 1.20 - 2.00 |
Manganese (Mn) | 0.0 - 0.30 |
Magnesium (Mg) | 2.10 - 2.90 |
Chromium (Cr) | 0.18 - 0.28 |
Zinc (Zn)) | 5.10 - 6.10 |
Titanium (Ti) | 0.0 - 0.20 |
Other (Each) | 0.0 - 0.05 |
Others (Total) | 0.0 - 0.15 |
Aluminium (Al) | Balance |
Mechanical Properties Of Aluminium Alloys 7075 Bare Plates
Diameter (mm) | Proof Strength (Min) | Tensile Strength (Min) | Elongation % (Min) |
---|---|---|---|
Up to & incl. 6.3 | 400 | 469 | 7 |
Over 6.3 up to & incl. 38 | 420 | 483 | 8 |
Over 38 up to & incl. 76.2 | 407 | 476 | 8 |
Over 76.2 up to & incl. 114 | 393 | 469 | 7 |
Physical Properties Of Aluminium Alloys 7075 Bare Plates
Density | 2.81 g/cm3 |
---|---|
Melting Point | 635oC |
Thermal Expansion | 23.5 x10^-6 /K |
Modulus of Elasticity | 72 GPa |
Thermal Conductivity | 134-160 W/m.K |
Electrical Resistivity | 40 % IACS |
From Mumbai(India), we are providing a lot of products having quality and cost-effective prices. We have parted our infrastructure into several units and one of them is warehouse wherein we keep a huge stock for furnishing urgent and quick requirements of the clients.
Applications 5754 is typically used in : Treadplate Shipbuilding Vehicle bodies Rivets Fishing industry equipment Food processing Welded chemical and nuclear structures Alloy.
Designations Alloy 5754 also corresponds to the following standard designations and specifications but may not be a direct equivalent :
Chemical Composition
Element | % Present |
---|---|
Magnesium (Mg) | 2.60 - 3.60 |
Manganese + Chromium (Mn+Cr) | 0.10 - 0.60 |
Manganese (Mn) | 0.0 - 0.50 |
Silicon (Si) | 0.0 - 0.40 |
Iron (Fe) | 0.0 - 0.40 |
Chromium (Cr) | 0.0 - 0.30 |
Zinc (Zn) | 0.0 - 0.20 |
Titanium (Ti) | 0.0 - 0.15 |
Others (Total) | 0.0 - 0.15 |
Copper (Cu) | 0.0 - 0.10 |
Other (Each) | 0.0 - 0.05 |
Aluminium (Al) | Balance |
Generic Physical Properties
Property | Value |
---|---|
Density | 2.66 g/cm3 |
Melting Point | 600oC |
Thermal Expansion | 24 x10-6 /K |
Modulus of Elasticity | 68 GPa |
Thermal Conductivity | 147 W/m.K |
Electrical Resistivity | 0.049 x10-6 Ω .m |
Mechanical Properties
Property | Value |
---|---|
Proof Stress | 60 Min MPa |
Tensile Strength | 160 - 200 MPa |
Elongation A50 mm | 12 Min % |
Hardness Brinell | 44 HB |
We believe in keeping transparency in the transactions and thus we offer an invoice to the clients stating all the necessary details. We undertake both online and offline payment processing methods. Be it packaging small or large consignments, light or heavy products, we use the finest material to provide cost efficient and sustainable packaging solutions.
Temper Types Alloy QQ-A-200/3 is supplied in a range of tempers : T3 - Solution heat treated, cold worked and naturally aged T8511 - Solution heat treated, stress-relieved by stretching then artificially aged T3511 - Solution heat treated and stress-relieved by stretching. Equivalent to T4 condition.
Chemical Composition Of Aluminium Alloys 2024 Bare Sheet
Silicon | 0.5 |
---|---|
Iron | 0.5 |
Copper | 3.8-4.9 |
Manganese | 030.-0.9 |
Magnesium | 1.2-1.8 |
Chromium | 0.1 |
Zinc | 0.25 |
Mechanical Properties Of Aluminium Alloys 2024 Bare Sheet
Diameter (mm) | Proof Strength (Min) | Tensile Strength (Min) | Elongation % (Min) |
---|---|---|---|
Up to & incl. 6.25mm | 290 | 393 | 12 |
Over 6.3mm up to & incl. 19mm | 303 | 414 | 12 |
Over 19mm up to & incl. 38mm | 317 | 448 | 10 |
Over 38mm | 358 | 483 | 10 |
Physical Properties Of Aluminium Alloys 2024 Bare Sheet
Physical Property | Value |
---|---|
Density | 2.74 g/cm3 |
Melting Point | 640oC |
Thermal Expansion | 23.1 x10^-6 /K |
Modulus of Elasticity | 73 GPa |
Thermal Conductivity | 121 W/m.K |
Electrical Resistivity | 30 % IACS |