1 Products availableWe are leaders in the market for providing best range of PHENOLIC MODIFIED ALKYD RESINS, Cardanol Phenolic Resin, Cashew Nut Shell Liquid Resin, Bhilawan Nut Shell Liquid Resin and Oil Modified Polyurethane Resin
PRODUCT: ALKYD MODIFIED CARDANOL RESIN (70%)
CODE: SILKYD 110 (70%)
INTRODUCTION: Silkyd 110are Cardphenol modified with Long Oil Alkyd based Phenolic Resins. The Rosinated Alkyds are very popular in the Paint Industry. They were introduced primarily to reduce costs and to improve the drying time. But these advantages are gained at the cost of sharp deterioration of the properties of the original Alkyd particularly its chemical & water resistance & outdoor durability properties. Keeping these in consideration we have developed these resins. It reduces the drying time, improve the resistance to chemical & water & outdoor durability, yet the cost is lower than the Alkyds. They are Golden yellow in colour and are suitable for Semi Dark colored & Semi Light colored Synthetic hard glossy enamels, Furniture enamels, Insulating varnishes having outstanding film properties.
The Cardphenol Resins are reacted with Alkyds and have both ester & ether linkages in the structure. They exhibit outstanding Water, Alkali & Chemical Resistance combined with excellent weather resistance particularly because the modifying methylol is based on Phenol. The C-15 aliphatic chain further improves the flexibility and water resistance of the resultant polymer.
They are clear transparent and comparatively pale resins and are uniquely suitable for base formulations of synthetic enamels of superior quality with improved outdoor durability.
Comparative Film Properties:
| Film Properties | Silkyd 110 | 66% oil length Long oil Alkyd Resin | Rosinated Alkyds 70% |
| Colour | Pale Golden Yellow | Very Light Pale | Pale Yellow |
| Hard Dry Time (Tack Free) | 3 - 3.5 hours | 4 - 6 hours | 4 - 5 hours |
| Appearance | Highly glossy | Highly Glossy | Highly Glossy |
| Scratch Hardness | 1000 gms | 600 gms | 800 gms |
| Adhesion | Good | Good | Satisfactory |
| Flexibility | Good | Better | Good |
| Resistance to Water Sodium Carbonate 5% Sulphuric Acid 2% White Spirits Linseed Oil Outdoor Weather Resistance Corrosion Resistance |
NE (100) NE (75) NE (100) NE (100) NE (100) Good Excellent |
SB (8) SB (25) SB (48) NE (100) SB (100) Excellent Fair |
NE (100) SB (25) SB (8) SB (50) SB (100) Fair Fair |
Abbreviations: NE (No Effect), SB (Slight Blushing), SE (Slight Effect)
( ) Figures within brackets indicate the number of hours tested.
Additional Information:
Payment Terms : D/P, T/T
Packaging Details : PACKED IN MILD STEEL DRUMS OF 200 KGS NET EACH
Delivery Time : 3-5 DAYS
some of our most popular grades are as follows :
Additional Information:
Payment Terms : T/T,
Packaging Details : PACKED IN MILD STEEL DRUMS OF 200 KGS NET
Delivery Time : 3-5 DAYS
Properties Of Cardanol Based Resins
| Phenolic component | Formaldehyde Phenol Mole Ratio | Catalyst | Physical Appearance | Melting Point Durran Deg. C | Gel time with DCO at 250 Deg. C | Solubility in | |||||
| Linseed Oil | White Spirit | Xylene | Alcohol | Acetone | Butanol | ||||||
| Cardanol | 0.0007094907 | Ammonia | Clear reddish soft solid | 97-98 | 7 min | S | S | S | I | S | S |
| Cardanol | 0.0007094907 | Sodium Hydroxide | Clear reddish highly viscous liquid | Viscous liquid | 5 min | S | S | S | I | S | S |
| Cardanol | 0.0007048611 | Oxalic Acid | Clear reddish highly viscous liquid | Viscous liquid | No Gelation for 3 hrs. | S | S | S | I | S | S |
| Cardanol+Phenol (1:1 Mole) | 0.0007094907 | Ammonia | Clear light reddish Solid | 110-112 | 5 min | S | S | S | I | S | S |
| Cardanol+Phenol (1:1 Mole) | 0.0007094907 | Sodium Hydroxide | * Reddish brown clear viscous liquid | Liquid | 5 min | S | S | S | I | S | S |
| Cardanol+Phenol (1:1 Mole) | 0.0423611111 | Oxalic Acid | Viscous liquid with Solid separation | Liquid | No Gelation for 3 hrs. | S | S | S | I | S | S |
| Cardanol+para tertiary butyl phenol (1:1 Mole) | 0.0007094907 | Ammonia | Clear reddish Solid | 88-90 | 5 min. | S | S | S | I | S | S |
| Cardanol+para tertiary butyl phenol (1:1 Mole) | 0.0007094907 | Sodium Hydroxide | * Reddish brown viscous liquid | Liquid | 5 min. | S | S | S | I | S | S |
| Cardanol+para tertiary butyl phenol (1:1 Mole) | 0.0423611111 | Oxalic Acid | Reddish brown clear viscous liquid | Liquid | No Gelation for 3 hrs. | S | S | S | I | S | S |
presently we are making the following grades of resins based on cnsl (reddish brown in colour) & cardanol (golden yellow in colour) :
Properties Of CNSL
| Appearance | Dark Brown Liquid |
|---|---|
| Specific Gravity @ 30°C | 0.92 – 0.96 |
| Viscosity @ 30°C | 50 – 200 cps |
| Ash Content (%) | 1% (Max.) |
| Moisture Content | 2% (Max.) |
| Insolubles in Toluene (%) | 1% (Max.) |
| Acid Value (mgmKOH/gm) | < 20 |
| Hydroxyl Value (mgmKOH/gm) | 170-250 |
| Iodine Value (WIJS) | 220 – 270 |
| Saponification Value | 18 – 30 |
| Specification of CNSL | IS-840 is the BIS specification for CNSL. |
These resins are mostly recommended for making Black Stoving enamel paints, Ship Bottom paints, Anti Corrosive Black, Bituminous Black, Black Japan etc.
Features:
Additional Information:
Payment Terms : T/T
Packaging Details : PACKED IN EXPORT WORTHY MILD STEEL DRUMS OF 190/200 KGS NET
Delivery Time : 3-5 DAYS
Single Pack Polyurethane
| Code No. | Description and Appearance | Solid Content | Viscosity@ 50% Solids B-4 cup Seconds | Hard dry with driers (30%) Solution in MTO | Scratch Hardness Air Dried Gms. | Resistance to Water and Chemicals | Max. Acid Value | Suggested Applications | |
| In Air Hrs | At 120°C Mts. | ||||||||
| 4.1 SILAC U 210 | Urethane Oil Varnish Single Pack Yellow Light Pale | 50±2% | 120 to 150 | 15 Min. | 4 | ≤1500 | Excellent | <1 free NCO <.01% | Very Fast Drying Paints With High Scratch Hardness, Gloss/Excellent Water/Chemical and Abrasion Resistance, Wood Lacquers and High Class Insulating Varnishes etc., |
| 4.2 SILAC U 220 | Urethane Oil Varnish Single Pack very Light Pale | 50±2% | 120 to 150 | 20 Min. | 4 | ≥1500 | Excellent | <1 free NCO <.01% | Same as above but with better Non-Yellowing properties |
| 4.3 SILAC U 230 | Urethane Oil Alkyd varnish Golden Yellow | 50±2% | 150 to 200 | 45 Min. | 8 | ≥1000 | Excellent | <5 free NCO <.01% | Fast drying alkyd with better Chemical/Water Resistance for Super Enamels, Hammertone Finishes and Wood Lacquers |
we are manufacturing various types & grades of cnsl based resins for the application in paints, primers, anti corrosive coatings, enamel paints, insulating varnishes etc.,
.
Additional Information:
Payment Terms : T/T,
Packaging Details : PACKED IN MILD STEEL DRUMS OF 200 KGS NET
Delivery Time : 3-5 DAYS
Technical Write-Up of Silex-50 Plain CNSL Phenolic Resin
Introduction: Silex-50 is a Plain Cashew Nut Shell Liquid based Phenolic resins and is processed using special catalyst to cater to the need of various dark & semi dark coloured quick drying paints and primers. The resins has got both air drying and baking properties and is suitable for making high gloss dark & semi dark coloured paints, primers, anti-termite chemicals and varnishes, Black offset printing inks, Insulating Varnishes of outstanding properties particularly in regard to resistance to the water and chemical.
Compatibility: Silex-50 is compatible with all Drying oils, Alkyds, Epoxies, Ester gums, Phenolics, Maleics etc., in all proportion and only to a limited extent in chlorinated resins specially chlorinated rubber. It is not compatible with urea resins.
Solubility: Silex-50 is soluble in Mineral Turpentine oil (MTO) in all proportion. It is also soluble in most of the common paints solvent like Toluene, Xylene, Naphthas, Ester etc., but having limited solubility in Epoxies, vinyl & ethyl ketones.
Recommended Driers: Driers such as 0.5% lead or 0.5% cobalt and 1.5% Manganese as metal on the solid resin content is recommended. If require the proportion of Manganese can be increased to further 1.0% with beneficial effects. After addition of driers ageing for 24 hours is recommended.
Mode of Supply: It is supplied in 200 kgs packings as 100%, 80%, and 70% solids. For most of the paints and varnishes applications 70% execution is recommended as it has the best film properties & flowable from drums.
Application Technique:Film of Silex-50 can be applied either by brush, spray or flow technique.
Storage: The storage stability is Silex-50 is satisfactory for 6 months or more if stored in air tight containers in a cool place.
Recommended uses: Silex-50 either alone or in combination with other resins and used for formulating primers, dark coloured enamels and paints, insulating varnishes, knifing putty, Black offset Printing inks and similar other applications including special purpose anti corrosive paints baking composition etc.
Caution: Some times Silex-50 may be used along with basic pigment like Zinc Chrome,
Zinc Oxide, basic lead sulphate etc. It is advised that these pigments are not ground along
with the main pigment in the CNSL resin as there is a possibility of reaction. The reactive
pigments should be added after the grinding for proper dispersion of the Pigment. Hence it
is advisable to grind the main pigments with any Long Oil Alkyd Resin and then add our
CNSL resin outside and stir well to avoid reaction.
Additional Information:
Payment Terms : T/T,
Packaging Details : PACKED IN MILD STEEL DRUMS CONTAINING 200 KGS NET MATERIAL
Delivery Time : 3-5 DAYS
Pure Phenolics
| Code No. | Description and Appearance | Solid Content | Viscosity@ 50% Solids B-4 cup Seconds | Hard dry with driers (30%) Solution in MT | Scratch Hardness Air Dried Gms. | Resistance to Water and Chemicals | Max. Acid Value | Suggested Applications | |
| In Air Hrs. | At 120°C Mts. | ||||||||
| 1.1 SILEX 50 | CNSL Fromaldehyde Viscous Reddish Brown Resin |
100±2% | 80 to 100 | 3.5 | 20 | 900 | Very Good | 5 | Semi Dark & Darker Enamels, Redoxide, Zinc Chrome Primers, Baking Compositions, Putty Glossy & Matty Red Oxide Paints, Anti Corrosive Black Paints, Insulating Varnishes Etc., |
| 80±2% | 100 to 120 | 3 | 20 | ||||||
| 65±2% | 120 to 180 | 2.5 | 15 | ||||||
| 1.2 SILAC V 10 | 45±2% | 180 to 250 | 2.5 | 20 | 1000 | Very Good | 5 | ||
| 1.3 SILEX 55 | Styrenated Cardphenol Formaldehyde clear golden yellow viscous liquid resin | 100±2% | 60 to 80 | 3 | 15 | 1100 | Excellent | 5 | Air drying/Baking Enamels, Insulating Varnishes, Food Cal Laquers, Chemical Resistance Paints, Wood Finishes Bobbin Paints and 100% Resin for Hammertone Finishes |
| 80±2% | 80 to 120 | 2.5 | 15 | ||||||
| 65±2% | 120 to 180 | 2.5 | 15 | ||||||
| 1.4 SILAC V 20 | 45±2% | 150 to 250 | 2 | 15 | 1100 | Excellent | 5 | ||
| 1.5 SILEX 60 | Styrenated CNSL Formaldehyde Brown Viscous Resin | 80±2% | 80 to 120 | 2.5 |
15 |
1100 | Excellent | 5 | Same as for Silex 55, Particularly recommended for dark coloured compositions and Anti Fouling Paints |
| 65±2% | 120 to 180 | 2.5 | 15 | ||||||
| 1.6 SILAC V 30 | 45±2% | 180 to 250 | 2.5 | 15 | 1100 | Excellent | 5 | ||
| 1.7 SILEX 70 | Cardphenol Formaldehyde Clear Golden Yellow Liquid Resin | 100±2% | 80 to 100 | 3.5 | 30 | 1000 | Excellent | 5 | Air drying/Banking Enamels, Dark & Semi Dark Enamels, Insulating Varnishes, Food Can Lacquers, Wood Polishes, Coatings for Anti-Corrosive Properties etc. |
| 80±2% | 100 to 120 | 3 | |||||||
| 1.8 SILAC V 50 | 65±2% | 120 to 150 | 2.5 | 20 | |||||
| 45±2% | 150 to 250 | 2.5 | 15 | ||||||
Mr. Nilesh Kumar Jain (Rishabh Resins & Chemicals)
15 E & F Sri Venkateshwara Co-Op. Industrial Estate IDA, Jeedimetla, Hyderabad, Telangana - 500055
Share us via
View Contact Number 