Contact SupplierWe are engaged in offering wear resistant steel plates to our valuable clients. The wear resistant steel plates can be easily wielded and assure high performance. Also known as abrasion resistant steel plate, the wear resistant steel plates have high resistance and durability. Our wear resistant steel plates are available in different grades and thickness.
applications
mining and earth moving
standards
hsla corrosion resistant steel plates corten a, irsm41, sailcor, astm 588 gr. A, en-s355j2w high strength steel plates s355j2g3, astm537-cl.1/2, is-8500-fe540, sailma-350hi-410hi-450hi is2062:2006. E350, e410, e450 abrasion resistant plates quenched & tempered steels sail-hard 200 bhn materials, 400 bhn material, hardox-400, jfe ever-hard 360 le, quard 400, ar-400, xar-400, nicrodur-400, dillidur-400 high strength steel plates quenched & tempered jfe-hiten 780le, weldox, naxtra70, s690ql, dillimax690, astm 514 gr.b.
C | Si | Mn | P | S | Cr | Mo | B |
---|---|---|---|---|---|---|---|
≤ 20 | ≤ 0. 80 | ≤ 1.50 | ≤ 0. 025 | ≤ 0. 010 | ≤ 1.00 | ≤ 0. 50 | ≤ 0. 005 |
The steel has a fine-grained microstructure. Nitrogen is absorbed to form nitrides by means of Al and, where applicable, Nb or Ti. Delivery Condition : Quenched or quenched and tempered (see ‘Heat Treatment’). Hardness at Room Temperature : In the delivery condition - 360-440 HB The Brinell hardness shall be determined in accordance with ISO 6506. |
Carbon equivalent CET (%) [CET=C+(Mn+Mo) /10+(Cr+Cu)/20+Ni/40]: | 0.27 |
---|---|
Carbon equivalent CE (%) [CE=C+Mn/6+(Cr+Mo+V) /5+(Ni+Cu) /15]; | 0.42 |
Yield strength (MPa) *) | 1050 |
Tensile strength (MPa) : | 1250 |
Elongation at fracture A (%) : | 12 |
Bend radius for bending test on transverse test pieces | |
(t=test piece thickness; bend angle: 180o) | ≥ 10xt |
Notch-bar impact energy at -40oC | |
on Charpy V-longitudinal test specimens (J) | 30 |
*) 1 MPa = 1 N/mm2 | |
Number of Tests Unless otherwise agreed upon in the order, the Brinell hardness shall be determined from each heat. The hardness shall be measured roughly 1mm below the surface. General Processing Information Prior to any processing, it is advisable to make use of the information available from the steel producer in order to draw on that experience for the processing. The following information can deal with only a few essential points. The recommendations given in STAHL-EISEN-Werkstoffblatt 088 (Weldable fine-grained structural steels, guidelines for processing, in particular for welding) correspondingly apply to this steel as well. Recommendations for welding are also given in EN 1011 part 1 and part 2 – Welding, Recommendation for welding of metallic materials-. It is left to the discretion of the processor/fabricator to decide which of the familiar precautions must be adopted to avoid cracking during thermal cutting and welding under the prevailing construction and fabrication conditions. Cold Forming The products made of this steel are suitable for cold bending provided, that consideration is given to the high hardness. The formability of steel decreases with increasing hardness. This has to be kept in mind when forming. The forming must take place at a slow and steady rate, the cut edges must be deburred and the plates heated, if necessary, prior to forming. A final stress-relieving is not necessary for this steel. Machinability In spite of its high wear resistance, the steel exhibits good machinability if sufficiently heavy machine-tools and sharp carbide-tipped tools are used. The feed rate and cutting speed have to be adjusted to the high hardness of the material. Heat Treatment Plates made of XAR®400 grade receive the required properties as a result of austenitizing and follow-on quenching in special facilities and, where applicable, tempering below Ac1. Direct quenching after hot-rolling is considered equivalent to conventional quenching. The heat treatment depends on the chemical composition and the product thickness. To avoid hardness losses, the steel must not be heated above 250°C. Thermal Cutting Preferably the flame-cutting process is used. For small product thicknesses, however, the plasma cutting process is used in the interest of minimum distortion. Preheating is not normally necessary when flame-cutting thicknesses up to around 30mm. However, if the workpiece temperature is below +5oC, or the cut edges are to be cold-formed in the course of further processing, preheating to about 150oC should be considered in the interest of cold cracking resistance. Welding If due consideration is given to the general rules for welding, this steel is weldable both manually and automatically. To prevent cold cracking in the welded joints only welding consumables giving welds of very low hydrogen content should be used. Preheating is not generally necessary for welding with austenitic filler metals. Preheating may be necessary for welding with ferritic filler metals. The preheat temperature level for welding depends on the plate thickness and the residual stress state of the structure. The working temperature should not go beyond 250oC. The wear resistance of components fabricated of XAR®400 may be increased with the aid of wear resistant layers deposited by means if welding or metal spraying. General Information Unless otherwise agreed in the order, the delivery will be governed by the conditions outlined in EN 10021. The admissible tolerances are based on EN 10051 for plates cut from hot strip and EN 10029 for four-high mill plates, unless other terms have been agreed upon. The plates will be supplied with a maximum flatness tolerance according to EN 10029, table 4, steel type H. Smaller flatness tolerances can be agreed upon at the time of ordering. For surface quality requirements EN 10163 is applicable. As per special agreement it is possible to supply plates descaled or descaled and prime |