Contact SupplierTectyl Rust Preventive (Tectyl 846) is a solvent cutback, wax base, general purpose, and corrosion preventive compound. The company has cemented its presence among the prominent Suppliers and Exporters of Tectyl Rust Preventive (Tectyl 846). Our Tectyl Rust Preventive (Tectyl 846) is excellent for long term protection of metallic surfaces against corrosion in either indoor or outdoor exposure. It widely for the protection of machinery, machine rolls/tools, automatic parts, dies, tubing, and spare parts.
Surface Preparation : The maximum performance of Tectyl 846 can be achieved only when the metal surfaces to be protected are clean, dry and free of rust, oil and mill scale. Valvoline recommends that the metal substrate temperature be 10-35 °C at the time of product application.
Application : Tectyl 846 is formulated to be used as supplied. Ensure uniform consistency prior to use. Continued stirring is generally not required. If the product thickens due to cold storage or loss of solvent during use, contact Valvoline. DO NOT THIN Tectyl 846. Incorrect thinning will affect film build, dry time and product performance. Valvoline recommends that the ambient and product temperature be 10-35 °C at the time of product application. Tectyl 846 can be applied by airless spray or brush. Tectyl 846 can have a shelf life of 3 years minimum.
Caution : Adequate ventilation is required for cure and to ensure against formation of combustible liquid. THE PARTIALLY CURED FILM SHOULD NOT BE EXPOSED TO IGNITION SOURCES SUCH AS FLARES, FLAMES, SPARKS, EXCESSIVE HEAT OR TORCHES. Refer to Valvoline Material Safety Data Sheet for additional handling and first aid information.
Flashpoint; PMCC |
40 |
oC |
Specific Gravity @ 60oF |
0.87 |
kg/ltr |
Recommended Dry Film Thickness |
50 |
microns |
Theoretical Coverage @ Avg. Recommended DFT |
9.2 |
m²/l |
Non Volatile |
52 |
weight % |
Viscosity; DIN (53 211) Cup No. 2 @ 20oC (at time of manufacture) |
85 |
seconds |
Dry to Touch Time @ 25oC |
± 2 |
hours |
Cure Time @ 25oC |
± 24 |
hours |
Volatile Organic Content (VOC) (ASTM D-3960) |
415 |
g/l |
Accelerated Corrosion Tests @ Avg. Recommended DFT |
||
Salt Spray; 5 % NaCl @ 35oC; DIN 50 021 (ASTM B-117) (DIN 1623 Steel Panels) |
40+ |
days |
Humidity; 100 % RH; @ 40oC; DIN 50 017-KK (DIN 1623 Steel Panels) |
100+ |
days |