Stainless Steel 410 (AMS 5504) UNS S41000:
Type 410 is a basic hardenable martensitic stainless steel and is well suited for use in highly stressed parts where properties such as corrosion resistance, good strength and ductility are required. 410 is used for steam / gas turbine blades and buckets, bushings, valve components, fasteners, nuclear reactor control rod mechanisms, petrochemical equipment and machine parts.
Resisitance to oxidation and corrosion - Alloy 410 exhibits good corrosion resistance to atmospheric corrosion, potable water, food acids and to mildly corrosive chemical environments because of its ability to form a tightly adherent oxide film which protects the surfaces from further attack.
Specifications ;
Type 410 Stainless Steel is covered by the following specifications:
| Grade | US Aerospace/Military | US Commercial | Other |
| 410410 Mod | AMS 5504 Sheet / strip / plate AMS 5505 Sheet / strip / plate (Mod) AMS 5591 Seamless tube AMS 5609 Bars / wire AMS 5611 Bars / wire / forging AMS 5612 Bars / wire / forging AMS 5613 Bars / wire / forging AMS 5614 Bars / wire / forging QQ-S-763, QQ-S-766 | ASTM A176 / ASME SA176 ASTM A240 / ASME SA240 ASTM A276 / ASME SA276 ASTM A479 / ASME A479 ASTM A493 / ASME SA493 ASTM A580 / ASME SA580 ASTM F899 | UNS S41000 |
| Chemical Composition Limits | |||||||
| Weight % | C | Si | Mn | P | S | Cr | Fe |
| Alloy 410 | 0.15 max | 1.0 max | 1.0 max | 0.040 max | 0.030 max | 11.5-13.5 | Bal |
| Material | Tempering Temp °C (°F) | 0.2 % Yield Strength (Mpa) | Ultimate Tensile Strength (Mpa) | % Elongation in 2" | % Reduction of Area | Charpy V Notch Impact Strength (J) | Hardness Brinell |
| Alloy 410 Bar Hardened 1850°F (1010°C) 30 mins, oil quench, tempered 4 Hrs | 260 (500) | 1089 | 1331 | 17 | 62 | 76 | 401 |
| Alloy 410 Bar Hardened 1850°F (1010°C) 30 mins, oil quench, tempered 4 Hrs | 317 (700) | 1069 | 1296 | 17 | 60 | 66 | 401 |
| Alloy 410 Bar Hardened 1850°F (1010°C) 30 mins, oil quench, tempered 4 Hrs | 482 (900) | 1014 | 1303 | 18 | 58 | 38 | 401 |
| Alloy 410 Bar Hardened 1850°F (1010°C) 30 mins, oil quench, tempered 4 Hrs | 538 (1000) | 917 | 965 | 19 | 62 | 33 | 285 |
| Alloy 410 Bar Hardened 1850°F (1010°C) 30 mins, oil quench, tempered 4 Hrs | 593 (1100) | 724 | 827 | 20 | 63 | 52 | 248 |
| Alloy 410 Bar Hardened 1850°F (1010°C) 30 mins, oil quench, tempered 4 Hrs | 649 (1200) | 634 | 731 | 21 | 65 | 119 | 223 |