Listing ID #6658858
Company Information
Ask for more detail from the seller
Contact SupplierStandards | Designation |
---|---|
ASTM | A 240 |
ASME | SA 240 |
STANDARD | UNS | WERKSTOFF NR. | EN | AFNOR | BS | GOST | JIS |
---|---|---|---|---|---|---|---|
SS 316 | S31600 | 1.4401 / 1.4436 | X5CrNiMo17-12-2 / X3CrNiMo17-13-3 | Z7CND17‐11‐02 | 316S31 / 316S33 | - | SUS 316 |
SS 316L | S31603 | 1.4404 / 1.4435 | X2CrNiMo17-12-2 / X2CrNiMo18-14-3 | Z3CND17‐11‐02 / Z3CND18‐14‐03 | 316S11 / 316S13 | 03Ch17N14M3 / 03Ch17N14M2 | SU |
Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | |
---|---|---|---|---|---|---|---|---|---|---|
316 | Min | - | - | - | 0 | - | 16 | 2 | 10 | - |
Max | 0.08 | 2 | 0.75 | 0.05 | 0.03 | 18 | 3 | 14 | 0.1 | |
316L | Min | - | - | - | - | - | 16 | 2 | 10 | - |
Max | 0.03 | 2 | 0.75 | 0.05 | 0.03 | 18 | 3 | 14 | 0.1 | |
316H | Min | 0.04 | 0.04 | 0 | - | - | 16 | 2 | 10 | - |
Max | 0.1 | 0.1 | 0.75 | 0.05 | 0.03 | 18 | 3 | 14 | - |
Grade | Tensile Str (MPa) min |
Yield Str 0.2% Proof (MPa) min |
Elong (% in 50mm) min |
Hardness | |
Rockwell B (HR B) max | Brinell (HB) max | ||||
316 | 515 | 205 | 40 | 95 | 217 |
316L | 485 | 170 | 40 | 95 | 217 |
316H | 515 | 205 | 40 | 95 | 217 |
Grade | Density (kg/m3) |
Elastic Modulus (GPa) |
Mean Co-eff of Thermal Expansion (µm/m/°C) | Thermal Conductivity (W/m.K) |
Specific Heat 0-100°C (J/kg.K) |
Elec Resistivity (nΩ.m) |
|||
0-100°C | 0-315°C | 0-538°C | At 100°C | At 500°C | |||||
316/L/H | 8000 | 193 | 15.9 | 16.2 | 17.5 | 16.3 | 21.5 | 500 | 740 |
Grade | UNS No |
Old British | Euronorm | Swedish SS |
Japanese JIS |
||
BS | En | No | Name | ||||
316 | S31600 | 316S31 | 58H, 58J | 1.44 | X5CrNiMo17-12-2 | 2347 | SUS 316 |
316L | S31603 | 316S11 | - | 1.44 | X2CrNiMo17-12-2 | 2348 | SUS 316L |
316H | S31609 | 316S51 | - | - | - | - | - |
Note: These comparisons are approximate only. The list is intended as a comparison of functionally similar materials notas a schedule of contractual equivalents. If exact equivalents are needed original specifications must be consulted.
Grade | Why it might be chosen instead of 316? |
---|---|
316Ti | Better resistance to temperatures of around 600-900°C is needed. |
316N | Higher strength than standard 316. |
317L | Higher resistance to chlorides than 316L, but with similar resistance to stress corrosion cracking. |
904L | Much higher resistance to chlorides at elevated temperatures, with good formability |
2205 | Much higher resistance to chlorides at elevated temperatures, and higher strength than 316 |