Reinforced Plastic Tarpaulin

Listing ID #3261236

Get Latest Price

Width and length---
WeldingOnly 1 is allowed, lengthwise. Min resistance 80% of original tarpaulin tensile strength in the weft under ISO 1421 plus additional procedure
UV resistanceMax 5% loss of original tensile strength under ISO 1421 after 1500 hours UV under ASTM G53/94 (UVB 313nm peak)
Tear strengthMin 100N both directions (BS 4303 wing tear or equivalent) or under ISO 4674 (A2)
Supply Type Supplier
Preferred Buyer Location All over the world

View More Details

Send Enquiry

Product Details

Welding Only 1 is allowed, lengthwise. Min resistance 80% of original tarpaulin tensile strength in the weft under ISO 1421 plus additional procedure
UV resistance Max 5% loss of original tensile strength under ISO 1421 after 1500 hours UV under ASTM G53/94 (UVB 313nm peak)
Denier Min 1000
Tear strength Min 100N both directions (BS 4303 wing tear or equivalent) or under ISO 4674 (A2)
Tensile strength Min 600N both directions warp and weft (BS 2576, 50mm grab test or equivalent)
Size / roll 4.00 m x 50.00 m +- 1
Materials -----
Size / sheet 4.00 m x 5.00 m +- 1
Eyelets Aluminum reinforcement eyelets or equivalent on 4 sheet sides of single sheets at 100cm (±5 cm) Centre to Centre, providing very strong fixation
Width and length ---
Sheet / roll 190 gsm ±20 g/m² woven Polyethylene (HDPE) inner black fibers, warp x weft, laminated on both sides with LDPE coating

Key Features:

Reinforced plastic tarpaulin in 4 m x 5 m sheets or 4 m x 50 m rolls developed by international research project and designed for long outdoor use in all climates
Made of woven high density black polyethylene (HDPE) fibres, warp x weft, laminated on both sides with low density polyethylene (LDPE) coating
Highly recommended for family shelter protection

Dimensions

Size / sheet	4.00 m x 5.00 m ±1
Size / roll	4.00 m x 50.00 m ±1

Materials

Sheet / roll	190 gsm ±20 g/m² woven Polyethylene (HDPE) inner black fibers, warp x weft, laminated on both sides with LDPE coating
Denier	Min 1000
Tensile strength	Min 600N both directions warp and weft (BS 2576, 50mm grab test or equivalent)
Tear strength	Min 100N both directions (BS 4303 wing tear or equivalent) or under ISO 4674 (A2)
UV resistance	Max 5% loss of original tensile strength under ISO 1421 after 1500 hours UV under ASTM G53/94 (UVB 313nm peak)
Welding	Only 1 is allowed, lengthwise. Min resistance 80% of original tarpaulin tensile strength in the weft under ISO 1421 plus additional procedure
Eyelets	Aluminum reinforcement eyelets or equivalent on 4 sheet sides of single sheets at 100cm (±5 cm) Centre to Centre, providing very strong fixation

Interested in this product? Ask for more details & Latest Price from seller

Send Enquiry

Product Images

Company Details

Welcome to- Lamifabs & Papers Pvt. Ltd.
Established in the year 1987, at Aurangabad, (Maharashtra, India), we at “Lamifabs”, manufacture “POLYTARPS” HDPE / PP waterproof Tarpaulin, HDPE Vermibed under the brand name “TETRAA VERMI BED”, “POLYPOND” Brand HDPE pond lining.
We also make HDPE IRRIGATION PIPE, WIDE WIDTH FABRIC, HDPE FUMIGATION COVER and AZOLLA TETRAA POND, etc. Owing to the features such as excellent strength and high durability, these products are highly applauded globally.
Vision
“TO BRING ABOUT A CHANGE IN AGRICULTURAL PRACTICES GLOBALLY, HELPING THE WORLD GET ONE STEP CLOSER TO A SUSTAINABLE ENVIRONMENT.”
Mission
“OUR PASSION FOR INTEGRATED AND HARMONIZED PRODUCT SOLUTIONS FOCUSES OUR ACTIONS TOWARDS ONE COMMON PURPOSE: OFFERING DISTINCTIVE AND EXCLUSIVE PRODUCT SOLUTIONS THAT REFLECT THE UNIQUE AND REFINED PROFILE OF OUR CLIENTS.”
“ANALYSIS, DESIGN, IMPLEMENTATION AND SERVICE ARE KEY INGREDIENTS TO OUR QUALITY FIRST IDEOLOGY.”