Listing ID #1191970
Company Information
Ask for more detail from the seller
Contact SupplierWe are one of the most eminent names in the manufacturing and supplying of Polyurethane Paints & Primers in India. They provide excellent base coat for PU system and have high adhesion too. Our wide range of Polyurethane Paints and Primers are made by using premium quality raw material, under the expert guidance of our expert team members. These polyurethane paints & primers are provided pre-treatment and form plastic like films on to-be painted surfaces and provide excellent corrosion and abrasion resistance.
Properties :
Application :
PRODUCT | SHADE | SUBSTRATE | RECOMMENDED USE |
---|---|---|---|
Polyurethane Primer | Grey / MIO brown | Metal / Cement Plastic |
Excellent base coat for PU system. Adhesion to metal, fibreglass, cement & ABS surface |
Polyurethane (interior-Aromatic) | White / Black / iS & RAL Shades |
Metal / Fibre / ABS / Cement |
Excellent water, chemical & solvent resistance Recommended for interior application |
Polyurethane (Exterior-Aliphatic) | White / Black IS & RAL Shades |
Metal / Fibre / ABS / Cement |
Excellent colour & gloss retention on outdoor exposure, excellent chemical & solvent resistance |
Type | Single Pack |
Composition | Grey-Modified alkyd medium suitably pigmented with zinc phosphate. Red oxide-CNSL base suitably Pigmented with Red oxide |
Viscosity (Ford Cup B4) | 90±10 Seconds |
Specific Gravity | 1.20±0.05 |
Application | Brush/Roller/ conventional or airless spray |
Recommended DFT | 30±5µ per coat |
Theoretical Spreading Rate | 5-6 Sq.Mtr./ Liter |
Drying Time | Surface Dry-50-55 min Tack Free- 3-4 hours Hard Dry-over night |
Over coating interval | Min: Overnight Max: 2 Days |
Flash Point | Above 40Ëš C |
Colour | Grey, Red oxide |
Packing | 4,10,20 liters |
Thinner | Pragati make G.P. Thinner |
Finish | Grey- Smooth & Matt Red oxide- Smooth & Matt/Glossy |
Type | Single Pack |
Composition | Modified alkyd medium suitably pigmented |
Application | Brush/Roller/ conventional or airless spray |
Viscosity (Ford Cup B4) | 70±10 seconds |
Specific Gravity | 1.00±0.05 |
Recommended DFT | 25±5µ per coat |
Theoretical Spreading Rate | 6-7 Sq.Mtr./ Liter |
Drying Time | Surface Dry-55-60 min Tack Free- 4 hours Hard Dry-over night |
Over coating interval | Min: Overnight Max: 2 Days |
Flash Point | Above 40Ëš C |
Colour | As per IS & RAL K5 Shade cards |
Packing | 4,10,20 liters |
Thinner | Pragati make G.P. Thinner |
Finish | Smooth & Semi Glossy/Glossy |
After complete curing following tests should be carried. | ||
Examine Test | Specification | Result |
Adhesion Test | After 24 hrs. ( No lifting of film form) | Pass |
Scratch Hardness Test | 1000-1500 gm. | Pass |
Flexibility | To pass ¼ inch mandrel | Pass |
Salt Spray | 100-140 Hrs. | Pass |
Humidity Test | 140 hrs. No blistering / rusting & no loss of adhesion | Pass |
Resistance to Grease | For 48 hrs at R.T.No blistering. No deterioration of hardness, No failure of adhesion | Pass |
Chemical Resistance | ||||
Exposures | Splash & Spillage | Mild Fumes/Out door Resistance | ||
PRIMERS | PAINTS | PRIMERS | PAINTS | |
Acid | Good | Good | Very Good | Good |
Alkalis | Good | Excellent | Good | Excellent |
Solvents | Very Good | Good | Good | Good |
Salt | Excellent | Excellent | Excellent | Excellent |
Water | Excellent | Excellent | Excellent | Excellent |
Temperature Resistance :
Weatherability : Excellent
Flexibility : Good
Abrasion Resistance : Good
Storage Life : Up to 6 month in intact condition or sealed the containers are kept under cover in a dry place under normal temp.conditions.
Surface Preperation :
Steel : remove grease, oil & other contaminants preferably by using degreasing solvent. Blast clean to a minimum of Sa2 ½ Swedish std SIS 05 5900. For severe corrosion, blast to Sa 3 with a surface profile not exceeding 65 microns.
If blasting is not practical, make full use of mechanical tools along with manual chipping & wire brushing to remove loose rust & scale to st 2 swedish std SIS 05 5900. Excessive burning of steel is to be avoided. Thoroughly dust down all surfaces. Best results can be achieved if the manually cleaned surface is primed with protectomastic- self priming surface tolerant coating; otherwise treatment with metal conditioning solution will also produce satisfactory results.
The surface should be clean & dry before application of primer coat.
Concrete : new concrete- ensures that the concrete is cured for a minimum of 3 months. The surface is to be made rough & free from laitance & other contaminants by sand sweeping.
Old concrete- removes all salt deposits from the surface by water jet washing. Light sand blast the surface to remove all loosely bound coating & roughening up to firmly adhering coating to ensure anchorage with recommended system. Ensure all dust/ other particles are fully removed by suction or air blast & the surface is fully cleaned & dry before application of paint.
In non critical areas where blasting is not possible, water jet washing & hard wire brushing are minimum requisites.
Application :
Note :