Item Code: RXSOL-68-6801-005
RX JELLY Paste is highly concentrate paste which is used to clean weld seams and surrounding areas and is applied with brush. This is very effective product to acts as Degreasing, cleaning, pickling and passivating of austenitic and duplex stainless steel 304, 316, nickel and aluminium.
Strong adhesion on inclined and vertical surface . For local pickling and cleaning all types of welds. Remains active with temperatures >10°C
Degrease thoroughly the surface with RXSOL-10-1005-025 . Never let the product dry. Hose off completely and thoroughly with a high-pressure spraying pistol. Remaining grease and product will influence the pickling process adversely. Let the surface dry, rub dry or blow dry.
Stir the pickling paste. Spread the undiluted paste over the surface or the weld by using the supplied acid resistant brush.Contact time: 30 min to 2 h. (depending on the kind of weld, the room temperature and material).The pickling process is terminated as soon as the paste turns green. Always rinse abundantly with clean water. Rinse preferably with demineralised water.
Never let the product dry Prolonged pickling lead to accelerated corrosion sensitivity and damages the passivation process .
In case of doubt, try out on a test surface or contact our technical service. It is used to remove heavy scales, discolouration, annealing colours, rust particles near weld and welding affected area by heat without grinding or wire brushing or buffing.Coverage : Approx. 100 meters of running weld seam kg of Passivating Pickling Paste
Dose :::
1.Passivating Pickling Paste is applied on weld seam & surrounding areas with a nylon bristled plastic brush. Application Temp. = between 5 � 40 deg. C
2. Keep Passivating Pickling Paste for 5 to 30 minutes (contact time) depending on contamination, temperature & grade of Stainless Steel.

Item Code: RXSOL-68-6801-005
RX JELLY Paste is highly concentrate paste which is used to clean weld seams and surrounding areas and is applied with brush. This is very effective product to acts as Degreasing, cleaning, pickling and passivating of austenitic and duplex stainless steel 304, 316, nickel and aluminium.
Strong adhesion on inclined and vertical surface . For local pickling and cleaning all types of welds. Remains active with temperatures >10°C
Degrease thoroughly the surface with RXSOL-10-1005-025 . Never let the product dry. Hose off completely and thoroughly with a high-pressure spraying pistol. Remaining grease and product will influence the pickling process adversely. Let the surface dry, rub dry or blow dry.
Stir the pickling paste. Spread the undiluted paste over the surface or the weld by using the supplied acid resistant brush.Contact time: 30 min to 2 h. (depending on the kind of weld, the room temperature and material).The pickling process is terminated as soon as the paste turns green. Always rinse abundantly with clean water. Rinse preferably with demineralised water.
Never let the product dry Prolonged pickling lead to accelerated corrosion sensitivity and damages the passivation process .
In case of doubt, try out on a test surface or contact our technical service. It is used to remove heavy scales, discolouration, annealing colours, rust particles near weld and welding affected area by heat without grinding or wire brushing or buffing.Coverage : Approx. 100 meters of running weld seam kg of Passivating Pickling Paste
Dose :::
1.Passivating Pickling Paste is applied on weld seam & surrounding areas with a nylon bristled plastic brush. Application Temp. = between 5 � 40 deg. C
2. Keep Passivating Pickling Paste for 5 to 30 minutes (contact time) depending on contamination, temperature & grade of Stainless Steel.