Fabric phenolic laminates, Color : Off-White

Listing ID #3812934

Get Latest Price

GradeF-1
ColorOff-White
Thickness Range0.5mm - 50mm
Applications- Heavy Duty Gears - Pulleys - Automobile couplings - Machine tools fibs/Slid Waxes etc.
Characteristics- Combination of good machining and electrical properties. - Good applicability for making automobile parts and fine machining parts.
Supply Type Manufacturer, Exporter, Supplier
Preferred Buyer Location All over the world

View More Details

Product Details

Grade	F-2
Color	Brownish/Natural
Thickness Range	0.5mm - 150mm
Characteristics	- Superior machining, punching and chemical resistance. - Offers excellent Strength:Weight ratio.
Applications	- Shuttle gears, Pulleys - Automobile couplings - Structural parts, Spindles - Machine tool fibs/Slide waxes Low voltage contract breakers Friction plates - Rolling Mill bearings etc.

Grade	F-3
Color	Brownish Red
Thickness Range	0.8mm - 150mm
Characteristics	- Mechanically strong with adequate machinability. - Offers high impact resistance.
Applications	- Heavy Duty Gears - High impact Strength Bearing components Pulleys - Pilling Dolly - Work bench tops - Rolling Mill bearings etc.

Grade	F-4
Color	Brownish
Thickness Range	0.5mm - 150mm
Characteristics	- Good mechanical strength at room temperature.
Applications	- Heavy Duty Gears - Pulleys - Pilling Dolly - Friction Plates etc.

Grade	F-5
Color	Brownish
Thickness Range	0.5mm - 150mm
Characteristics	- Good mechanical strength with adequate - electrical properties at room temperature.
Applications	- Heavy Duty Gears - Pulleys - Pilling Dolly - Friction Plates etc.

Properties

Unit

Grade

Fabric Phenolic

IS 2036:1995

NEMA LI 1-1983

IEL

IF-2001

IF-2002

IF-2003

IF-2004

IF-2005

Mechanical Properties

Test Applicable for Thickkness

IEL AVG. VALUE

LIMITING VALUE

IEL AVG. VALUE

LIMITING VALUE

IEL AVG. VALUE

LIMITING VALUE

IEL AVG. VALUE

LIMITING VALUE

IEL AVG. VALUE

LIMITING VALUE

Cross Breaking Strength

Mpa

Not less than 1.6 mm

145

135 (min)

135

110 (min)

110

100 (min)

110

100 (min)

110

100 (min)

Tensile Strength

Shear Strength

Mpa (min)

Less than 1.6 mm

65(min)

60(min)

65(min)

Compression Strength

Impact Strength

KJ/m2

Not less than 5.00 mm

8.0

6 (min)

7.2 (min)

10.5

8.8 (min)

7.0 (min)

8.0

6.0 (min)

Electrical Properties

Electrical Strength (Flatwise)

MV/m

Not more than 3.00 mm

Complies

Electrical Strength (Edgewise)

More than 3.00 mm

Complies

2.0 (min)

Complies

1.00 (min)

Complies

1.00 (min)

Complies

15 (min)

Complies

20 (min)

Insulation Resistance

M.ohms

Not more than 25 mm

5.00

1.00 (min)

4.00

0.5 (min)

4.00

0.5 (min)

100.00

50 (min)

180.00

150 (min)

Water Absorption (1.6mm)

(all thickness)

160

220 (max)

160

220 (max)

160

220 (max)

105

145 (max)

105

145 (max)

Specific Gravity

Grams/CC

1.33

1.35

1.36

1.33

Company Details

Industrial Laminates are structural composite materials that consists of two components - a reinforcement material and a thermosetting resin system. The two components are cured together under pressure at high temperature into the finished composite material. The reinforcement materials and the resin systems can be combined individually, making it possible to construct composite materials with very specific properties which helps it being attractive and versatile in nature when compared to its alternatives in other structural materials.
Laminates also have stable geometry at high temperatures and have minimal deformation when subjected to loads. In addition, they have a high strength to weight ratio and also have properties that do not deteriorates with age. From their other application as insulating material in electro-mechanical designs, modern laminates have spread to a large number of other industries, resulting in a constantly increasing number of new applications.