Grade

C

Mn

Si

S

Cu

Fe

Ni

Cr

Nickel 200

0.15 max

0.35 max

0.35 max

0.01 max

0.25 max

0.40 max

99.0 min

–

Nickel 201

0.15 max

0.35 max

0.35 max

0.01 max

0.25 max

0.40 max

99.0 min

–

Element

Density

Melting Point

Tensile Strength

Yield Strength (0.2%Offset)

Elongation

Nickel 200

8.9 g/cm3

1446 °C (2635 °F)

Psi – 67000 , MPa – 462

Psi – 21500 , MPa – 148

45 %

Nickel 201

8.9 g/cm3

1446 °C (2635 °F)

Psi – 67000 , MPa – 462

Psi – 21500 , MPa – 148

45 %

Grade

C

Mn

Si

S

Cu

Fe

Ni

Cr

Nickel 200

0.15 max

0.35 max

0.35 max

0.01 max

0.25 max

0.40 max

99.0 min

–

Nickel 201

0.15 max

0.35 max

0.35 max

0.01 max

0.25 max

0.40 max

99.0 min

–

Element

Density

Melting Point

Tensile Strength

Yield Strength (0.2%Offset)

Elongation

Nickel 200

8.9 g/cm3

1446 °C (2635 °F)

Psi – 67000 , MPa – 462

Psi – 21500 , MPa – 148

45 %

Nickel 201

8.9 g/cm3

1446 °C (2635 °F)

Psi – 67000 , MPa – 462

Psi – 21500 , MPa – 148

45 %