Contact SupplierCHARACTERISTIC | TEST METHOD | MIN. | MAX |
---|---|---|---|
Appearence | A resprentative sample of the oil shall be examined in 100 mm thick layer at 27 degrree | The oil shall be clear, transparenta and free from suspended matter or sediments. | |
Density@29.5degrreC.G/cm3 | IS:1448(P-16)1977 | - | 0.89 |
Kinematic Viscosity, cSt@27degrreC | IS:1448(P-25)1976 | -I | 27 |
Interfacial Tension , N/M@ 27 degrre C | IS:6104:1971 | 0.04 | |
Flash Point Pensky-Marten (closed) degree C | IS:1448(P-21)1992 | 140 | |
Pour Point, degreeC | IS:1448(P-10)1970 | -6 | |
Netralisation Value | IS:14489(P-2)1967 | NIL | 0.03 |
a) Total Acidity , mgKOH/gm b)Inorganic Acidity/Alkalinity | No-corrosive | Non-corrosive | |
Corrrosive Sulphur Copper Strip,19hrs@140degreeC | ANNEX- B | ||
Electric Strength (BDV), KV,r | IS:6792:1992 | ||
a)New Unfiltered Oil | 30 | ||
b)After Filteration. | 60 | ||
Dielectric Dissipation Factor | IS:6262:1971 | -I | 0 |
(Tan Delta ) @90degreeC | |||
Specific Resistance (Resistivity) Ohm-cm | IS:6103:1971 | 1500*10 ^12 | |
a)At 27degree C | 35*10 ^12 | ||
b)at 90degree C. | |||
Oxidation Stability (after oxidation for 164hrs @100degree C | ANNEX-C | 1500*10^12 | 0.4 |
a)Neutralisation Value , mgKOH/gm | 35*10^12 | 0.1 | |
b)Total Acidity, wt% | |||
Acclerated Ageing Test(open Baker Method with Copper Catalyst) | IS:12177:1987 | ||
96hrs @115degree C | Method A | 2.5*10^12 | 0.2 |
a)Specific RESISTANCE , Resistivity Ohm-cm @ 90degree C | IS:6103:1971 | 0.2*10^12 | 0.05 |
b)Specific Resistance , Resistivity Ohm-cm @ 90degree C | IS:6103:1972 | ||
c)Dielectric Dissipation Factor ( Tan Delta) @90 degree C | IS:6103:1973 | ||
d)Total Acidity, mg KOH/GM | IS:14489(P-2)1967 | ||
e)Total Sludge Value , wt % | ANNEX A of IS:12177 | The soil shall contain no antioxidant additive. | |
Presence of Oxidation Inhibitor | IS:13631:1992 | ||
Water Content, ppm | IS:13567:1992 | 50 |