Description

Luban polypropylene is manufactured using Novolen vertical stirred Gas-phase polymerization process. Luban HP2100S is a Homopolymer polypropylene with good flowability and stiffness for general applications.

Application

Thin walled packaging, household articles & general purpose injection molding.

Note: These are typical properties only and are not to be construed as specifications. Users should confirm results by their own tests.

The Typical Processing Conditions for Luban HP2100S are:

Melt temperature 220 – 260 °C

Holding pressure 200 – 500 bar Maximum to avoid sink marks

Mold temperature 20 – 40 °C

Injection speed High

Shrinkage 1 – 2 % depending on wall thickness and molding parameters

Storage and Handling

Luban HP2100S should be stored in well ventilate area during handling or processing of to prevent accumulation of dust and fumes. Avoid contact with strong oxidizers, excessive heat, sparks or open flame as this could well speed up alteration and consequently loss of quality of the material in which could lead to unforeseen dangers. The bags must be protected from direct sunlight and should be stored in shaded and completely dry area for good processing.

Safety

Luban HP2100S is not classified as dangerous preparation. For further information about safety in handling and processing please refer to the Safety Data Sheet.

Food Contact

Luban HP2100S meets the requirements of the U.S. Food and Drug Administration (FDA) as specified in 21 CFR 177.1520, covering safe use of polyolefin articles and components of articles intended fo direct food contact. For additional information on approved conditions of use for food contac applications, please refer to the “Product Stewardship Declaration”.

Recycling

The product is suitable for recycling using modern methods of shredding and cleaning. In-house production waste should be kept clean to facilitate direct recycling.

Description

Luban polypropylene is manufactured using Novolen vertical stirred Gas-phase polymerization process. Luban HP2100S is a Homopolymer polypropylene with good flowability and stiffness for general applications.

Application

Thin walled packaging, household articles & general purpose injection molding.

Note: These are typical properties only and are not to be construed as specifications. Users should confirm results by their own tests.

The Typical Processing Conditions for Luban HP2100S are:

Melt temperature 220 – 260 °C

Holding pressure 200 – 500 bar Maximum to avoid sink marks

Mold temperature 20 – 40 °C

Injection speed High

Shrinkage 1 – 2 % depending on wall thickness and molding parameters

Storage and Handling

Luban HP2100S should be stored in well ventilate area during handling or processing of to prevent accumulation of dust and fumes. Avoid contact with strong oxidizers, excessive heat, sparks or open flame as this could well speed up alteration and consequently loss of quality of the material in which could lead to unforeseen dangers. The bags must be protected from direct sunlight and should be stored in shaded and completely dry area for good processing.

Safety

Luban HP2100S is not classified as dangerous preparation. For further information about safety in handling and processing please refer to the Safety Data Sheet.

Food Contact

Luban HP2100S meets the requirements of the U.S. Food and Drug Administration (FDA) as specified in 21 CFR 177.1520, covering safe use of polyolefin articles and components of articles intended fo direct food contact. For additional information on approved conditions of use for food contac applications, please refer to the “Product Stewardship Declaration”.

Recycling

The product is suitable for recycling using modern methods of shredding and cleaning. In-house production waste should be kept clean to facilitate direct recycling.