Brown Rectangular Solid High Alumina Bricks, For Construction, Size : Standard

₹ 125 - ₹ 3,450 / Nos

MaterialHigh Alumina
TextureSolid
ShapeRectangular
ColorBrown
Supply TypeManufacturer, Exporter, Supplier, Importer
Preferred Buyer Location All over the world

Technical Details

Product Name	Chemical Analysis (%)		Apparent Porosity(%)	Bulk Density (g/cc) Min.	CCS (kg/cm²)	PLC(%)	PCE(◦C/0C) Min.	RUL (Ts◦C)	Application Area
Product Name	Al2O3	Fe2O3	Apparent Porosity(%)	Bulk Density (g/cc) Min.	CCS (kg/cm²)	PLC(%)	PCE(◦C/0C) Min.	RUL (Ts◦C)	Application Area
TCC - 30D	28-31	1.7-2.2	13-18	2.1	400-700	± 0.5 at 1300◦C/2h		1330-1360	Back up of Aluminium pot furnace and other applications.
TCC - 40	36-40	2.5-3.5	17-22	2.15	350-550	-0.8 to 0.3 at 1400◦C/2h	1659/29	1350-1400	Cement preheater,Cyclone, Silicate Furnace & other moderate heat applications.
TCC - 40S	38-41	1.8-2.5	16-21	2.2	400-600	0.8 to 0.3 at 1450◦C/2h	1665/30	1370-1420	Special bricks for Cement Preheater & Cyclone.
TCC - 42D	41-43	1.3-1.7	15-18	2.25	450-650	-0.6 to 0.2 at 1450◦C/2h	1717/32	1450-1480	Dense brick for Blast Furnace & Anode Baking Furnace (ABF)
TCC - 45	42-45	2.5-3.5	17-22	2.23	400-500	-0.8 to 0.3 at 1400◦C/2h	1665/30	1360-1410	Cement preheater,Cyclone, Silicate Furnace & other moderate heat applications.
TCC - 45S	42-46	1.8-2.5	16-21	2.25	400-600	-0.8 to 0.3 at 1450◦C/2h	1683/31	1390-1440	Special purpose Cement Preheater, Cyclone, Chemical Plants,Sulphur Furnaces, Lime Kiln & Glass Tank Furnace.
TCC - 45D	44-48	1.2-1.5	14-18	2.35	450-700	-0.5 to 0.2 at 1450◦C/2h	1743/33	1460-1500	Blast Furnace, Preheating Zone of Cement Rotary Kiln & Glass Tank Furnace.
TCC - RW			17-21	2.25	400-600	-1.0 to 0.2 at 1450◦C/2h	1683/31	1390-1440	Reheating Furnace Wall
TCC - 50	47-50	2.6-3.5	17-21	2.32	450-650	-0.8 to 0.4 at 1450◦C/2h	1717/32	1400-1450	Preheating Zone of Cement Rotary Kiln & Reheating Furnace Wall.
TCC - 50S	47-50	1.8-2.2	16-21	2.3	450-650	-1.0 to 0.3 at 1450◦C/2h	1717/32	1400-1450	Dense brick for Petro-Chemicals,Fertilizer Plants & Anode baking Furnace.
TCC - RR			16-22	2.35	450-650	-0.5 to 1.0 at 1450◦C/2h	1743/33	1430-1480	Reheating Furnace Roof.
TCC - 55	52-55	2.9-3.9	17-22	2.42	450-650	-0.5 to 1.0 at 1450◦C/2h	1743/33	1400-1440	Preheating Zone of Cement Rotary Kiln & Reheating Furnace Wall.
TCC - 55S	52-56	1.7-2.2	16-21	2.35	500-700	-0.8 to 0.3 at 1500◦C/2h	1763/34	1450-1500	Reheating Furnace Roof & Petro Chemicals.
TCC - SILL	56-59	1.0-1.5	17-21	2.35	400-600	± 0.7 at 1500◦C/2h	1804/36	1500-1540	Glass Tank Furnace & Frit Furnace.
TCC - 60	57-60	3.4-4.2	17-22	2.5	550-800	-0.4 to 2.0 at 1450◦C/2h	1785/35	1420-1450	Reheating Furnace Wall, Ladle Back up.
TCC - 60L	57-61	2.8-3.8	17-22	2.45	500-800	-0.2 to 2.2 at 1500◦C/2h	1785/35	1430-1470	Reheating Furnace Wall, Ladle Back up.
TCC - 60S	58-61	1.7-2.2	16-21	2.45	500-800	-0.4 to 0.8 at 1500◦C/2h	1804/36	1470-1510	Sulphur Furnace,Alakli Resistant Bricks for Cement Rotary Kin & Ladle Back up.
TCC - 60M	59-61	0.9-1.1	14-18	2.45	600-800	± 0.5 at 1600◦C/2h	1820/37	1630-1670	Blast Furnace Stove Checkers,Solid Wall Bricks & Glass Tank Furnace.
TCC - 62DB	61-63	1.2-1.7	14-18	2.45	500-800	± 0.8 at 1500◦C/2h	1785/35	1500-1530	Blast Furnace Stove Checkers,Solid Wall Bricks & Glass Tank Furnace.
TCC - 62D	61-64	1.2-1.5	13-16	2.5	600-900	± 0.5 at 1500◦C/2h	1804/36	1500-1550	Blast Furnace Hearth,Non-Recovery Coke Oven,Glass Tank Furnace & Frit Furnace.
TCC - 628RN	62-64	0.9-1.2	42339	2.5	650-900	± 0.2 at 1500◦C/2h	1820/37	1500-1550 at 4kg/cm²	Blast Furnace Hearth,Non-Recovery Coke Oven,Glass Tank Furnace.
TCC - 70N	64-67	3.5-4.4	17-23	2.55	500-800	0.5 to 2.5 at 1450◦C/2h	1804/36	1440-1470	Boiler Cupola & Steel Foundry
TCC - 70	67-70	3.4-4.0	17-22	2.6	600-900	0.3 to 2.5 at 1450◦C/2h	1804/36	1460-1480	Boiler Cupola & Steel Foundry & Reheating Furnace.
TCC - 70S	67-70	2.8-3.2	17-22	2.6	600-900	0.5 to 3.0 at 1500◦C/2h	1804/36	1460-1480	Burning Zone of Cement Rotary Kiln & Steel Ladle.
TCC - 70L	67-70	2.4-2.8	16-21	2.55	600-800	0.5 to 2.5 at 1500◦C/2h	1804/36	1460-1480	Burning Zone of Cement Rotary Kiln & Steel Ladle.
TCC - 70/20	68-71	1.8-2.2	16-21	2.55	600-900	0.2 to 2.0 at 1500◦C/2h	1804/36	1470-1500	Burning Zone of Cement Rotary Kiln & Steel Ladle.