Contact SupplierC34500 high leaded brass "64%" is the brass with high machining ability. The increase in lead content will result in increased machining ability with good strength and atmospheric corrosion resistance. The increased lead content will also provide pressure tightness by sealing the shrinkage pores.
Applications :
Equivalent Specifications:
Specifications | Designation |
BS | CZ131 / CZ119 |
EN | CW601N/CuZn35Pb2 |
JIS | C3560 |
DIN | 2.0331 |
ISO | Â |
Russian (GOST) | Â |
Chemical Composition:
 | Cu | Pb | Zn | Fe |
Min/Max | 62 - 65 | 1.5 – 2.5 | Rem. (Max.) | 0.15 (Max.) |
Specifications:
Ingots | Â |
Bar | Â |
Square | Â |
Billets | Â |
Plate | Â |
Sheet | Â |
Flat | Â |
Rods | Â |
Profiles | Â |
Wire | Â |
Hollows | Â |
Hex | Â |
Tubes | Â |
Fabrication Properties:
Joining Technique | Suitability |
Soldering | Excellent |
Brazing | Good |
Oxyacetylene Welding | Not Recommended |
Gas Shielded Arc Welding | Not Recommended |
Coated Metal Arc Welding | Not Recommended |
Spot Weld | Not Recommended |
Seam Weld | Not Recommended |
Butt Weld | Fair |
Capacity for Being Cold Worked | Fair |
Capacity for Being Hot Formed | Poor |
Machinability Rating | 90 |
Mechanical Properties:
Form | Temper Code | Tensile Strength (ksi) | YS-0.5% Ext (ksi) | Elongation (%) | Rockwell B Scale | Section Size (in) | ||
Rods |
H02 | 50 Min for Standard 62 Max for Standard |
20 Min for Standard | 15 Min for Standard | 55 Min for Standard 75 Max for Standard |
0.75 | ||
H02 | 57 Min for Standard 80 Max for Standard |
25 Min for Standard | 7 Min for Standard | Â |