Contact SupplierWe are a reliable Importer and Supplier of MAG Carbon Bricks for Converter/ EAF /Ladle. The MAG Carbon Bricks for Converter/ EAF /Ladle that we bring to you is made up of top-notch quality raw materials and sophisticated machines.
i) Resin Bonded Bricks for converter | ||||||||||
MGO % | MGO (Loss Free Basis) % (Min) | FC % (Min) | AL2O3% (Max) |
A.P. % (Max) | BD gm/cc (Min) | C.C.S Kg/cm2 (Min) | HMOR Kg/cm2 @ 1400 oC (Min) |
Application Area | ||
97 | 84 | 12 | 3 | 2.8 | 3 | 450 | 120 | Bottom Lower Case | ||
97 | 84 | 12 | 3 | 2.8 | 3 | 450 | 120 | Lower Cone | ||
97 | 84 | 12 | 3 | 2.8 | 3 | 450 | 120 | Barrel | ||
97 | 84 | 12 | 3 | 2.8 | 3 | 450 | 120 | Top Cone | ||
97 | 87 | 9 | 3 | 2.8 | 3 | 450 | 120 | Charge Paid | ||
97 | 80 | 15 | 3 | 2.8 | 3 | 450 | 120 | Trunion | ||
97 | 81 | 13 | 3 | 2.8 | 3 | 450 | 120 | Tap Hole | ||
ii) Pitch Bonded bricks for converter | ||||||||||
98 | 90 | 5 | 2.98 | 4- | 480- | 80 | Hot & Cold Spots | |||
96 | 85 | 10 | 2.97 | 4- | 420- | 80 | ||||
96 | 82 | 13 | 2.96 | 4- | 400- | 80 | ||||
93 | 80 | 15 | 2.95 | 4- | 400- | 80 |
Typical & Average data of Magnesia Carbon Bricks for EAF/UHPF Furnace | |||||||||
---|---|---|---|---|---|---|---|---|---|
MGO % (Min) | MGO Loss Free % (Min) | FC % (Min) | BD gm/cc (Min) | A.P. % (Max) | Coked A.P. @ 1000oC % (Max) |
CCS Kg/ cm2 (Min) | MOR Kg/cm2 @ room temp |
HMOR Kg/ cm2 @ 1400oC (Min) |
Area of Application |
97 | 86 | 12 | 2.98 | 3 | 11 | 420 | 140 | 120 | Hot Spots |
97 | 84 | 14 | 2.96 | 3 | 12 | 400 | 140 | 120 | |
97 | 81 | 16 | 2.9 | 2.8 | 13 | 400 | 140 | 120 | |
98 | 87 | 12 | 2.98 | 3 | 11 | 450 | 110 | 80 | Hot & Cold Spots |
98 | 85 | 14 | 2.96 | 3 | 12 | 420 | 110 | 80 | |
98 | 82 | 16 | 2.9 | 2.8 | 13 | 400 | 110 | 80 | |
96 | 85 | 12 | 2.98 | 4 | 11 | 420 | 90 | 60 | Cold Spots |
96 | 84 | 14 | 2.96 | 4 | 12 | 400 | 90 | 60 | |
96 | 81 | 16 | 2.9 | 4 | 13 | 400 | 90 | 60 |
Typical and Average Data of Magnesia Carbon Bricks for Ladle | ||||||||||
---|---|---|---|---|---|---|---|---|---|---|
MGO % (Min) | MGO Loss Free % (Min) | FC % (Min) | BD gm/cc (Min) | A.P. % (Max) | Coked A.P @ 1000oC % (Max) |
CCS Kg/ cm2 (Min) | MOR Kg/cm2 @ room temp. |
HMOR Kg/ cm2 @ 1400 oC (Min) |
Area of Application | |
98 | 90 | 5 | 3 | 3 | 10 | 480 | 160 | 90 | Bottom & Metal Zone | |
98 | 88 | 8 | 2.99 | 3 | 10 | 450 | 150 | 90 | -“- | |
98 | 86 | 10 | 2.99 | 2.8 | 10 | 400 | 140 | 90 | Slag Zone | |
98 | 84 | 12 | 2.92 | 2.8 | 11 | 400 | 140 | 90 | - “ - | |
96 | 89 | 5 | 3 | 4 | 10 | 480 | 140 | 80 | Bottom & Metal Zone | |
96 | 87 | 8 | 2.98 | 4 | 10 | 450 | 120 | 80 | - “ - | |
96 | 85 | 10 | 2.95 | 4 | 10 | 400 | 110 | 80 | Slag Zone | |
96 | 83 | 12 | 2.9 | 4 | 11 | 400 | 110 | 90 | - “ - | |
95 | 5 | 88 | 2.98 | 4 | 10 | 400 | 110 | 60 | Bottom & Metal Zone | |
95 | 86 | 8 | 2.98 | 4 | 10 | 400 | 110 | 60 | - “ - | |
95 | 84 | 10 | 2.95 | 4 | 10 | 400 | 110 | 60 | Slag Zone | |
95 | 82 | 12 | 2.9 | 4 | 11 | 400 | 100 | 60 | - “ - | |
93 | 83 | 8 | 2.85 | 6 | 1A | 400 | 100 | 50 | Free Board & Low Temp Applications | |
92 | 82 | 8 | 2.85 | 6 | 1A | 350 | 90 | 50 | -- | |
90 | 81 | 8 | 2.85 | 7 | 14 | 300 | 100 | 50 | -- |