Contact SupplierAlloy 904L is a high-combination austenitic stainless steel with low carbon content. The evaluation is proposed for utilization under extreme destructive conditions. It has been application demonstrated over numerous years and was initially created to oppose consumption in weaken sulphuric corrosive. It is institutionalized and affirmed for weight vessel use in a few nations. Basically, Alloy 904L is completely austenitic and is less delicate to precipitation ferrite and sigma stages than customary austenitic evaluations with high molybdenum content. Distinctively, because of the mix of generally high substance of chromium, nickel, molybdenum and copper 904L has great imperviousness to general erosion, especially in sulphuric and phosphoric conditions.
SPECIFICATIONS:
ASTM B677, B366
ASME SB677, SB366
FEATURES OF ALLOY 904L
Profoundly impervious to setting, hole and general erosion.
High imperviousness to chloride stress erosion breaking
50% stronger than 300-arrangement austenitic stainless steels
Superb effect sturdiness
Superb workability and weldability
USES OF ALLOY 904L
Seawater taking care of gear
Mash factory dye frameworks
Compound transforming hardware
Sustenance transforming hardware
Desalination hardware
Vent gas desulphurization scrubbers
CHEMICAL COMPOSITION OF ALLOY 904L:
Element Min Max
C - 0.2
Mn - 2
Ni 23 28
Cr 19 23
S - 0.3
Mo 4 5
N - 0.1
Cu 1 2
P - 0.03
Si - 0.7
MECHANICAL PROPERTIES OF ALLOY 904L:
Temper Annealed
Tensile Rm 71 ksi (min)
Tensile Rm 490 MPa (min)
R.p. 0.2% Yield 32 ksi (min)
R.p. 0.2% Yield 220 MPa (min)
Elongation (2†or 4D gl) 35 % (min)
PHYSICAL PROPERTIES OF ALLOY 904L
Specific Heat (0-100°C) 450 J.kg-1.°K-1
Thermal Conductivity 11.5 W.m -1.°K-1
Thermal Expansion 15.8 mm/m/°C
Modulus Elasticity 190 GPa
Electrical Resistivity 9.52 μohm/cm
Density 7.95 g/cm3