Temperature Resistance :

• Continuous- 80°C
• Intermittent- 100°C

Weatherability : Good
Flexibility :  Excellent
Abrasion Resistance : Moderate

Storage  :Up to 6 month in intact condition or sealed the containers are kept under cover in a dry place under normal temp.conditions.

Surface Preperation :
Steel : remove grease, oil & other contaminants preferably by using degreasing solvent. Blast clean to a minimum of Sa2 ½ Swedish std SIS 05 5900. For severe corrosion, blast to Sa 3 with a surface profile not exceeding 65 microns.
If blasting is not practical, make full use of mechanical tools along with manual chipping & wire brushing to remove loose rust & scale to st 2 swedish std SIS 05 5900. Excessive burning of steel is to be avoided. Thoroughly dust down all surfaces. Best results can be achieved if the manually cleaned surface is primed with protectomastic- self priming surface tolerant coating; otherwise treatment with metal conditioning solution will also produce satisfactory results.
The surface should be clean & dry before application of zinc phosphate primer.

Application : Mix the contents thoroughly before & during use.
Brush / Roller : Apply without thinning to the recommended dry film thickness.
Airless spray : Add up to 10-20% thinner. Use any standard equipment having pump ratio 30:1. Tip size 0.43-0.53 mm. Tip pressure 120-150 Kg/cm2

Note :

• Do not apply when temp.falls below 10°C or rises above 50°C & when relative humidity rises above 90%. Do not apply during rain Fog or mist.
• Brushes & Roller should be cleaned with thinner otherwise equipment is liable to be damaged.

Temperature Resistance :  Up to 650 Ë C dry heat
Weather ability : Excellent.
Flexibility : Moderate
Abrasion Resistance : Moderate

Storage Life : Up to Six months as long as the sealed containers are kept under cover in a dry place under normal temperature conditions.

Surface preparation : Make full use of mechanical tools along with manual chipping and wire brushing to remove loose rust and scale to St.2 Swedish Standard SIS 05 5900. Excessive burnishing of steel is to be avoided. Thoroughly dust down all surfaces. Best results can be achieved if the manually cleaned surface is treated with Bison Metal Conditioning Solution.
The surface should be clean and dry before application of H.R. paint

Notes :

• Application must be carried out on cold surfaces only after the final coat has dried completely; the painted surface may be gradually heated.
• The mixed paint must be used off within 48 hours for obtaining high lustrous finish.
• Do not apply when temperature falls below 10Ë C or rises above 50Ë C & when relative humidity rises above 90%.Do not apply during rain, fog or mist.

Health & Safety : Please refer to the separate safety data sheet available with detailed information.

Temperature Resistance :

• Continuous- 100Ëš C
• Intermittent- 150Ëš C

Weatherability : Excellent
Flexibility :  Good
Abrasion Resistance : Good

Storage Life : Up to 6 month in intact condition or sealed the containers are kept under cover in a dry place under normal temp.conditions.

Surface Preperation :
Steel : remove grease, oil & other contaminants preferably by using degreasing solvent. Blast clean to a minimum of Sa2 ½ Swedish std SIS 05 5900. For severe corrosion, blast to Sa 3 with a surface profile not exceeding 65 microns.
If blasting is not practical, make full use of mechanical tools along with manual chipping & wire brushing to remove loose rust & scale to st 2 swedish std SIS 05 5900. Excessive burning of steel is to be avoided. Thoroughly dust down all surfaces. Best results can be achieved if the manually cleaned surface is primed with protectomastic- self priming surface tolerant coating; otherwise treatment with metal conditioning solution will also produce satisfactory results.
The surface should be clean & dry before application of primer coat.

Concrete : new concrete- ensures that the concrete is cured for a minimum of 3 months. The surface is to be made rough & free from laitance & other contaminants by sand sweeping.
Old concrete- removes all salt deposits from the surface by water jet washing. Light sand blast the surface to remove all loosely bound coating & roughening up to firmly adhering coating to ensure anchorage with recommended system. Ensure all dust/ other particles are fully removed by suction or air blast & the surface is fully cleaned & dry before application of paint.
In non critical areas where blasting is not possible, water jet washing & hard wire brushing are minimum requisites.

Application :

• Stir base thoroughly & then mix 4 parts of base & 1 part of catalyst by volume to uniform consistency. Allow the mixture to mature for 30 minutes & stir again before application & during use.
• Brush / Roller: add up to 5% thinner if required during application.
• Conventional spray: add up to 15% thinner depending on conditions. Use only standard equipment at an atomizing pressure of 3.5-4.9 Kg/cm2.
• Airless spray: apply preferably without thinning. However up to 5% thinner may be added if absolutely essential depending on conditions. Use any standard equipment having pump ratio 30:1. Tip size 0.38-0.43mm.Tip pressure 110-160 Kg/cm2 .

Note :

• Use off the mixed paint within the specified pot life period.
• Do not apply when temp.falls below 10Ëš C or rises above 50Ëš C & when relative humidity rises above 90%. Do not apply during rain Fog or mist.
• Brushes & spray equipment should be cleaned with thinner otherwise equipment is liable to be damaged.

 After complete curing, the following tests should be carried :

Temperature Resistance

• Continuous- 90Ëš
• Intermittent- 120ËšC

Weatherability : Good
Flexibility :  Good
Abrasion Resistance : Moderate

Storage Life : Up to 6 month in intact condition or sealed the containers are kept under cover in a dry place under normal temperature conditions.

Surface Preparation :
Steel : remove grease, oil & other contaminants preferably by using degreasing solvent. Blast clean to a minimum of Sa2 ½ Swedish std. SIS 05 5900. For severe corrosion, blast to Sa 3 with a surface profile not exceeding 65 microns.
If blasting is not practical, make full use of mechanical tools along with manual chipping & wire brushing to remove loose rust & scale to St. 2 Swedish std. SIS 05 5900. Excessive burning of steel is to be avoided. Thoroughly dust down all surfaces. Best results can be achieved if the manually cleaned surface is primed with protectomastic- self-priming surface tolerant coating; otherwise, treatment with metal conditioning solution will also produce satisfactory results.
The surface should be clean & dry before application of primer coat.

Application :

• Mix the contents thoroughly before & during use.
• Apply with suitable thinner for the recommended dry film thickness.
• Brush / Roller: add up to 5% thinner if required during application.
• Conventional spray: add up to 15-20% thinner depending on conditions. Use only standard equipment at an atomizing pressure of 3.5-4.9 Kg/cm2.

Note :

• Do not apply when temperature falls below 10ËšC or rises above 50ËšC & when relative humidity rises above 90%. Do not apply during rain Fog or mist.
• Brushes & Roller should be cleaned with thinner otherwise, equipment is liable to be damaged.
• Primed steel work should not be exposed with one coat for a long period.

Temperature Resistance :

• Continuous- 80°C
• Intermittent- 100°C

Weatherability : Good
Flexibility :  Excellent
Abrasion Resistance : Moderate

Storage  :Up to 6 month in intact condition or sealed the containers are kept under cover in a dry place under normal temp.conditions.

Surface Preperation :
Steel : remove grease, oil & other contaminants preferably by using degreasing solvent. Blast clean to a minimum of Sa2 ½ Swedish std SIS 05 5900. For severe corrosion, blast to Sa 3 with a surface profile not exceeding 65 microns.
If blasting is not practical, make full use of mechanical tools along with manual chipping & wire brushing to remove loose rust & scale to st 2 swedish std SIS 05 5900. Excessive burning of steel is to be avoided. Thoroughly dust down all surfaces. Best results can be achieved if the manually cleaned surface is primed with protectomastic- self priming surface tolerant coating; otherwise treatment with metal conditioning solution will also produce satisfactory results.
The surface should be clean & dry before application of zinc phosphate primer.

Application : Mix the contents thoroughly before & during use.
Brush / Roller : Apply without thinning to the recommended dry film thickness.
Airless spray : Add up to 10-20% thinner. Use any standard equipment having pump ratio 30:1. Tip size 0.43-0.53 mm. Tip pressure 120-150 Kg/cm2

Note :

• Do not apply when temp.falls below 10°C or rises above 50°C & when relative humidity rises above 90%. Do not apply during rain Fog or mist.
• Brushes & Roller should be cleaned with thinner otherwise equipment is liable to be damaged.

Temperature Resistance :  Up to 650 Ë C dry heat
Weather ability : Excellent.
Flexibility : Moderate
Abrasion Resistance : Moderate

Storage Life : Up to Six months as long as the sealed containers are kept under cover in a dry place under normal temperature conditions.

Surface preparation : Make full use of mechanical tools along with manual chipping and wire brushing to remove loose rust and scale to St.2 Swedish Standard SIS 05 5900. Excessive burnishing of steel is to be avoided. Thoroughly dust down all surfaces. Best results can be achieved if the manually cleaned surface is treated with Bison Metal Conditioning Solution.
The surface should be clean and dry before application of H.R. paint

Notes :

• Application must be carried out on cold surfaces only after the final coat has dried completely; the painted surface may be gradually heated.
• The mixed paint must be used off within 48 hours for obtaining high lustrous finish.
• Do not apply when temperature falls below 10Ë C or rises above 50Ë C & when relative humidity rises above 90%.Do not apply during rain, fog or mist.

Health & Safety : Please refer to the separate safety data sheet available with detailed information.

Temperature Resistance :

• Continuous- 100Ëš C
• Intermittent- 150Ëš C

Weatherability : Excellent
Flexibility :  Good
Abrasion Resistance : Good

Storage Life : Up to 6 month in intact condition or sealed the containers are kept under cover in a dry place under normal temp.conditions.

Surface Preperation :
Steel : remove grease, oil & other contaminants preferably by using degreasing solvent. Blast clean to a minimum of Sa2 ½ Swedish std SIS 05 5900. For severe corrosion, blast to Sa 3 with a surface profile not exceeding 65 microns.
If blasting is not practical, make full use of mechanical tools along with manual chipping & wire brushing to remove loose rust & scale to st 2 swedish std SIS 05 5900. Excessive burning of steel is to be avoided. Thoroughly dust down all surfaces. Best results can be achieved if the manually cleaned surface is primed with protectomastic- self priming surface tolerant coating; otherwise treatment with metal conditioning solution will also produce satisfactory results.
The surface should be clean & dry before application of primer coat.

Concrete : new concrete- ensures that the concrete is cured for a minimum of 3 months. The surface is to be made rough & free from laitance & other contaminants by sand sweeping.
Old concrete- removes all salt deposits from the surface by water jet washing. Light sand blast the surface to remove all loosely bound coating & roughening up to firmly adhering coating to ensure anchorage with recommended system. Ensure all dust/ other particles are fully removed by suction or air blast & the surface is fully cleaned & dry before application of paint.
In non critical areas where blasting is not possible, water jet washing & hard wire brushing are minimum requisites.

Application :

• Stir base thoroughly & then mix 4 parts of base & 1 part of catalyst by volume to uniform consistency. Allow the mixture to mature for 30 minutes & stir again before application & during use.
• Brush / Roller: add up to 5% thinner if required during application.
• Conventional spray: add up to 15% thinner depending on conditions. Use only standard equipment at an atomizing pressure of 3.5-4.9 Kg/cm2.
• Airless spray: apply preferably without thinning. However up to 5% thinner may be added if absolutely essential depending on conditions. Use any standard equipment having pump ratio 30:1. Tip size 0.38-0.43mm.Tip pressure 110-160 Kg/cm2 .

Note :

• Use off the mixed paint within the specified pot life period.
• Do not apply when temp.falls below 10Ëš C or rises above 50Ëš C & when relative humidity rises above 90%. Do not apply during rain Fog or mist.
• Brushes & spray equipment should be cleaned with thinner otherwise equipment is liable to be damaged.

 After complete curing, the following tests should be carried :

Temperature Resistance

• Continuous- 90Ëš
• Intermittent- 120ËšC

Weatherability : Good
Flexibility :  Good
Abrasion Resistance : Moderate

Storage Life : Up to 6 month in intact condition or sealed the containers are kept under cover in a dry place under normal temperature conditions.

Surface Preparation :
Steel : remove grease, oil & other contaminants preferably by using degreasing solvent. Blast clean to a minimum of Sa2 ½ Swedish std. SIS 05 5900. For severe corrosion, blast to Sa 3 with a surface profile not exceeding 65 microns.
If blasting is not practical, make full use of mechanical tools along with manual chipping & wire brushing to remove loose rust & scale to St. 2 Swedish std. SIS 05 5900. Excessive burning of steel is to be avoided. Thoroughly dust down all surfaces. Best results can be achieved if the manually cleaned surface is primed with protectomastic- self-priming surface tolerant coating; otherwise, treatment with metal conditioning solution will also produce satisfactory results.
The surface should be clean & dry before application of primer coat.

Application :

• Mix the contents thoroughly before & during use.
• Apply with suitable thinner for the recommended dry film thickness.
• Brush / Roller: add up to 5% thinner if required during application.
• Conventional spray: add up to 15-20% thinner depending on conditions. Use only standard equipment at an atomizing pressure of 3.5-4.9 Kg/cm2.

Note :

• Do not apply when temperature falls below 10ËšC or rises above 50ËšC & when relative humidity rises above 90%. Do not apply during rain Fog or mist.
• Brushes & Roller should be cleaned with thinner otherwise, equipment is liable to be damaged.
• Primed steel work should not be exposed with one coat for a long period.