1 Products availableOur Complete range of products are Titanium Wire, Inconel X750 Round Bar, Alloy A286 Round Bar, Hastelloy X round bar and stainless steel 422 Round Bar.
STANDARD | WERKSTOFF NR. | UNS |
Inconel X750 | 2.4669 | N07750 |
Grade | Ni | Cr | Al | C | Mn | Ti | Cu | Si | S |
Inconel X-750 | 70.0 min | 14.0 - 17.0 | 0.40 - 1.0 | .08 max | 1.00 max | 2.25 - 2.75 | 0.50 max | .50 max | .01 max |
Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
8.28 g/cm3 | 1430°C | 1267 MPa | 868 MPa | 25 % |
STANDARD | WERKSTOFF NR. | UNS |
Hastelloy X | 2.4665 | N06002 |
Grade | Ni | Mo | Cr | Fe | Mn | C | Co | Si | P | S |
Hastelloy X | Balance | 8.00 - 10.00 | 20.50 - 23.00 | 17.00 - 20.00 | 1.00 max | 0.05 - 0.15 | 0.50 - 2.50 | 1.00 max | 0.04 max | 0.03 max |
Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
8.22 g/cm³ | 1355°C | 655 MPa | 240 MPa | 35% |
STANDARD | WERKSTOFF NR. | UNS | JIS | BS | GOST | AFNOR | EN |
SS 422 | 1.4742 | S42200 | SUS 422 | 442S19 | – | – | – |
Grade | C | Si | Ni | S | Mn | P | Cr | Mo | V | Cu | W | |
SS 422 | min. | 0.20 | 0.20 | 0.50 | - | - | - | 11.0 | 0.75 | 0.17 | - | 0.90 |
max. | 0.25 | 0.60 | 1.00 | 0.030 | 1.00 | 0.040 | 13.5 | 1.25 | 0.30 | 0.50 | 1.25 |
Grade | Tensile Strength (MPa) min | Elongation (% in 50mm) min | Yield Strength 0.2% Proof (MPa) min | Hardness | |
Rockwell B (HR B) max | Brinell (HB) max | ||||
Stainless Steel 422 | 115 | 25 | 140 | 293 | 341 |
STANDARD | WERKSTOFF NR. | UNS |
Nimonic 90 | 2.4632 | N07090 |
Grade | C | Cr | Co | Ti | Al | Si | Cu | Mn |
Nimonic Alloy 90 | 0.2 max | 18 - 21 | 15 - 21 | 2 - 3 | 1 - 2 | 1.0 max | 0.2 max | 1.0 max |
Density | Melting Point | Coefficient of Expansion | Modulus of Rigidity | Modulus of Elasticity (Annealed + Aged) (Spring Temper + Aged) |
8.18g/cm³ | 1370°C | 12.7 μm/m °C (20 - 100°C) | 82.5 kN/mm² | 213 kN/mm² 227 / 240 kN/mm² |
STANDARD | WERKSTOFF NR. | UNS | JIS | GOST | EN | OR |
Hastelloy C276 | 2.4819 | N10276 | NW 0276 | ХН65МВУ | NiMo16Cr15W | ЭП760 |
Grade | C | Mn | Si | S | Co | Ni | Cr | Fe | Mo | P |
C276 | 0.010 max | 1.00 max | 0.08 max | 0.03 max | 2.50 max | 50.99 min* | 14.50 – 16.50 | 4.00 – 7.00 | 15.00 – 17.00 | 0.04 max |
Element | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
Hastelloy C276 | 8.89 g/cm3 | 1370 °C (2500 °F) | Psi – 1,15,000 , MPa – 790 | Psi – 52,000 , MPa – 355 | 40 % |
STANDARD | UNS | WERKSTOFF NR. |
---|---|---|
ASTM A105 | K03504 | – |
Carbon Steel | C | Si | Mn | P | S | Cr |
---|---|---|---|---|---|---|
A105 | 0.35 | 0.10-0.35 | 0.60-1.05 | 0.035 | 0.040 | 0.30 |
Tensile Strength (N/mm2) | Elongation % | HB max |
---|---|---|
485 | 22 | 187 |
STANDARD | WERKSTOFF NR. | UNS | GOST | AFNOR | JIS | BS | EN |
Monel 400 | 2.4360 | N04400 | МНЖМц 28-2,5-1,5 | NU-30M | NW 4400 | NA 13 | NiCu30Fe |
Grade | C | Mn | Si | P | S | Cr | Mo | Ni | W |
Monel 400 | 0.010 max | 0.50 max | 0.08 max | 0.02 max | 0.02 max | 20 - 22.5 | 12.5 - 14.5 | Bal | 2.5 - 3.5 |
Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
8.69 g/cm3 | 1399 °C (2550 °F) | Psi – 1,00,000, MPa–690 | Psi – 45000, MPa–310 | 45 % |
Grade | C | Mn | Si | S | Cu | Fe | Ni | Cr |
Inconel X750 | 0.08 max | 1.00 max | 0.5 max | 0.01 max | 0.5 max | 9.0 max | 70.0 min | 17 max |
STANDARD | WERKSTOFF NR. | UNS |
Inconel X750 | 2.4669 | N07750 |
Grade | C | Mn | Si | S | Cu | Fe | Ni |
Inconel X-750 | 0.08 max | 1.00 max | 0.5 max | 0.01 max | 0.5 max | 5.0-9.0 | 70 max. |
STANDARD | WERKSTOFF NR. | UNS |
Inconel X-750 | 2.4669 | N07750 |
Grade | Ni | Cr | Co | Ti | Al | C | Si | Cu | Fe | Mn | B | S | Zr | Pb |
Nimonic 90 | Bal | 18-21 | 15-21 | 2-3 | 1-2 | 0.2 max | 1.0 max | 0.2 max | 1.5 max | 1.0 max | 0.02 max | 0.015 max | 0.15 max | 0.0020 max |
Grade | Material Sheet |
Temperature °C | Yield Strength 0.2 % (MPa) | Tensile Strength (MPa) | Elongation (%) | Hardness HV |
Nimonic 90 | Nimonic 90 sheet Solution Treated (BS HR202) |
RT | – | – | – | 250 max |
Nimonic 90 sheet Precipitation Treated (BS HR 202) |
RT | 695 min | 1080 min | 25 min (0.45mm-3.0mm) |
280 min | |
Nimonic 90 sheet Precipitation Treated (BS HR202) |
500 | 740 (typical) | 995 (typical) | 30 | – | |
Alloy 90 Cold Rolled Sheet (Heat Treated) |
– | – | – | – | – |
STANDARD | WERKSTOFF NR. | UNS |
Nimonic 90 | 2.4632 | N07090 |
STANDARD | WERKSTOFF NR. | UNS |
Monel R405 | – | N04405 |
Grade | Fe | C | Ni | Mn | Si | S | Cu | Al |
Monel R405 | 2.5 max | 0.3 max | 63 min | 2.0 max | 0.5 max | 0.025 – 0.060 | 28.0-34.0 | – |
STANDARD | WERKSTOFF NR. | UNS |
Monel K500 | 2.4375 | N05500 |
Grade | Ni | Fe | C | Mn | Si | Cu | Al | S | Ti |
Monel K500 | 63.0 min | 0.5 – 2 | 0.25 max | 1.5 max | 0.5 max | 27.0 – 33.0 | 2.3 – 3.15 | 0.010 max | 0.35 – 0.85 |
Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
8.44 g/cm3 | 1350 °C (2460 °F) | Psi – 160000 , MPa – 1100 | Psi – 115000 , MPa – 790 | 20 % |
STANDARD | WERKSTOFF NR. | UNS |
---|---|---|
Nimonic Alloy 75 | – | N06075 |
Grade | C | Ni | Cu | Cr | Ti | Fe | Mn |
---|---|---|---|---|---|---|---|
Nimonic Alloy 75 | 0.08 / 0.15 | Bal | 0.5 max | 18.9 – 21.0 | 0.2 / 0.6 | 5.0 max | 1.0 max |
Mechanical & Physical Properties | 21.1°C | 100°C | 204.4°C | 315.6°C | 400 °C | 537.8°C | 648.9°C | 700°C | 760 °C | 815 °C | 870 °C | 982 °C |
---|---|---|---|---|---|---|---|---|---|---|---|---|
Ultimate Tensile Strength /MPa | 792 | – | – | – | – | 726 | 473 | – | 286 | – | 139 | 66 |
0.2% Yield Strength /MPa | 407 | – | – | – | – | 363 | 275 | – | 152 | – | 68 | 31 |
Elongation % | 31 | – | – | – | – | 27 | 32 | – | 75 | – | 90 | 91 |
1,000 hr Rupture Strength | – | – | – | – | – | – | 83 | 47 | 26 | 15 | 8.3 | – |
Coefficient of Thermal Expansion /µm/m°C ** | – | 11 | 12.7 | 13.4 | 13.9 | 14.3 | 15 | 15.4 | – | 16.5 | 17.1 | 18.2 |
Thermal Conductivity /kcal/(hr.m.°C) ** | 10.06 | – | – | – | – | – | – | – | – | – | – | – |
Modulus of Elasticity / GPa | 221 | 216 | 210 | 203 | 197 | 190 | 181 | 173 | – | 165 | 153 | 140 |
STANDARD | WERKSTOFF NR. | UNS |
---|---|---|
Nimonic Alloy 80A | 2.4631 | N07080 |
Grade | C | Ni | Cu | Cr | Ti | Fe | Mn |
---|---|---|---|---|---|---|---|
Nimonic Alloy 80A | 0.10 max | Bal | 0.2 max | 18.0-21.0 | 1.8-2.7 | 3.0 max | 1.0 max |
Ultimate Tensile Strength (N/mm²) | Proof Stress (N/mm²) | Elongation (%) | Hardness (HB) |
---|---|---|---|
1000 | 620 | 20 | – |
STANDARD | WERKSTOFF NR. | UNS |
---|---|---|
Nimonic Alloy 263 | 2.4650 | N07263 |
Grade | C | Cr | Co | Ti | Al | Si | Cu | Mn |
---|---|---|---|---|---|---|---|---|
Nimonic Alloy 263 | 0.04-0.08 | 19 – 21 | 19 – 21 | 1.90 – 2.40 | 0.60 max | 0.40 max | 0.20 max | 0.60 max |
Mechanical properties | Test Method | As Built | Heat Treated |
---|---|---|---|
Tensile strength | ISO 6892-1:2009(B) Annex D | 900 ± 40 MPa | 1100 ± 30 MPa |
Yield strength (Rp 0.2 %) | ISO 6892-1:2009(B) Annex D | 650 ± 40 MPa | 800 ± 30 MPa |
Elongation at break | ISO 6892-1:2009(B) Annex D | 40 ± 5 % | 35 ± 5 % |
Young’s Modulus | – | 220 ± 15 MPa | 220 ± 15 MPa |
Nickel Alloy 200/201 Bars Equivalent Grades
STANDARD | UNS | WNR. | JIS | EN |
---|---|---|---|---|
Nickel 200 | N02200 | 2.4066 | NW 2200 | Ni 99.2 |
Nickel 201 | N02201 | 2.4068 | NW 2201 | LC-Ni 99 |
Nickel Alloy 200/201 Round Bar Chemical Composition
Grade | C | Mn | Si | S | Cu | Fe | Ni |
---|---|---|---|---|---|---|---|
Nickel 200 | 0.15 max | 0.35 max | 0.35 max | 0.01 max | 0.25 max | 0.40 max | 99.0 min |
Nickel 201 | 0.02 max | 0.35 max | 0.35 max | 0.01 max | 0.25 max | 0.40 max | 99.0 min |
Nickel Alloy 200/201 Round Bars Mechanical Properties
Grade | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
---|---|---|---|---|---|
Nickel 200 | 8.9 g/cm3 | 1446 °C (2635 °F) | Psi – 67000 , MPa – 462 | Psi – 21500 , MPa – 148 | 45 % |
Nickel 201 | 8.9 g/cm3 | 1446 °C (2635 °F) | Psi – 67000 , MPa – 462 | Psi – 21500 , MPa – 148 | 45 % |
Standard | AISI / SAE 4130 |
UNS | - |
WERKSTOFF NR. | 25CrMo4, GS-25CrMo4 |
BS 970 | 708A30, CDS110 |
UNI | 25CrMo4 (KB), 30CrMo4 |
JIS | SCM 420, SCM 430, SCCrM1 |
EN name | - |
EN # | 1.7218 |
Grade | C | Si | Mn | Cr | Mo | P | S |
AISI 4130 | 0.28-0.33 | 0.15-0.35 | 0.4-0.8 | 0.8-1.1 | 0.15-0.25 | 0.035 | 0.04 |
Grade | Delivery State | T.S. N/mm2 Min |
Y.S. N/mm2 Min |
A,% Min |
Z,% Min |
Hardness, (annealing or tempering) HB,max |
Forging ratio | Grain Size (level) |
Nonmetal ratio |
AISI 4130 | Hot rolled, forged, or heat treatment | 930 | 735 | 12 | 50 | 229 | ≥ 4:1 | ≥ 6 | ≤ 2.0 |
Standard | AISI / SAE 4340 |
UNS | - |
WERKSTOFF NR. | 34CrNiMo6, 40NiCrMo8-4 |
BS 970 | 817M40, En24 |
UNI | 35NiCrMo6 (KB), 40NiCrMo7 (KB) |
JIS | SNCM 447, SNB24-1-5 |
EN name | 34CrNiMo6 |
EN # | 1.6582, 1.6562 |
C | Mn | Si | S | P | Cr | Ni | Mo | |
SAE - 4340 | .38- .43 | .60 - .80 | .15 - .35 | .035 MAX | .040 MAX | .70 - .90 | 1.65 -2.00 | .20 - .30 |
Tensile strength kgf/mm² | Yield strength kgf/mm² | Elongation % | Cross section reduction rate % | Impact value | Hardness Hb |
---|---|---|---|---|---|
≧100 | ≧90 | ≧16 | ≧45 | ≧7 | 293~352 |
STANDARD | UNS | WERKSTOFF NR. |
ASTM A350 LF2 | K03011 | 1.0508 |
Grade | C | Ni | Si | S | Mn | P | |
ASTM A350 LF2 | min. | - | - | 0.17 | - | 0.6 | - |
max. | 0.30 | 0.40 | 0.37 | 0.040 | 1.35 | 0.035 |
Grade | Tensile Strength (ksi) min | Elongation (% in 50mm) min | Yield Strength 0.2% Proof (ksi) min | Hardness |
ASTM A350 LF2 | 485 | 22 | 250 | 197 |
STANDARD | WERKSTOFF NR. | UNS |
Duplex S31803 | 1.4462 | S31803 |
Grade | UNS No | C % | Cr % | Ni % | P % | Si % | S % | Mo % | N % | Mn % |
31803 | S31803 | < 0.03 | 21.0-23.0 | 4.5-6.5 | 1.03 max | 1 max | 0.02 max | 2.5-3.5 | 0.08-0.2 | < 2.0 |
Grade | YS (MPa) | UTS (MPa) | % Elongation | Hardness(BHN) |
31803 | 450 min. | 620 min. | 25 min. | 293 max. |
C | P | Mo | Mn | S | Cr | Si | Ni | |
EN - 24 | .35 - .45 | .040 | .20 - .40 | .45 - .70 | .040 | .90 - 1.40 | .10 - .35 | 1.30 - 1.80 |
Max Stress | 850-1000 n/mm2 | |
Yield Stress | 680 n/mm2 Min | Up to 150mm LRS |
654 n/mm2 Min | 150 to 250mm LRS | |
0.2% Proof Stress | 665 n/mm2 Min | Up to 150mm LRS |
635 n/mm2 Min | 150 to 250mm LRS | |
Elongation | 13% Min | (9% if cold drawn) |
STANDARD | WERKSTOFF NR. | UNS |
Hastelloy B2 | 2.4617 | N10665 |
Grade | Ni | Mo | Cr | Fe | Mn | C | P | S | Si |
Hastelloy B2 | Bal | 26 - 30 | 1.0 | - | 0.1 | 0.02 | 0.04 | 0.03 | 0.1 |
Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
9.2 g/cm3 | 1370 °C (2550 °F) | Psi – 1,15,000 , MPa –760 | Psi – 52,000 , MPa – 350 | 40% |
STANDARD | WERKSTOFF NR. | UNS |
2205 Duplex | 1.4462 | S32205 |
Grade | UNS No | C % | Cr % | Ni % | P % | Si % | S % | Mo % | N % | Mn % |
2205 | S32205 | < 0.03 | 22.0-23.0 | 4.5-6.5 | 0.03 max | 1 max | 0.02 max | 3.0-3.5 | 0.14-0.20 | < 2.0 |
Grade | YS (MPa) | UTS (MPa) | % Elongation | Hardness(BHN) |
2205 | 450 min. | 655 min. | 25 min. | 293 max. |
STANDARD | WERKSTOFF NR. | UNS |
Hastelloy B3 | 2.4600 | N10675 |
Grade | Ni | Mo | Cr | Fe | W | Mn | C | Al | Ti | Si |
Hastelloy B3 | 65.0 min | 28.5 | 1.5 | 1.5 | 3.0 max | 3.0 max | 0.01 max | 0.50 max | 0.2 max | 10 max |
Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
9.2 g/cm3 | 1370 °C (2550 °F) | Psi – 1,15,000 , MPa –760 | Psi – 52,000 , MPa – 350 | 40% |
STANDARD | UNS | DIN |
CS EN-9 Round Bar | - | - |
Grade | C | Cr | Ni | Si | S | Mn | P | Mo |
EN - 9 | .50 - .60 | - | - | .05 - .35 | .040 MAX | .50 - .80 | .040 MAX | - |
Heat Treatment | Condition Tons/SQ.inch | Tensile Stress RE MPA | RP0.2 MPA | A min on 5.65so | Impac | Hardness HB | Limited Ruling Section mm | |
IZODFT.L.b | KCV Joules | |||||||
Normalise | 45 | 700 | - | 12 | - | - | 201-255 | 63 |
39 | 600 | - | 13 | - | - | 170/223 | 250 | |
R | 45/55 | 700/850 | 385 | 14 | - | - | 201/277 | 100 |
S | 50/60 | 775/925 | 450 | 14 | - | - | 223/277 | 63 |
T | 55/65 | 850/1000 | 555 | 12 | - | - | 248/302 | 19 |
STANDARD | WERKSTOFF NR. | UNS |
Hastelloy C4 | 2.4610 | N06455 |
Grade | Ni | Mo | Cr | Fe | Co | Mn | C | Al | Ti | Si |
Hastelloy C4 | 65.0 min | 14 - 17 | 14 - 18 | 3.0 max | 2.0 max | 1.0 max | 0.01 max | - | 0.7 max | 0.08 max |
Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
8.64 g/cm3 | 1350-1400 °C | 783 | 365 | 55% |