Anodizing Color in Mumbai

• Coating Thickness : 10-25 microns
• Temperatures : 55 – 60 C
• Heat Fastness : Good
• Time : 10-15 Minute.
• Buffer : the bath must be buffered with
• pH : 5.5 +- 0.5
• Physical Form : Dry Powder
• Appearance : Dark Red Powder
• Water Quality : preferably de –ionized; dyeing is also possible in tap water, but this can reduce the service life of dye bath
• Concentration : 4- 5 g/l

 Alumon Red A3LW is azo dye, used to give a fire red shade.   SEALING: The dyed oxide film must be properly sealed properly using a hot sealing salt ANO SEAL CA-350 for best result. Other Recommendation: 1) Ammonium compounds shall not be used for controlling of the pH or to buffer dye         bath s more...

• Appearance : Dark Blue Powder
• Buffer : the bath must be buffered with 8 g/l sodium acetate tri hydrate 0.4 ml/l acetic acid for pH 5.5
• Water Quality : preferably de –ionized; dyeing is also possible in tap water, but this can reduce the service life of dye bath
• pH : 5.5 +- 0.5
• Light Fatness : excellent
• Heat Fastness : excellent
• Concentration : 3 – 4 g/l
• Chemical Class : Phthalocyanine.
• Coating Thickness : 10-25 microns
• Temperatures : 55 – 60 C

Alumon Turq. Blue A2SG is a powder dye recommended for panels, signs and labels. It can be also used for Jewellery application.     1) Ammonium compounds shall not be used for controlling of the pH or to buffer dye         bath solution. 2) The presence of ammonium compounds in the sealing solution m more...

• Anodic coating thickness : 10 - 25 microns.
• pH range : 4.5 - 6.0
• Heat fastness : Excellent.
• Chemical description : metalized azo dyes
• Physical appearance : Black to dark grey powder
• Immersion time : 10 – 20 minutes
• Concentration : 5 - 8 g/l
• Buffering : Sodium Acetate or Acetic Acid
• Light fastness : 8+
• Dye bath temperature : 50° - 60° C

Alumon Black 3 is  a single component black dye suitable for exterior application. The dye bath is stable against contamination by drag-in of sulfates or aluminum salts from the anodizing electrolyte.   The dyed oxide film must be properly sealed properly using a hot sealing salt ANO SEAL CA-350 for best re more...