1 Products availableOur product range contains a wide range of Copper Alloy Hollow
We offer Cupro Nickel Rods in two grade such as 90/10 and 95/5, which is widely used in heat exchanger /condenser application. Our range of Cupro Nickel Rods is available in different specifications as per the clients requirements. These Cupro Nickel Rods are manufactured in compliance with the international standards that ensure high performance.
Popular for :| Chemical Properties | |
| Pb | 0.05 Max. |
| Fe | 1.00 - 1.80 |
| Mn | 1.00 Max. |
| Zn | 1.00 Max. |
| Chemical Properties | |
| Sn | 0.10 Max. |
| Pb | 0.05 Max |
| Ni | 4.00 - 5.00 |
| Fe | 0.10 Max. |
| Mn | 0.25 Max. |
| As | 0.10 Max. |
| Cu + Ag | 95.00 - 96.000 |
| Sb | 0.01 Max. |
| Bi | 0.0025 Max. |
| Mechenical Properties Light Drawn | |
| Flattening Test | Reqd. (After 'O') |
| U.T.S. ksi | 45.00 Min |
| Y.S. at 0.5% Ext. ksi | 35.00 Min. |
| Expansion Test 30% at 60 degree Reqd. (After 'O') | |
| Mechenical Properties Annealed | |
| U.T.S. MPa | 216 - 275 (Strip cut from Ring Tube) |
| %Elongation at 5.65Sq.Rt So G.L. | 40.00 Min. (Strip cut from Ring Tube) |
| Flattening Test | Reqd. |
| Bend Test | Reqd. (180 degree close) |
| Annealed Temper | |
| Flattening Test | Reqd. |
| Grain Size at 75 X mm Avg. | 0.010 - 0.045 |
| U.T.S. ksi | 40.00 Min. |
| Y.S. at 0.5% Ext. ksi | 15.00 Min |
| Expansion Test 30% at 60 degree Reqd. | |
We are engaged in the Manufacturing and Exporting of Admiralty Brass Tube that are extensively used for various industrial applications. These tubes are high on demand in the global market for their high strength combined with good corrosion resistance and low susceptibility to stress corrosion cracking. Features : High strengthGood corrosion resistanceExcellent flexibilityEasy joiningDimensionally accurate Specifications : Outside diameter : 5.0mm(min)-133mm(max)Wall thickness : 0.5mm (min)Length : 15000 mm (max) Applications : Air coolersWater heatersTurbine oil coolersShip buildingPetrochemicalsGenerator
| As Manufactured | As Manufactured-1 | As Manufactured-2 | As Manufactured-3 | As Manufactured-4 | As Manufactured-5 | |
|---|---|---|---|---|---|---|
| %Elongation at 5.65Sq.Rt So G.L. | 12.00 Min. | 12.00 Min.. | 16.00 Min. | 18.00 Min. | 20.00 Min. | 22.00 Min. |
| U.T.S. N/mm Sq. | 500 Min. | 460 Min. | 380 Min. | 350 Min. | 320 Min. | 280 Min |
| 0.2% P.S. N/mm sqr. | 410 Min. | 380 Min. | 320 Min. | 250 Min. | 200 Min. | 120 Min. |
| Size | Over 6 mm to 18 mm | Over 18 mm to 40 mm | Over 40 mm to 60 mm | Over 60 mm to 80 mm | Over 80 mm to 100 mm | Over 100 mm to 120 mm |
Specifications
| Electrical Tough pitch high conductivity copper | 99.90% min copper 0.03 max impurities (excl. Oxygen & Silver) |
|---|---|
| Phosphorus De-Oxidised non arsenical copper | 99.85% min copper 0.013-0.050% phosphorus 0.06% max impurities |
| Oxygen free high conductivity copper | 99.95% min copper 0.03% max impurities (excl. Oxygen & silver) |
| Oxygen free high conductivity copper | 99.99% min copper 0.0050% man impurities |
| Silver Bearing copper | 99.99% min copper, 0.085% silver, 0.03% max impurities |
| Free Machining copper sulphur | 0.03-0.60% sulphur, 0.2% max impurities reminder copper |
| Free Machining copper tellurium | 0.03-0.70% tellurium, 0.2% max impurities reminder copper |
Specifications
| Cartridge Brass | 70% Copper, 30% Zinc |
|---|---|
| Basis Brass | 63% Copper, 37% Zinc |
| Naval Brass | 62% Copper, 37% Zinc 1% Tin |
| High Tensile Brasses | 58% Copper, 39% Zinc 0.6% Tin, 1% Aluminum, 0.7% Iron, 1% Manganese |
| High Tensile Brasses | 58% Copper, 39% Zinc 0.6% Tin, 0.1% Max, Aluminum, 0.7% Iron 1% Manganese |
| Free Machining Brass | 58% Copper, 30% Zinc, 3% Lead |
| Arsenical Brass | 70% Copper, 30% Zinc, 0.04% Lead |