1 Products availableOur product range contains a wide range of Spheroidal Graphite Cast Iron Rolls, Definite Chilled Iron Rolls, definite chilled rolls and Indefinite Chilled Cast Iron Rolls
Based in Punjab, we are a renowned Manufacturer and Supplier of Spheroidal Graphite Cast Iron Rolls. Spheroidal Graphite Cast Iron Rolls are developed using S. G. Iron or ductile iron in compliance with the set industry norms and standards. Their matrix structure varies from Ferrito-Pearlitic, Pearlitic to Bainitic & Martensitic together with different carbide contents and graphite in the form of spheroids/nodules. They are extensively used as roughing, intermediate rolls and finishing rolls for slabbing and blooming mills, rail and structural mils and wire rod and narrow strip mils. We make available Spheroidal Graphite Cast Iron Rolls in a wide range of hardness and composition for a variety of applications.
Additional Information:
Packaging Details : null
Chemical Composition
Matrix | Hardness Shore D | C | Mn | Si | P | S | Ni | Cr | Mo | UTS Kg/sq.mm |
---|---|---|---|---|---|---|---|---|---|---|
Pearlitic | 40 – 50 | 3.0/3.3 | 0.3/0.6 | 1.5/2.3 | 0.10 Max | 0.015 Max | 1.5/2.0 | 0.30 Max | .25/.4 | 50-65 |
Pearlitic | 50 – 60 | 3.0/3.3 | 0.3/0.6 | 1.5/2.3 | 0.10 Max | 0.015 Max | 1.5/2.0 | 0.40 Max | .25/.4 | 50-60 |
Pearlitic | 60-70 | 3.10/3.50 | 0.5/1.0 | 1.3/1.8 | 0.10 Max | 0.015 Max | 1.5/2.5 | 0.3/0.8 | 0.3/0.6 | 50-60 |
Pearlitic | 70-75 | 3.10/3.50 | 0.5/1.0 | 1.3/1.8 | 0.10 Max | 0.015 Max | 1.5/2.5 | 0.3/0.8 | 0.3/1.6 | 40–60 |
Bainitic Acicular | 40 – 50 | 3.0/3.3 | 0.3/0.5 | 1.80/2.30 | 0.080 Max | 0.015 Max | 2.0/3.0 | 0.20 Max | 0.6/0.9 | 60-70 |
Bainitic Acicular | 50 – 60 | 3.0/3.3 | 0.3/0.5 | 1.80/2.30 | 0.080 Max | 0.015 Max | 2.0/3.0 | 0.50 Max | 0.7/1.0 | 55-70 |
Bainitic Acicular | 60-70 | 3.10/3.50 | 0.5/0.8 | 1.3/2.0 | 0.080 Max | 0.015 Max | 2.0/3.5 | 0.3/0.8 | 0.8/1.20 | 50–70 |
Bainitic Acicular | 70-80 | 3.10/3.50 | 0.5/0.8 | 1.3/2.0 | 0.080 Max | 0.015 Max | 2.5/4.5 | 0.3/0.8 | 0.8/1.20 | 50–70 |
We bring forth precision-engineered Definite Chilled Iron Rolls for industrial applications. White graphite free structure of these rolls consists of eutectic carbide and transformed austentite. This gives a hard layer which confers good resistance to wear. The core and neck are made upon steel shaft in specialized double poured centrifugally cost chill Rollers barrels. Our Definite Chilled Iron Rolls are less soft, strong and incapable of withstanding high dynamic stresses. Owing to their greater hardness, these rolls have better wear-resistance and high compressive strength. Definite Chilled Iron Rolls are made available in customized specifications to meet diverse requirements. Also, they are budget-friendly. Applications :
Chemical Composition
Hardness Shore C | C | Mn | Mn | Si | P | S | Ni | Cr | Mo | Uts kgmf/mm2 |
---|---|---|---|---|---|---|---|---|---|---|
50-60 | 3.00/3.20 | 0.60/0.90 | 0.60/0.90 | 1.00/1.50 | 0.15 Max. | 0.06 Max. | 1.00/1.50 | 0.80/1.20 | 0.25/0.40 | 35-45 |
60-70 | 3.00/3.30 | 0.60/0.90 | 0.60/0.90 | 1.00/1.50 | 0.15 Max. | 0.06 Max. | 1.50/2.00 | 0.80/1.20 | 0.25/0.40 | 35-45 |
70-75 | 3.10/3.50 | 0.60/0.90 | 0.60/0.90 | 1.00/1.50 | 0.15 Max. | 0.06 Max. | 1.70/2.50 | 0.80/1.20 | 0.25/0.40 | 35-45 |
The working surface ofMahalaxmi Rolls Castingsshows the white graphite free structure consisting of eutectic carbide and transformed austentite. This gives a hard layer which confers good resistance to wear. The core and neck are made upon steel shaft in specialized double poured centrifugally cost chill Rollers barrels. Compared to grey iron, whiteMahalaxmi Rolls Castingsis less soft, strong and incapable of withstanding high dynamic stresses, but owing to its greater hardness, has better wear-resistance, and has high compressive strength. It retains a fair proportion of its strength at elevated temperature, for example, in hot rolling. These make excellent work steel re-rolling mills, semi-automatic or Automatic plants, Wire roll plants, TMT plants, Roughing mill Rollers, Intermediate mill Rollers for two, three and four-high mills, turning out of high grade ferrous and non-ferrous sheet and strip or section. High AlloyMahalaxmi Rolls Castingshave proved well
Chemical Composition
Grade | C | Mn | Si | P | S | Ni | Cr | Mo | UTSKgmf/mm² |
---|---|---|---|---|---|---|---|---|---|
50-60 | 3.00/3.20 | 0.60/0.90 | 1.10/1.50 | 0.15Max. | 0.06Max. | 1.50/1.80 | 0.80/1.20 | 0.25/0.35 | 35-45 |
60-70 | 3.00/3.30 | 0.60/0.90 | 1.00/1.50 | 0.15Max. | 0.06Max. | 1.50/2.50 | 0.80/1.20 | 0.25/0.40 | 35-45 |
70-75 | 3.10/3.50 | 0.60/0.90 | 1.00/1.30 | 0.15Max. | 0.06Max. | 2.00/3.00 | 0.80/1.20 | 0.30/0.45 | 35-45 |