Tempered glass starts life as float glass. Float glass, when shattered breaks into large pieces and can be harmful; it is therefore unsuitable for applications. In the tempering process, the surfaces of the glass are heated in a furnace nearly over 670C.
The hot glass is then cooled rapidly by a blast of air over a period of between 3 and 10 seconds. As a result, the surfaces shrink, and tensile stresses develop on the surfaces.
Tempered glass is 5 times stronger glass than normal glass. It provides greater thermal strength. It offers increased resistance to both sudden temperature changes and temperature differentials up to 250C (as against 40C of normal glass).
Tempered glass is difficult to break. However if it does break under high impact, only small fragments without any sharp edges are formed.
Architectural Faades, Windows, Partitions
AutomotiveSide Window Glass, Windscreens, Back Glass
IndustrialLightning, White Goods, Modular Kitchen
SolarSolar Panels
Two or more liters of glass are assembled and separated at a fixed interval using an aluminum spacer filled with a drying agent called desiccants to absorb the moisture within air space.
The surrounding edges of the double glazed units are then sealed first by a primary sealant and then by secondary sealant.
Tinted glass | Reflective glass |
Low E glass with max emissivity k = 0.08 |
4 mm | 5 mm | 6 mm | 8 mm |
10 mm | 12 mm |
Krypton Gas | Xenon Gas | Argon Gas |
5.5 mm | 9.5 mm | 14.5 mm | 19.5 mm | 6.5 mm |
10.5 mm | 15.5 mm | 21.5 mm | 7.5 mm | 11.5 mm |
16.5 mm | 23.5 mm | 8.5 mm | 13.5 mm | 17.5 mm |
Minimum | 300mm x 300mm |
Maximum | 1500mm x 2000mm |
Triangle | Trapezium | Pentagon |
Doubled glazed unit | Triple glazed unit | Step glazing |
Heat Strengthened glass follows almost the same process as tempered glass, except that the annealed glass is heated to a slightly lower temperature of 620C and the volume and pressure of cooling process is less rapid.