1 Products availableOur Complete range of products are brass brazing alloys, Silver Brazing Alloys (Cadmium Free Grade), Silver Brazing Alloys (Cadmium Bearing Grade) and Copper Phosphorus Brazing Alloys.
Details :
Technical Details
Grade | Nominal Composition % | Melting Range | Operating Temp. | Density | Tensile Strength | International Standard | |||||||
Cu | Zn | Si | Others | oc | oc | g/cm3 | N/mm2 | IS 2927 | BS 1845 | AWS A5.8 | DIN 851 3 | DIN EN 1044 | |
Rajat : SC-6 | 60 | 39.7 | 0.3 | - | 890-900 | 900 | 8.4 | 370 | SCB | CZ6 | - | L-CuZn40 | CU301 |
Rajat : SC-8 | 60 | 39.6 | 0.2 | 0.2Mn | 900-915 | 8.4 | - | SCB | - | - | - | - | |
SBR | 54 | 46 | - | - | 880-890 | 890 | 8.3 | - | - | - | - | L-CuZn46 | - |
SBR-60 | 59 | 39.7 | 0.2 | 1 Sn | 888-999 | 900 | 8.4 | 400 | - | - | RBCuZn45 | - | - |
Details :
Technical Details
Grade | Nominal Composition % | Melting Range | Operating Range | Density | Tensile Strength | International Standard | |||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|
Silver Brazing Alloy | Ag | Cu | Zn | Others | C | Degree C | g/cm2 | N/mm2 | IS 2927 | BS 1845 | AWS A5.8 | DIN 8513 | DIN EN 1044 |
Rajat : 1209/93 | 92.5 | 7.3 | - | 0.20Li | 760-890 | 930 | 10.2 | - | BACuAgO | - | Bag-19 | - | - |
Rajat : 1208/85 | 85 | - | - | 15 mn | 960-970 | 960 | 9.4 | - | - | AG19 | Bag-23 | L-Ag85 | AG501 |
Rajat : 1208/83 | 83 | 15 | 2 | - | 780-830 | 830 | 10.2 | - | - | - | - | L-Ag83 | - |
Rajat : 1207/75 | 75 | 22 | 3 | - | 740-775 | 770 | 10 | - | BACuAg2 | - | - | L-Ag75 | - |
Rajat : 1207/72 | 72 | 28 | - | - | 779 | 780 | 10 | 350 | BACuAg3 | AG7 | Bag-8 | L-Ag72 | AG401 |
Rajat : 1207/70 | 70 | 20 | 10 | - | 690-740 | 790 | 9.8 | - | - | - | Bag-10 | - | - |
Rajat : 1206/67 | 67 | 23 | 10 | - | 700-730 | 730 | 9.7 | - | - | - | - | L-Ag67 | - |
Rajat : 1206/65 | 65 | 20 | 15 | - | 690-720 | 720 | 9.7 | 400 | - | - | Bag-9 | L-Ag64 | AG201 |
Rajat : 1206/63 | 63 | 283.5 | - | 2.5 Ni, 6Sn | 690-800 | 850 | 9.9 | - | - | - | Bag-21 | - | - |
Rajat : 1206/61 | 61 | 29 | 10 | - | 690-735 | - | - | - | BACuAg6 | - | - | - | - |
Rajat : 1206/60 | 60 | 23 | 14 | 3Sn | 620-735 | 680 | 9.6 | 480 | - | - | - | L-Ag60Sn | AG101 |
Rajat : 1206/60 | 60 | 26 | 14 | - | 695-730 | 710 | 9.5 | 450 | - | AG13 | - | L-Ag60 | AG202 |
Rajat : 1206/60 | 60 | 30 | - | 10Sn | 600-720 | 720 | 9.8 | 420 | BACuAg7 | - | Bag-18 | - | - |
Rajat : 1205/56 | 56 | 22 | 17 | 5Sn | 620-650 | 650 | 9.5 | 410 | BACuAg8 | - | Bag-7 | - | AG102 |
Rajat : 1205/55 | 55 | 21 | 22 | 2Sn | 620-660 | 650 | 9.4 | 390 | - | AG14 | - | L-Ag55Sn | AG103 |
Rajat : 1205/56 | 56 | 42 | - | 2 Ni | 770-895 | 925 | 9.8 | - | - | - | Bag-13a | - | - |
Rajat : 1205/54 | 54 | 40 | 5 | 1Ni | 718-857 | 910 | 9.7 | - | BACuAg8b | - | Bag-13 | - | - |
Rajat : 1205/50 | 50 | 20 | 28 | 2 Ni | 660-750 | 780 | 9 | 450 | - | - | Bag-24 | - | - |
Rajat : 1205/50 | 50 | 34 | 16 | - | 688-774 | - | 9.4 | - | BACuAg9 | - | Bag-6 | - | - |
Details
Grade | Nominal Composition % | Melting Range | Operating Range | Density | Tensile Strength | International Standard | |||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|
Silver Brazing Alloy | Ag | Cu | Zn | Others | C | Degree C | g/cm2 | N/mm2 | IS 2927 | BS 1845 | AWS A5.8 | DIN 8513 | DIN EN 1044 |
RAJAT : 1204/45 | 45 | 27 | 25 | 3Sn | 640-680 | 670 | 9.2 | 350 | - | - | Bag-36 | L-Ag-45sn | AG104 |
RAJAT : 1204/45 | 44 | 30 | 25 | 670-740 | 730 | 9.1 | 545 | BACuAg14 | AG15 | Bag-5 | L Ag44 | AG203 | |
RAJAT : 1204/43 | 43 | 37 | 20 | 700-775 | 760 | 9.1 | 400 | BACuAg16 | AG5 | ||||
RAJAT : 1203/40 | 40 | 30 | 28 | 2Sn | 640-700 | 690 | 9.1 | 430 | - | AG20 | Bag-28 | L Ag40Sn | AG105 |
RAJAT : 1203/40 | 40 | 58 | 2Ni | - | - | - | - | - | - | - | - | - | |
RAJAT : 1203/38 | 38 | 32 | 28 | 2Sn | 650-720 | 710 | 9.1 | 430 | - | - | Bag-34 | - | - |
RAJAT : 1200/35 | 35 | 32 | 33 | 680-750 | 740 | 9 | 450 | - | - | Bag-35 | - | - | |
RAJAT : 1200/34 | 34 | 36 | 27 | 3Sn | 630-730 | 710 | 9 | 450 | - | - | - | L Ag34Sn | AG106 |
RAJAT : 1200/30 | 30 | 38 | 32 | 680-765 | 750 | 8.9 | 400 | - | AG-16 | Bag-20 | L Ag30 | AG204 | |
RAJAT : 1200/30 | 30 | 36 | 32 | 2Sn | 650-750 | 740 | 8.8 | 440 | - | AG-21 | - | L Ag30Sn | AG107 |
RAJAT : 1200/25 | 25 | 40 | 33 | 2Sn | 680-760680-76 | 750 | 8.7 | 420 | - | - | Bag-37 | L Ag255nL Ag255 | AG108 |
RAJAT : 1200/25 | 25 | 41 | 34 | 700-800 | 780 | 8.8 | 405 | - | AG17 | - | L Ag25 | AG205 | |
RAJAT : 1200/25 | 25 | 38 | 33 | 2Ni, 2Mn | 705-800 | 835 | 8.6 | - | - | - | Bag-26 | - | - |
RAJAT : 1200/20 | 20 | 44 | 35.9 | 0.1Si | 690-810 | 810 | 8.7 | 390 | - | - | - | L Ag20 | AG206 |
RAJAT : 1200/18 | 18 | 50 | 30 | 2.0 Sn | 720-790 | 790 | 8.4 | - | - | - | - | - | - |
RAJAT : 1105/16 | 16 | 48 | 36 | 790-830 | 820 | 8.6 | - | - | - | - | - | - | |
RAJAT : 1105/12 | 12 | 48 | 40 | 800-830 | 830 | 8.5 | 410 | - | - | - | L Ag 12 | AG207 | |
RAJAT : 1106/9 | 9 | 53 | 38 | 765-850 | 870 | 8.6 | - | BACuAg23 | - | - | - | - | |
RAJAT : 1106/7 | 7 | 85 | 8Sn | 665-958 | 1020 | 9.1 | - | - | - | - | - | - | |
RAJAT : 1104/5 | 5 | 55 | 39.9 | 0.1Si | 820-870 | 860 | 8.4 | 390 | - | - | - | L Ag5 | AG208 |
RAJAT : 1104/4 | 4 | 55 | 40.7 | 0.3 Sn | 860-890 | 900 | 8.4 | 370 | - | - | - | - | - |
RAJAT : 1103/2 | 2 | 55 | 42.9 | 0.1Si | 870-890 | 900 | 8.4 | 340 | - | - | - | - | - |
RAJAT : 1101/1 | 60 | 38.98 | 0.1Si | 890-900 | 900 | 8.3 | 350 | - | - | - | - | - |
Details :
Technical Details
Grade | Nominal Composition % | Melting Range | Operating Temp. | Density | Tensile Strength | International Standard | ||||||||
Ag | Cu | Zn | Cd | OthersOthers | oc | oc | g/cm3 | N/mm2 | IS 2927 | BS 1845 | AWS A5.8 | DIN 851 3 | DIN EN 1044 | |
RAJAT : 1205/50 | 50 | 15.5 | 16.5 | 18 | - | 620-640 | 640 | 9.5 | 420 | BACuAg 10 | Ag1 | BAg-1 a | L Ag50Cd | AG301 |
RAJAT : 1204/45 | 45 | 15 | 16 | 24 | - | 607-618 | 620 | 9.3 | 450 | BACuAg15 | - | Bag-1BAg- | - | AG302 |
RAJAT : 1204/43 | 43 | 16 | 20 | 21 | - | 616-620 | 620 | 9.1 | 400 | BACuAg 16A | - | - | - | - |
Raja!: 1204/42Raja!: 1204/4 | 42 | 17 | 16 | 25 | - | 610-620 | 610 | 9.1 | 390 | - | AG-2 | - | - | AG303 |
RAJAT : 1203/40 | 40 | 19 | 21 | 20 | - | 595-630 | 610 | 9.3 | 450 | - | AG-10 | - | L Ag40Cd | AG304 |
RAJAT : 1203/38 | 38 | 20 | 22 | 20 | - | 605-650 | 640 | 9.2 | 420 | BACuAg19 | AG-3 | - | - | - |
Raja!: 1201/35 | 35 | 26 | 21 | 18 | - | 610-700 | 700 | 9.1 | 420 | BACuAg20 | - | Bag-2 | - | AG35AG305 |
RAJAT : 1201/34 | 34 | 22 | 24 | 20 | - | 610-680 | 640 | 9.1 | 400 | - | AG11 | - | L Ag34Cd | - |
RAJAT : 1200/30 | 30 | 28 | 21 | 21 | - | 600-690 | 680 | 9.2 | 380 | BACuAg21 | AG12 | Bag-2a | L Ag30Cd | AG306 |
RAJAT : 1200/25AJAT : 1200/25 | 25 | 30 | 27 .527 .5 | 17.5 | - | 607-682 | 710 | 8.8 | 380 | - | - | Bag-33 | L Ag25Cd | AG307 |
RAJAT : 1200/25 | 25 | 35 | 26.5 | 13.5 | - | 605-745 | 745 | 9 | - | - | - | Bag-27 | - | - |
RAJAT : 1200/21RAJAT : 1200/2 | 21 | 35.5 | 26 .526 .5 | 16.5 | 0.5 Si | 610-750 | 720 | 8.6 | 380 | - | - | - | - | AG308 |
RAJAT : 1200/20 | 20 | 40 | 25 | 15 | - | 605-765 | 750 | 8.7 | 380 | - | - | - | L Ag20Cd | AG309 |
RAJAT : 1107/17 | 17 | 41 | 26 | 15 | - | 620-760 | 760 | 8.7 | 350 | - | - | - | - | - |
RAJAT : 1107/13 | 13 | 44 | 33 | 10 | - | 605-795 | 790 | 8.7 | 350 | - | - | - | - | - |
RAJAT : 1107/12 | 12 | 50 | 31 | 7 | - | 620-825 | 800 | 8.5 | 410 | - | - | - | L Ag12Cd | - |
Details :
Technical Details
Grade | Nominal Composition % | Melting Range | Operating Temp. | Density | Tensile Strength | International Standard | |||||||
Ag | Cu | P | Others | oc | oc | g/cm3 | N/mm2 | IS 2927 | BS 1845 | AWS A5.8 | DIN 851 3 | DIN EN 1044 | |
Rajat : 1200/18 | 18 | 75 | 7 | - | 645 | 650 | 8.4 | 250 | - | - | - | CP101 | |
Rajat : 1105/15 | 15 | 80 | 5 | - | 650-800 | 710 | 8.4 | BACuP-5 | CP1 | BcuP-5 | L-Ag15P | CP102 | |
Rajat : 1104/06 | 6 | 87 | 7 | - | 643-718 | 700 | 8.3 | 250 | - | BcuP-4 | - | ||
Rajat : 1104/05 | 5 | 89 | 6 | - | 650-810 | 710 | 8.2 | 250 | BACuP-4 | CP4 | BcuP-3 | L-Ag_5P | CP104 |
Rajat : 1103/2 | 2 | 91.5 | 6.5 | - | 650-810 | 710 | 8.1 | 250 | BACuP-3 | CP2 | BcuP-6 | L-Ag2P | CP105 |
Rajat : 1101/1 | 1 | 92.5 | 6.5 | - | 650-810 | 710 | 8.1 | 250 | - | - | |||
Rajat : 1100/0 | - | 92.7 | 7.3 | - | 710-820 | 720 | 8.1 | 250 | BACuP-2 | CP3 | BcuP-2 | L-CuP7 | CP102 |
Rajat : 1101/0 | - | 93.8 | 6.2 | - | 710-880 | 730 | 8.1 | 250 | BACuP-1 | CP6 | BcuP-1 | LcuP6 | CP103 |