At Harsh Steel Nickel Alloy 200/UNS N02200 is available in Nickel Alloy 200 wire, Nickel Alloy 200 Round bar, Nickel Alloy 200 Forged bar, Nickel Alloy 200 hex bar, Nickel Alloy 200 Flat bar, Nickel Alloy 200 Circles, Nickel Alloy 200 Ring, Nickel Alloy 200 Tube, Nickel Alloy 200 seamless Pipe, Nickel Alloy 200 Welded / ERW Pipe, Nickel Alloy 200 Sheet, Nickel Alloy 200 Plate, Nickel Alloy 200 Coil, Nickel Alloy 200 Flanges, Nickel Alloy 200 fasteners, Nickel Alloy 200 Socket weld Fittings, Nickel Alloy 200 ferrule fittings, Nickel Alloy 200 Buttweld fittings Like cap, elbow, tee, Reducer.
Nickel Alloy 200 and Nickel Alloy 201 is solid solution strengthened, in a commercial sense pure wrought materials together with good mechanized properties in excess of a variety of temperature ranges and superb level of resistance to a lot of corrosives, specifically hydroxides. Nickel Alloy 201 ended up being a modification of 200 to overpower carbon and (. 02 max) which keeps this coming from becoming embrittled through intergranular precipitates at temperature ranges of 600° F to 1400° F in lots of procedures. Normally, your essential constraints of both equally, nickel 200 and nickel 201, are usually blended into just one, dual-certified chemistry resulting providing a one metal while using desired attributes of both equally precious metals, Nickel Alloy 200/201.
Nickel Alloy 200 and 201 deliver corrosion amount of resistance within lowering and simple advertising together with within oxidizing atmospheres provided that the actual oxidizing advertising makes it possible for the actual formation of a passive oxide film. This oxide film makes up about the actual components exceptional amount of resistance within caustic environments. Deterioration prices within both equally marine and rural atmospheres are incredibly low. The amount of resistance connected with Nickel Alloy 200 and 201 to be able to corrosion by distilled and normal seas is very useful. And yes it likewise offers exceptional support within going sea water actually at excessive pace, but in at standstill as well as very low-velocity sea water severe local episode may occur beneath fouling microorganisms as well as different remains. Within warm water devices in which the water is made up of fractional carbon and atmosphere using some size, corrosion prices will probably be at first excessive however will minimize eventually when conditions favor the actual formation of a protective film.
Nickel Alloy 200 is generally on a support at temps below 600° F. At increased temps Nickel Alloy 200 merchandise may have problems with graphitization which can result in severely compromised properties. Whenever functioning temps are hoped for to be able to exceed 600° F, carbon written content gets to be critical. The lower carbon written content connected with Nickel Alloy 201 tends to make the actual materials repellent to be able to graphitization and as a consequence fewer at the mercy of embrittlement. Nickel Alloy 200/201 are generally accepted with regard to structure connected with strain wrecks and elements beneath ASME Boiler and Pressure . Nickel Alloy 200 is usually accepted with regard to support up to 600° F though Nickel Alloy 201 is usually accepted with regard to support up to 1230° F. Reduction point is usually 2615-2635° F.

In what forms is Nickel Alloy 200/201 available at Harsh Steel?

• Nickel Alloy 200 Sheet
• Nickel Alloy 200 Plate
• Nickel Alloy 200 Bar
• Nickel Alloy 200 Pipe & Tube (welded & seamless)
• Nickel Alloy 200 Fittings (i.e. flanges, slip-ons, blinds, weld necks, lapjoints, long welding necks, socket welds, elbows, tees, stub-ends, returns, caps, crosses, reducers, and pipe nipples)
• Nickel Alloy 200 Wire

What are the characteristics of Nickel Alloy 200/201?Highly resistant to various reducing chemicals

• Excellent resistance to caustic alkalies
• High electrical conductivity
• Excellent corrosion resistance to distilled and natural waters
• Resistance to neutral and alkaline salt solutions
• Excellent resistance to dry fluorine
• Widely used to handle caustic soda
• Good thermal, electrical and magnetostrictive properties
• Offers some resistance to hydrochloric and sulfuric acids at modest temperatures and concentrations

At Harsh Steel Nickel Alloy 201 (UNS N02201) is available in Nickel Alloy 201 wire, Nickel Alloy 201 Round bar, Nickel Alloy 201 Forged bar, Nickel Alloy 201 hex bar, Nickel Alloy 201 Flat bar, Nickel Alloy 201 Circles, Nickel Alloy 201 Ring, Nickel Alloy 201 Tube, Nickel Alloy 201 seamless Pipe, Nickel Alloy 201 Welded / ERW Pipe, Nickel Alloy 201 Sheet, Nickel Alloy 201 Plate, Nickel Alloy 201 Coil, Nickel Alloy 201 Flanges, Nickel Alloy 201 fasteners, Nickel Alloy 201 Socket weld Fittings, Nickel Alloy 201 ferrule fittings, Nickel Alloy 201 Buttweld fittings Like cap, elbow, tee, Reducer.
Nickel Alloy 200 and Nickel Alloy 201 are solid solution strengthened, commercially pure wrought materials with good mechanical properties over a wide range of temperatures and excellent resistance to many corrosives, in particular hydroxides. Nickel Alloy 201 was a modification of 200 to control carbon (.02 max) which keeps it from being embrittled by intergranular precipitates at temperatures of 600° F to 1400° F in many processes. Typically, the elemental restrictions of both, nickel 200 and nickel 201, are combined into one, dual-certified chemistry resulting in a single alloy with the desired characteristics of both alloys, Nickel Alloy 200/201.
Nickel Alloy 200 and 201 deliver corrosion amount of resistance within lowering and simple advertising together with within oxidizing atmospheres provided that the actual oxidizing advertising makes it possible for the actual formation of a passive oxide film. This oxide film makes up about the actual components exceptional amount of resistance within caustic environments. Deterioration prices within both equally marine and rural atmospheres are incredibly low. The amount of resistance connected with Nickel Alloy 200 and 201 to be able to corrosion by distilled and normal seas is very useful. And yes it likewise offers exceptional support within going sea water actually at excessive pace, but in at standstill as well as very low-velocity sea water severe local episode may occur beneath fouling microorganisms as well as different remains. Within warm water devices in which the water is made up of fractional carbon and atmosphere using some size, corrosion prices will probably be at first excessive however will minimize eventually when conditions favor the actual formation of a protective film.
Nickel Alloy 200 hundred is generally on a support at temps below 600° F. At increased temps Nickel Alloy 200 hundred merchandise may have problems with graphitization which can result in severely compromised properties. Whenever functioning temps are hoped for to be able to exceed 600° F, carbon written content gets to be critical. The lower carbon written content connected with Nickel Alloy 201 tends to make the actual materials repellent to be able to graphitization and as a consequence fewer at the mercy of embrittlement. Nickel Alloy 200/201 are generally accepted with regard to structure connected with strain wrecks and elements beneath ASME Boiler and Pressure . Nickel Alloy 200 is usually accepted with regard to support up to 600° F though Nickel Alloy 201 is usually accepted with regard to support up to 1230° F. Reduction point is usually 2615-2635° F.
Nickel Alloy-201 (UNS N02201) is a commercially pure wrought nickel, with good mechanical properties and an excellent resistance to many corrosives. Nickel Alloy 201 has low carbon (0.02% max) for applications over 315°C it is mainly used for food processing equipment, chemical shipping drums, caustic handling equipment and piping, electronic parts, aerospace and missile components, rocket motor cases, magnetostrictive devices.

In what forms is Nickel Alloy 200/201 available at Harsh Steel?

• Nickel Alloy 201 Sheet
• Nickel Alloy 201 Plate
• Nickel Alloy 201 Bar
• Nickel Alloy 201 Pipe & Tube (welded & seamless)
• Nickel Alloy 201 Fittings (i.e. flanges, slip-ons, blinds, weld-necks, lapjoints, long welding necks, socket welds, elbows, tees, stub-ends, returns, caps, crosses, reducers, and pipe nipples)
• Nickel Alloy 201 Wire

What are the characteristics of Nickel Alloy 200/201?

• Highly resistant to various reducing chemicals
• Excellent resistance to caustic alkalies
• High electrical conductivity
• Excellent corrosion resistance to distilled and natural waters
• Resistance to neutral and alkaline salt solutions
• Excellent resistance to dry fluorine
• Widely used to handle caustic soda
• Good thermal, electrical and magnetostrictive properties
• Offers some resistance to hydrochloric and sulfuric acids at modest temperatures and concentrations

Physical Properties AMS 4640

Melting Point - Liquidus - 1930 F

Melting Point - Solidus - 1895 F

Density - 0.274 lb/in3 at 68 F

Specific Gravity - 7.58

Electrical Resistivity - 116.0 ohms-cmil/ft @ 68 F

Electrical Conductivity - 7 %IACS @ 68 F

Thermal Conductivity - 22.6 Btu · ft/(hr · ft2·oF)at 68F

Coefficient of Thermal Expansion - 9.0 ·10-6 per oF (68-572 F)

Specific Heat Capacity - 0.09 Btu/lb/oF at 68 F

Modulus of Elasticity in Tension - 7500 ksi

Modulus of Rigidity - 6400 ksi

Machinability Rating -30%

Specifications

Similar Specifications

ASTM B-150, B-124, B-171, B-283

CA105

SAE J463

QQ-C-465

DELTA CA18

DELTA CA21

CW307G

AU10N

NF L14-705

Werkstoff 2.0966

DIN 17672

GAM MM11 CuAl9Ni5Fe2

GAM MM13 CuAl9Ni5Fe4

ISO 428 

NFA 51-116

NES 833

NC4

UNS C63000

AMS 4640 Aluminium Bronze Bar, Drawn and Stress releived (HR50) or Temper Annealed (TQ50)

Harsh Steel export Copper AMS 4640 to below countries.

Harsh steel is a major stockist and Exporter of Copper AMS 4640 to many countries of the world such as Singapore, Brisbane, Sydney, Melbourne, Australia, Houston, TX, San Diego, San Francisco, Atlanta, USA, Brentford, United Kingdom, Phoenix, Ireland, New Zealand and Canada, Western Australia , Queensland, New South Wales, South Australia, Victoria, Australian Capital Territory, Tasmania, Northern Territory, Ontario, British Columbia, Yukon Territory, Alberta, Manitoba, Saskatchewan, New foundland, Prince Edward Island, New Brunswick, Nova Scotia, Eastern Cape, Gauteng, Kwazulu-Natal, Western Cape, England, Scotland, Wales, Northern Ireland, Lagos, Abuja Capital Territory, Vadodara, Mumbai, Chennai, New Delhi, Mahape, Gurgaon, Noida, Bangalore, Coimbatore, Cochin, Ash Sharqiyah, Ar Riyad, Makkah, Dhahran, Riyadh, Jiddah, Jeddah, Masqat, Kwazulu-Natal, Gauteng, Western Cape, Free State, Eastern Cape, Alberta, Saskatchewan, British Columbia, Newfoundland, New Brunswick, Manitoba, Ontario, Nova Scotia, Quebec, Calgary, Edmonton, Vancouver, Toronto, Birmingham, Brentford, Manchester, Bristol, Sheffield, Milton Keynes, London, Poplar, Edinburgh, Thames Ditton.

CA104 is wrought high strength aluminium bronze, the commonly most used bronze in the market in the UK. Used for its high strength and excellent corrosion resistance to sea water and other aggressive environments aluminium bronze BS2874 CA104 has good wear and abrasive resistance the ability to withstand shock loading.

• Aluminium is the main alloying metal added to copper in contrast to standard bronze (copper/tin)• Higher strength and corrosion resistance compared to other bronzes• Resistance to corrosion in seawater• Material reacts with atmospheric oxygen to create a tough layer of aluminium oxide• Commonly used in the marine sector, oil and petrochemical industries (non sparking environments)• Used in the manufacture of valves and fasteners