Gunjan Paints Limited

Kalol, Gandhinagar, Gujarat

:

This is an acrylic aliphatic coating provide  a durable finish for chemical and coastal environment. It has excellent colour and gloss retention properties, good abrasion resistance and UV resistance.

:

Chemicals & Fertilizer Industries, Petrochemical Complexes, Refineries, Bulk Storage Tanks, Plants Equipments, Structures etc.

Maintenance Coating, Mild Steel, Stainless Steel, GI, Aluminium, Plastics, ABS, FRP, Wood, Acrylics, Polystyrene Polycarbonates, Cement, Concrete, etc. Hygienic Wall Coating. Original Equipment Coating

:

Two pack, cured with aliphatic polyisocyanate

:

3 : 1 ( Base: Hardener) By volume

:

30 Minutes

:

2 – 3 hrs

:

Glossy / semi glossy/ matt

:

Any assorted shade

(THEORATICALLY)

:

10 – 12 Sq. Mt./ Ltr. per coat at 35 micron DFT

:

30 - 35 Microns per coat

:

Approx. 45%

:

Touch : 1 hr, Handle : 6-8 hrs., Hard : Overnight

:

Min. Overnight. Max - 6 days

:

Above 250C

:

Polyurethane Thinner

:

Brush, roller, Conventional or airless Spray

:

Surface should be clean, for free rust, grease, oil, moisture

and lose flakes. Sand blast mild steel substrate. Stir the contents before use. Mix base and hardener properly in the recommended ratio. Allow mixture to mature for 20 minutes before applying by brush or spray. Use if necessary recommended thinner. Primer surface should not be exposed to corrosive environment for a long time without application of finishing paints.

:

A Single pack high performance heat resistance alluminium paint based on silicone resin medium for protection of steel at elevated temperatures  between 400C-600C dry heat.

:

Furnace equipment, recation vessels, hot metal stacks, kilns ,flues ,exhaust systems ,hot pipes and similar areas exposed  to dry heat attack.

:

Single Pack

:

Bright Metallic

:

Aluminum

:

Moderate.

:

15-20 microns per coat

:

OVER NIGHT

:

After application of the final coat of lumeros HR Aluminium, allow the system to air dry for minium24 hrs. Under ambient conditions. The temperature is then to be gradually increased to the working temperature rang for obtaining optimum performance.

:

Above 25C

:

Brush, Spray

:

Surface should be clean, dry, and free from rust and loose flakes. Blast cleaning is recommended.

:

A two pack epoxy polyamide cured coating with good  performance in marine and industrial environments. Good resistance to water and mild chemicals.

:

For application on Structural Steel, Pipelines, etc. subjected to aggressive environment. Suitable for application on columns and structures of  fertilizer plants, chemical units .

:

Two pack, cured with polyamide.

:

Base : Catalyst : 3 : 1 by volume.

:

20 Minutes

:

5-6 hrs.

:

Glossy, Semi Glossy and Matt.

:

Grey or As per your requirement.

(THEORATICALLY)

:

9 - 11 Sq.Mt/Ltr.

:

30 - 40 microns per coat

:

APPROX 37 %

:

Touch – 1 hr.  Hard – Overnight

:

Min. Overnight

:

Above 250C

:

EPOXY Thinner

:

Brush and Spray

:

Surface should be clean, free rust, grease, oil, moisture and lose flakes.

Stir the contents before use. Mix base and hardener properly in the recommend ratio. Allow mixture to mature for 20 minutes before applying by brush or spray.

Use  necessary recommend thinner if required.