Our Products
Mortar
1 Products availableLeading Manufacturer, Supplier & Retailer of Fire Bricks, Silica Insulation Bricks, Kyanite Insulation Bricks, Insulation Bricks and alumina bricks.
Specifications
Properties | DR | DR |
---|---|---|
B.D. (Gm/cc) Max. | 1.2 | 1 |
CCS (Kg/cm2) Min. | 80 | 15 |
A.P. (%) Min. | 55 | 65 |
T.C.at 600oHF Temp. (Kcal/m/hr/oC) Max. | 0.4 | 0.25 |
PLC (%) for 5 hrs. Max. | 1.5 at 1200oC | 1.5 at 1100oC |
SWT (oC) Max. | 1350 | 1150 |
PCE (OC) Min. | 30 | - |
Al2O3 (%) Min. | 18 | 18 |
SiO2(%) Min. | 70 | 75 |
Fe2O3 (%) Max. | 2 | 2 |
Specifications
Brand Name | Al2O3 % min | Fe2O3 % max | A.P. % min | B.D. Gms/cc min | C.C.S. kg/cm2 min | P.C.E. Orton min | R.U.L. taoc | P.L.C. % max |
---|---|---|---|---|---|---|---|---|
DR | 30 | 2.20 | 25 | 1.90 | 250 | 31.00 | 1350 | ±1.5 at 1350Co/2Hrs |
DR | 40 | 2.50 | 23 | 2.10 | 350 | 32.00 | 1350 | ±1.0 at 1450Co/2Hrs |
DR | 45 | 2.60 | 21 | 2.20 | 370 | 32.00 | 1420 | ±1.5 at 1450Co/2Hrs |
DR | 50 | 2.75 | 23 | 2.30 | 400 | 32.00 | 1430 | ±1.5 at 1450Co/2Hrs |
DR | 55 | 2.90 | 23 | 2.40 | 400 | 33.00 | 1440 | ±1.5 at 1450Co/2Hrs |
DR | 60 | 3.00 | 23 | 2.55 | 430 | 34.00 | 1450 | ±1.5 at 1500Co/2Hrs |
DR | 65 | 3.00 | 23 | 2.60 | 450 | 34.50 | 1460 | ±2.0 at 1500Co/2Hrs |
DR | 70 | 3.20 | 23 | 2.65 | 500 | 35.00 | 1470 | ±2.0 at 1500Co/2Hrs |
DR | 80 | 3.50 | 21 | 2.75 | 600 | 37.00 | 1500 | ±2.5 at 1500Co/2Hrs |
Specifications
Properties | DR500 | DR600 | DR700 |
---|---|---|---|
B.D. (Gm/cc) Max. | 0.53 | 0.63 | 0.63 |
CCS (Kg/cm2) Min. | 7 | 9 | 12 |
A.P. (%) Min. | 80 | 75 | 72 |
T.C. at 600?HF Temp. (Kcal/m/hr/oC) Max | 0.14 | 0.16 | 0.18 |
PLC (%) for 5 hrs. Max. | 1.5 at 950oC | 1.5 at 1000oC | 1.5 at 1000oC |
SWT (?C) Max. | 1000 | 1000 | 1050 |
Specifications
Properties | DRCFI |
---|---|
B.D. (Gm/cc) Max. | 0.8 |
CCS (Kg/cm2) Min. | 15 |
A.P. (%) Min. | 70 |
T.C.at 600oF Temp. (Kcal/m/hr/oC) Max. | 0.19 |
PLC (%) for 5 hrs., Max. | 1.5 at 1000oC |
SWT (?C) Max. | 1050 |
PCE (OC) Min. | - |
Al2O3 (%) Min. | 28 |
SiO2(%) Min. | 60 |
Fe2O3 (%) Max. | 2 |