| Product | Setting | Grading (mm) | AI2O3(%min) | Application |
|---|---|---|---|---|
| Crown-70K | Air | 0 - 0.2 | 70 | Jointing Mortar For Plate & Nozzle |
| Crown-95K | Air | 0 - 0.2 | 90 | Jointing Mortar For Plate & Nozzle |
| Crown-95H | Air | 0 - 4 | 94 | Ramming Mass For Fixing Well Block |
We manufacture and supply high quality Whytheat A 90% Alumina Dense Castable. These are generally used to form strong joints and are applied extensively in building material, metallurgy, and petrochemical industries.Our Castables are very cost effective.
Additional Information:
Packaging Details : 25 kg bags
Technical Specification
| General Properties | |
|---|---|
| Max.Service Temperature | 1700. c |
| Maximum Grain Size | 5mm |
| Water Required For Casting | 8.10-10.0% |
| Chemical Analysis % | Typical Value |
| AI2o3 | 85 - 90 |
| Fe2o3 | 0.8 - 1.5 |
| Cao | 5.5 - 06.5 |
| Physical Properties | |
| Bulk Density | g/cc |
| Afer Drying At 110c/24 Hrs | 2.65 - 2.80 |
| CCS, kg/cm2 After Drying AT 110.C/24hrs | 600 - 700 |
| After Heating At 1100. C/3 hrs | 300 - 400 |
| After Heating At 1550. C/3 hrs | 650 - 800 |
| % Retained On max. Size | 0 - 5 |
| Thermal Properties | |
| Refractoriness, Orton / .C | 0.02 |
| PLC% | |
| After heating at 1100.C/3 hrs | -0.40 to + 0.20 |
| After heating at 1550.C/3 hrs | -1.00 to 2.50 |
| Packaging | 25 kg bags |
| Storage life | 6 months |
| Delivery state | dry |
We are engaged in providing high quality Firecrete (Super) 70% Alumina Castable to our clients. These catables are useful for forming strong joints and is used extensively in building material, metallurgy and petrochemical industries.
Technical Specification
| Product Type | Firecrete (Super) |
|---|---|
| Nature Of Bond | Hydraulic |
| Installation | Vibrations Casting |
| General Properties | |
| Max.Service Temperature | 1450. c |
| Maximum Grain Size | 5mm |
| Water Required For Casting | 10-11% |
| Chemical Analysis % | Typical Value |
| AI2o3 | 70.2 |
| Fe2o3 | 5.1 |
| Cao | 5.45 |
| Physical Properties | |
| Bulk Density | g/cc |
| Afer Drying At 110c/24 Hrs | 2.25 |
| CCS, kg/cm2 After Drying AT 110.C/24hrs | 380 |
| After Heating At 1100. C/3 hrs | 250 |
| After Heating At 1550. C/3 hrs | 430 |
| % Retained On Max. Size | 0.8 |
We offer Whytheat K 60% Alumina Dense Castable, which has an alumina content of 60% can be used for service temperatures upto 1600ºC. This castable also has a low iron content and can resist carbon monoxide attack. It can be used in various industries like: blast furnaces, foundries, boiler industry stoker arches, soak pit covers, forge furnaces, tunnel kilns, heat treatment furnace car tops as well as electro - phosphorus furnaces.
Technical Specification
| General Properties | |
|---|---|
| Max.Service Temperature | 1600. c |
| Maximum Grain Size | 5mm |
| Water Required For Casting | 10.6-11.8 |
| Chemical Analysis % | Typical Value |
| AI2o3 | 56 - 60 |
| Fe2o3 | 1.00 - 1.25 |
| Cao | 4.00 - 4.70 |
| Physical Properties | |
| Bulk Density | g/cc |
| Afer Drying At 110c/24 Hrs | 2.15 - 2.25 |
| CCS, kg/cm2 After Drying AT 110.C/24hrs | 350 - 430 |
| After Heating At 1100. C/3 hrs | 180 - 280 |
| After Heating At 1550. C/3 hrs | 350 - 500 |
| % Retained On max. Size | 0 - 5 |
| Thermal Properties | |
| Refractoriness, Orton / .C | 0.018419489 |
| PLC% | - |
| After heating at 1100.C/3 hrs | -0.40 to + 0.20 |
| After heating at 1550.C/3 hrs | -1.20 to 2.40 |
| Packaging | 25 kg bags |
| Storage life | 6 months |
| Delivery state | Dry |