1 Products availableWe are leaders in the market for providing best range of High Impact Resistance White PP Copolymer (CPM2150), High Impact Resistance White PP Copolymer (CPM2200), High Melt Flow White PP Copolymer (PPM 2400), High Melt Flow Natural PP Copolymer (PPN 2400) and Unfilled Natural PP Copolymer (CPN2800)
CPM2150 is white granules recommended for use in Injection Molding processes where high impact strength is required and ideal material to use in manufacturing of air coolers, household items, furniture and electronic items.
Storage RecommendationsBags should be stored in dry / closed conditions at temperatures below 50°C and protected from UV / direct sunlight
PackagingStandard polymer bag with size of 25 Kgs each.
Typical Specification
| Properties | Test Method | Unit | Typical Values |
|---|---|---|---|
| Melt Flow Rate (230°C/2.16 kg) | ASTM D1238 | Gms/10min | 9 – 10 |
| Tensile Strength at Yield (50mm/min) | ASTM D638 | Kgs/cm² | 190-230 |
| Elongation at Yield (50mm/min) | ASTM D638 | % | 10 – 15 |
| Flexural Modulus | ASTM D790 | Kgs/cm² | 10000-12000 |
| Notched Izod Impact Strength(23°C) | ASTM D256 | Kgs.cm/cm | 15-17 |
| Ash Content (650°C) | ASTM D-5630 | % | Less than 2 |
CPM2200 is white granules recommended for use in Injection Molding processes where high impact strength is required and ideal material to use in manufacturing of air coolers, household items, furniture and electronic items.
Storage RecommendationsBags should be stored in dry / closed conditions at temperatures below 50°C and protected from UV / direct sunlight
PackagingStandard polymer bag with size of 25 Kgs each.
Typical Specification
| Properties | Test Method | Unit | Typical Values |
|---|---|---|---|
| Melt Flow Rate (230°C/2.16 kg) | ASTM D1238 | Gms/10min | 9 – 10 |
| Tensile Strength at Yield (50mm/min) | ASTM D638 | Kgs/cm² | 180-320 |
| Elongation at Yield (50mm/min) | ASTM D638 | % | 10 – 15 |
| Flexural Modulus | ASTM D790 | Kgs/cm² | 9500-11500 |
| Notched Izod Impact Strength(23°C) | ASTM D256 | Kgs.cm/cm | 20-23 |
| Ash Content (650°C) | ASTM D-5630 | % | Less than 2 |
PPM2400 is a white granules recommended for use in Injection Molding processes where high melt flow polymers are required. It is an ideal material to use in manufacturing of electronic items and industrial polymer compounds.
Storage RecommendationsBags should be stored in dry / closed conditions at temperatures below 50°C and protected from UV / direct sunlight
PackagingStandard polymer bag with size of 25 Kgs each.
Typical Specification
| Properties | Test Method | Unit | Typical Values |
|---|---|---|---|
| Melt Flow Rate (230°C/2.16 kg) | ASTM D1238 | Gms/10min | 35-45 |
| Tensile Strength at Yield (50mm/min) | ASTM D638 | Kgs/cm² | 210-250 |
| Elongation at Yield (50mm/min) | ASTM D638 | % | 10 – 15 |
| Flexural Modulus | ASTM D790 | Kgs/cm² | 13000-15000 |
| Notched Izod Impact Strength(23°C) | ASTM D256 | Kgs.cm/cm | 6 – 7 |
| Ash Content (650°C) | ASTM D-5630 | % | Less than 2 |
PPN2400 is a natural granules recommended for use in Injection Molding processes where high melt flow polymers are required. It is an ideal material to use in manufacturing of automotive components and industrial polymer compounds.
Storage RecommendationsBags should be stored in dry / closed conditions at temperatures below 50°C and protected from UV / direct sunlight
PackagingStandard polymer bag with size of 25 Kgs each.
Typical Specification
| Properties | Test Method | Unit | Typical Values |
|---|---|---|---|
| Melt Flow Rate (230°C/2.16 kg) | ASTM D1238 | Gms/10min | 35-45 |
| Tensile Strength at Yield (50mm/min) | ASTM D638 | Kgs/cm² | 210-250 |
| Elongation at Yield (50mm/min) | ASTM D638 | % | 10 – 15 |
| Flexural Modulus | ASTM D790 | Kgs/cm² | 13000-15000 |
| Notched Izod Impact Strength(23°C) | ASTM D256 | Kgs.cm/cm | 3 – 4 |
| Ash Content (650°C) | ASTM D-5630 | % | Less than 2 |
CPN2800 is natural granules recommended for use in Injection Molding processes where high impact strength is required and ideal material to use in manufacturing of electronic items and industrial polymer compounds.
Storage RecommendationsBags should be stored in dry / closed conditions at temperatures below 50°C and protected from UV / direct sunlight
PackagingStandard polymer bag with size of 25 Kgs each.
Typical Specification
| Properties | Test Method | Unit | Typical Values |
|---|---|---|---|
| Melt Flow Rate (230°C/2.16 kg) | ASTM D1238 | Gms/10min | 10 – 12 |
| Tensile Strength at Yield (50mm/min) | ASTM D638 | Kgs/cm² | 210-250 |
| Elongation at Yield (50mm/min) | ASTM D638 | % | 10 – 15 |
| Flexural Modulus | ASTM D790 | Kgs/cm² | 10000-12000 |
| Notched Izod Impact Strength(23°C) | ASTM D256 | Kgs.cm/cm | 8 – 10 |
| Ash Content (650°C) | ASTM D-5630 | % | Less than 2 |
CPB1020 is a black granules recommended for use in Injection Molding processes where high impact strength is required. It is an ideal material to use in manufacturing of automotive components and industrial polymer compounds.
Storage RecommendationsBags should be stored in dry / closed conditions at temperatures below 50°C and protected from UV / direct sunlight
PackagingStandard polymer bag with size of 25 Kgs each.
Typical Specification
| Properties | Test Method | Unit | Typical Values |
|---|---|---|---|
| Melt Flow Rate (230°C/2.16 kg) | ASTM D1238 | Gms/10min | 15-17 |
| Tensile Strength at Yield (50mm/min) | ASTM D638 | Kgs/cm² | 140-160 |
| Elongation at Yield (50mm/min) | ASTM D638 | % | 9 – 11 |
| Flexural Modulus | ASTM D790 | Kgs/cm² | 9400-9850 |
| Notched Izod Impact Strength(23°C) | ASTM D256 | Kgs.cm/cm | 20-23 |
| Ash Content (650°C) | ASTM D-5630 | % | 10 – 12 |
CPB2100 is a black granules recommended for use in Injection Molding processes where high impact strength is required. It is an ideal material to use in manufacturing of industrial polymer compounds, electronic items, automotive components and furniture.
Storage RecommendationsBags should be stored in dry / closed conditions at temperatures below 50°C and protected from UV / direct sunlight
PackagingStandard polymer bag with size of 25 Kgs each.
Typical Specification
| Properties | Test Method | Unit | Typical Values |
|---|---|---|---|
| Melt Flow Rate (230°C/2.16 kg) | ASTM D1238 | Gms/10min | 9 – 10 |
| Tensile Strength at Yield (50mm/min) | ASTM D638 | Kgs/cm² | 210-250 |
| Elongation at Yield (50mm/min) | ASTM D638 | % | 10 – 15 |
| Flexural Modulus | ASTM D790 | Kgs/cm² | 13000-15000 |
| Notched Izod Impact Strength(23°C) | ASTM D256 | Kgs.cm/cm | 10 – 12 |
| Ash Content (650°C) | ASTM D-5630 | % | Less than 2 |
CPB2150 is a black granules recommended for use in Injection Molding processes where high impact strength is required. It is an ideal material to use in manufacturing of plastic safety gear products, speed breakers, industrial polymer compounds, electronic items and automotive components.
Storage RecommendationsBags should be stored in dry / closed conditions at temperatures below 50°C and protected from UV / direct sunlight
PackagingStandard polymer bag with size of 25 Kgs each.
Typical Specification
| Properties | Test Method | Unit | Typical Values |
|---|---|---|---|
| Melt Flow Rate (230°C/2.16 kg) | ASTM D1238 | Gms/10min | 8 – 10 |
| Tensile Strength at Yield (50mm/min) | ASTM D638 | Kgs/cm² | 200-240 |
| Elongation at Yield (50mm/min) | ASTM D638 | % | 10 – 15 |
| Flexural Modulus | ASTM D790 | Kgs/cm² | 12500-14000 |
| Notched Izod Impact Strength(23°C) | ASTM D256 | Kgs.cm/cm | 15-17 |
| Ash Content (650°C) | ASTM D-5630 | % | Less than 2 |
CPB2200 is a black granules recommended for use in Injection Molding processes where high impact strength is required. It is an ideal material to use in manufacturing of plastic safety gear products, helmets, speed breakers, industrial polymer compounds, electronic items and automotive components.
Storage RecommendationsBags should be stored in dry / closed conditions at temperatures below 50°C and protected from UV / direct sunlight
PackagingStandard polymer bag with size of 25 Kgs each.
Typical Specification
| Properties | Test Method | Unit | Typical Values |
|---|---|---|---|
| Melt Flow Rate (230°C/2.16 kg) | ASTM D1238 | Gms/10min | 8 – 10 |
| Tensile Strength at Yield (50mm/min) | ASTM D638 | Kgs/cm² | 190-230 |
| Elongation at Yield (50mm/min) | ASTM D638 | % | 10 – 15 |
| Flexural Modulus | ASTM D790 | Kgs/cm² | 10500-12000 |
| Notched Izod Impact Strength(23°C) | ASTM D256 | Kgs.cm/cm | 20-24 |
| Ash Content (650°C) | ASTM D-5630 | % | Less than 2 |
CPB4800 is a black granules recommended for use in Injection Molding processes where high impact strength is required. It is an ideal material to use in manufacturing of automotive components and industrial polymer compounds.
Storage RecommendationsBags should be stored in dry / closed conditions at temperatures below 50°C and protected from UV / direct sunlight
PackagingStandard polymer bag with size of 25 Kgs each.
Typical Specification
| Properties | Test Method | Unit | Typical Values |
|---|---|---|---|
| Melt Flow Rate (230°C/2.16 kg) | ASTM D1238 | Gms/10min | 8 – 10 |
| Tensile Strength at Yield (50mm/min) | ASTM D638 | Kgs/cm² | 210-250 |
| Elongation at Yield (50mm/min) | ASTM D638 | % | 10 – 15 |
| Flexural Modulus | ASTM D790 | Kgs/cm² | 13000-15000 |
| Notched Izod Impact Strength(23°C) | ASTM D256 | Kgs.cm/cm | 8 – 9 |
| Ash Content (650°C) | ASTM D-5630 | % | 4 – 5 |
CPB5100 is a black granules recommended for use in Injection Molding processes where high impact strength is required. It is an ideal material to use in manufacturing of automotive components, industrial polymer compounds, electronic items, and furniture.
Storage RecommendationsBags should be stored in dry / closed conditions at temperatures below 50°C and protected from UV / direct sunlight
PackagingStandard polymer bag with size of 25 Kgs each.
Typical Specification
| Properties | Test Method | Unit | Typical Values |
|---|---|---|---|
| Melt Flow Rate (230°C/2.16 kg) | ASTM D1238 | Gms/10min | 9 – 10 |
| Tensile Strength at Yield (50mm/min) | ASTM D638 | Kgs/cm² | 210-250 |
| Elongation at Yield (50mm/min) | ASTM D638 | % | 10 – 15 |
| Flexural Modulus | ASTM D790 | Kgs/cm² | 13000-15000 |
| Notched Izod Impact Strength(23°C) | ASTM D256 | Kgs.cm/cm | 10 – 12 |
| Ash Content (650°C) | ASTM D-5630 | % | 4 – 5 |
CPN2150 is natural granules recommended for use in Injection Molding processes where high impact strength is required and ideal material to use in manufacturing of electronic items and industrial polymer compounds.
Storage RecommendationsBags should be stored in dry / closed conditions at temperatures below 50°C and protected from UV / direct sunlight
PackagingStandard polymer bag with size of 25 Kgs each.
Typical Specification
| Properties | Test Method | Unit | Typical Values |
|---|---|---|---|
| Melt Flow Rate (230°C/2.16 kg) | ASTM D1238 | Gms/10min | 10 – 12 |
| Tensile Strength at Yield (50mm/min) | ASTM D638 | Kgs/cm² | 200-250 |
| Elongation at Yield (50mm/min) | ASTM D638 | % | 10 – 15 |
| Flexural Modulus | ASTM D790 | Kgs/cm² | 10000-12000 |
| Notched Izod Impact Strength(23°C) | ASTM D256 | Kgs.cm/cm | 15 – 17 |
| Ash Content (650°C) | ASTM D-5630 | % | Less than 2 |
Mr. Puneet Bansal & Rajesh Gupta (Avdha Plast Alloys Private Limited)
H-270, Sector-2, Industrial Area, DSIIDC, Bawana, Delhi - 110039
Share us via
View Contact Number 