Aluminium partition panel (APP) consists of two corrosion resistant aluminium sheets and a polyethylene core layer. The front and back aluminium sheet has same colour. Due to multiple colour options, elegant look and other features APP is very popular these days.
Advantages and characteristics
Application
ALSTROM fireproof aluminium composite panel is a new type of composite material cored with non-combustible mineral. It has excellent fire resistance as compared with traditional aluminum composite panel. Meanwhile, ALSTROM fireproof ACP conforms to German standard DIN4102 and ASTM E84-05 grade B-1. If you are searching for environmentally friendly building material that offers excellent fire resistance and minimal gas generation when burnt, please try ALSTROM fire resistant aluminum composite panel.
Fireproof aluminum composite panel advantages and characteristics
Applications
ALSTROM fireproof composite panel can be widely used in office buildings, Shopping centers, Industrial buildings, Airports, Hotels, Bus center, Hospitals, Schools, Supermarkets, Residential buildings
| Hardly flammable | DIN 4102,Part1 | Class B1 | |||
| Class B1 Fireproof ACP | ASTM E84-05 | Flame spread index | 5 | ||
| Smoke developed index | 0 | ||||
| Min. rest length of burning | GB/T 8625-88 | ≧0mm | 330mm | ||
| Average rest length of burning | GB/T 8625-88 | ≧150mm | 422mm | ||
| DIN 4102,Part1 | – | 370mm～480mm | |||
| Smoke temperature | GB/T 8625-88 | ≦200℃ | 187℃ | ||
| DIN 4102,Part1 | 123℃～160℃ | ||||
| Flame tip's height | GB/T 8625-88 | ﹤150mm | 15mm | ||
| Smoke density grade | GB/T 8627-1999 | ≦75 | 11 | ||
| DIN 4102,Part1 | ≦400%min | 10%-16%min | |||
| |
|||||
ALSTROM Nano-PVDF aluminium composite panel is anti-graffiti and self cleaning. It is composed of a polyethylene core sandwiched between two 0.5mm aluminum skins. Coming with hydrophobic and lipophobic surface, the Nano-PVDF ACP features good water and dirt resistance. The protected object stays clean much longer and can be easily cleaned with pure water.
The LOTUS EFFECT is the most distinguished characteristic of Nano-PVDF aluminium composite panel. The lotus leaf is never polluted by dirt although coming from silt. The same as lotus leaves, ALSTROM ACP has high water repellency and the dirt on its surface can be easily cleaned away by a heavy rain.
Why choose ALSTROM Nano PVDF composite panel?
ALSTROM get a patent for Nano-PVDF panel which has the following advantages.
Advantages and applications
Due to above characteristics, the Nano-PVDF aluminium composite panel is ideal for wall decoration and protection for office buildings, shopping centres, industrial buildings, airports, hotels, bus centres, hospitals, schools, supermarkets, and residential buildings, to name a few.
| Coating Type | NANO Coating | PVDF Coating |
| Paint Particle | 0.001micron-0.03micron | 0.3micron |
| Pollution Resistance | Dust hardly sticks on the panel | Dust sticks easily |
| Easy-cleaning | Dust goes away with bead | NIL |
| Friction Resistance | Over 10,000 times | Several thousands times |
| Acid Resistance | 5% HCI, 240 hrs | 24 hrs |
| Alkali Resistance | 5% NaOH, 240 hrs | 24 hrs |
| Oil Resistance | 20# machine oil, 240 hrs | 24 hrs |
| Weathering | Both paints have prominent feature of weather proofing and color retention. | |
ALSTROM PVDF aluminium composite panel consists of a polyethylene core sandwiched between two 0.5mm aluminium skins. As its name suggests, the ACP is coated with PVDF Kynar 500 / HYLAR 5000 fluorocarbon coating in order to provide a long lasting, durable finish.
PVDF aluminium composite panel advantages and characteristics
Application
ALSTROM PVDF aluminium composite panel is ideal to be used for office buildings, shopping centres, industrial buildings, airports, hotels, bus stations, hospitals, schools, supermarkets, and residential buildings.
| Thickness of coating | PVDF paint ≧25 um | 26um to 28um |
| Coating Flexibility (T-bend) | PVDF paint≦2T | 2T |
| Coating Adhesion | ≧1 grade for 10*10mm2 gridding test | 1 grade |
| Pencil Hardness | ≧HB | HB |
| Resist Solvent | No change for 200 times (MEK) | No change |
| Chemical Resistance | 5%HCL or 5%NAOH-No change for 24hours | No change |
| Boiling Water Resistance | coating no tear off for 2 hours boiling | no tear off |
| Color difference | △E≦2.0(follow color sample) | 0.5 |
| Panel Peeling Strength | 7 N/mm for 4mm panel with 0.5mm aluminium. skin | 7N/mm |
| Impact Test for paint | 50Kg.cm impact--paint no split for panel | no split |
| Abrasion Resistance(L/Mil) | ASTM D968 | 44 |
| Chemical Resistance | ASTM D1308 | Appearance: No change |
| Film Adhesion | ASTM D3359(Note 1) | 5B |
| Detergent Resistance(3%) | ASTM D2248 | Appearance: No change |
| Stripping Strength(kgf/inch) | ASTM D903 | 18.5 |
| Humidity Resistance (3000hrs,100%RH,100°F) | ASTM D2247 | Appearance: No change |
| Salt Spray Resistance (3000hrs,5% salt) | ASTM B117 | Appearance: No change |
ALSTROM brush aluminium composite panel comes with special treated aluminium sheets. The surface of the aluminium skin is coating brush and anodized brush.
Made using high quality aluminium composite panel production lines , ALSTROM brush ACP is presented long warranty and reliable performance, but also offered at competitive prices.
|
Aluminum Alloy |
AA1100 series |
|
Aluminum skin |
0.15x0.15mm; 0.21x0.21mm; 0.30x0.30mm; 0.50x0.50mm |
|
Thickness |
3mm /4mm |
|
Width |
1220mm |
|
Length |
2440mm, 3050mm, 3660mm |
|
Surface finishing |
Improved Polyester brush paint |
Mirror aluminium composite panel is a new type of aluminium composite material skinned with anodized aluminium mirror sheets. The bottom aluminium skin is chromate treated and polyester coated.
| Aluminum alloy | AA1100 series |
| Aluminum skin | 0.30x0.30mm; 0.40x0.40mm |
| Thickness | 3mm / 4mm |
| Width | 1220mm |
| Length | 2440mm |
| Surface finishing | Mirror finish |
| Color | Silver & Gold |
Polyester aluminium composite panel refers to ACP coated with polyester coatings. As a leading aluminium composite panel supplier, ALSTROM is supplying ACP with double side polyester coated, and ACP with one side coated with polyester and the other with service coating or mill finish.
Advantages and characteristics
Application
| 2mm | 3mm | 4mm | ||
| Panel weight(kg/m2) | 2.9 | 3.8 | 4.8 | |
| Aluminium sheet thickness(mm) | 0.3 | 0.3 | 0.3 | |
| Panel thickness tolerance(mm) | +/-0.2 | |||
| Panel width tolerance(mm) | +/-2 | |||
| Panel length tolerance(mm) | +/-3 | |||
| Panel diagonal tolerance(mm) | +/-5 | |||
| Aluminium sheet thickness tolerance(mm) | +/-0.02 | |||
| Paint thickness(Micron) | 21-23 | |||
| Paint pencil hardness | > HB | |||
| Paint toughness | 3T | |||
| Impact strength (kg.cm) | 50 | |||
| Temperature resistance | -50℃ to + 90℃ | |||
| Peel strength(180°) | > 5 Newton/mm | |||
| Boiling water resistance | 2 hours without change | |||
| Acid resistance | Immersed surface in 2% HCI for 24 hours, without change | |||
| Alkali resistance | Immersed surface in 2% Ca(OH)2 for 24 hours, without change | |||
| Solvent resistance | 100 times with Dimethylbenzene without change | |||
| Cleaning resistance | Over 100 times without change | |||
| Expansion coefficient(100°K temperature difference) | 2.4 mm/m | |
||