Our Complete range of products are Electrodes for Cutting And Gouging, Electrodes for Cast Iron, Electrodes for Creep Resisting Steel, Electrodes for Galvanising and Electrodes for Hardfacing.
Aarya Elect rodes have a wide range of MMAW products for various type of welding.
| Description/Application | WELDINGPARAMETERS(AC/DC+ ) | ||
| Size(mm) | Amp | ||
| AARYACUT | Aarya CUT an very special red iron oxide based electrode designed for smooth cutting of metal in all positions. The special coating withstands at high currents without overheating. A arc force renders it possible to cut all metals. When using the electrode hold it at an angle of 45 to the weld job.Closer the arc, the faster and cleaner the cut. Keep the electrode continuously in motion holding it firmly against the surface of the metal. | 3.15X350 | 150-180 |
| 4.00X450 | 190-240 | ||
| 5.00X450 | 250-300 | ||
Aarya Elect rodes have a wide range of MMAW products for various type of welding.
| TypicalWeldMetalChemistry | TypicalMechanicalProperties | Description/Application | WELDINGPARAMETERS(AC/DC+ ) | |||||||
| Size(mm) | Amp | |||||||||
| AARYA NICI | AWS:ENiFeCI | C | : | 1.50 | Hardness | : | 190VPN | Aarya NICI AC/DC (+) graphite coated allpositioning electrodes electrode depositing weldmetal which contains nickel and iron. Ideally suitedfor cast iron to steel welding and repair of varietiesof cast irons. The weld deposit has superior bondstrength and shows greater tolerance to impurities inthe cast irons. Welds are easily machinable. | 2.50 X 350 | 70-90 |
| Mn | : | 1.30 | 3.15X350 | 100-130 | ||||||
| Si | : | 0.35 | 4.00X350 | 140-180 | ||||||
| Ni | : | 52.0 | 5.00X350 | 190-220 | ||||||
| Fe | : | Balance | ||||||||
| AARYA CI | AWS:ENiCI | C | : | 1.50 | Hardness | : | 170 VPN | Aarya CI an AC/DC (+) type electrode produceda soft and stable arc with low currents. Theelectrode deposits a soft, crack free and soundweld on grey cast iron. Welds can be machinedeasily.Surfacing of the above materials, cast machineryparts engine blocks, bearing blocks, frames, foundrycastings, etc. | 2.50 X 350 | 70-90 |
| Mn | : | 1.30 | 3.15X350 | 100-130 | ||||||
| Si | : | 0.35 | 4.00X350 | 140-180 | ||||||
| Cr | : | 1.25 | 5.00X350 | 190-220 | ||||||
| Ni | : | Balance | ||||||||
| Fe | 4.50 |
Aarya Elect rodes have a wide range of MMAW products for various type of welding.
| TypicalWeldMetalChemistry | TypicalMechanicalProperties | Description/Application | WELDINGPARAMETERS(AC/DC+ ) | |||||||
| Size(mm) | Amp | |||||||||
| AARYA 18 A1 | AWS:E7018-A1 | C | : | 0.065 | UTS(MPa) | : | 570 | Aarya-18A1 is basic coated, low hydrogen, iron powder type electrode producing a weldmetal which contains 0.50% Mo. The weldmetal displays good creep strength atelevated temperatures upto 475C. Theelectrode operates in all conventionalpositions depositing welds of radiographicquality. | 2.50 X 350 | 70-100 |
| Mn | : | 0.75 | ELONGATION | : | 26% | 3.15X350 | 100-140 | |||
| Si | : | 0.48 | 4.00X450 | 140-180 | ||||||
| Mo | : | 0.51 | 5.00X450 | 180-220 | ||||||
| S | : | 0.013 | ||||||||
| AARYA 8018B2 | AWS:E8018 B2 | C | : | 0.066 | UTS(MPa) | : | 605 | Aarya-8018B2 is a basic coated, lowhydrogen electrode producing weld metalcontaining 1.25% Cr and 0.50% Mo. Theweld metal shows goods elevatedtemperature strength upto 525 C. Theelectrode is easy to operate in all positionsand produces X-ray quality welds. | 2.50 X 350 | 70-100 |
| Mn | : | 0.76 | ELONGATION | : | 22% | 3.15X350/450 | 110-150 | |||
| Si | : | 0.44 | 4.00X450 | 140-180 | ||||||
| Cr | : | 1.25 | 5.00X450 | 190-240 | ||||||
| Mo | : | 0.50 | ||||||||
| S | 0.015 |
| AARYA 9018B3 | AWS:E9018 B3 | C | : | 0.066 | UTS(MPa) | : | 625 | Aarya-9018B3 is a basic, low hydrogen typeelectrode operating in all positions. Theelectrode produces weld metal containing2.25% Cr and 1% Mo and is suitable forwelding creep resisting steels of evencomposition for service at elevatedtemperatures as upto 575 C. Welds are ofradiographic quality. | 2.50X350 | 70-100 |
| Mn | : | 0.76 | ELONGATION | : | 19% | 3.15X450 | 100-140 | |||
| Si | : | 0.44 | 4.00X450 | 140-180 | ||||||
| Cr | : | 2.25 | 5.00X450 | 190-240 | ||||||
| Mo | : | 1.02 | ||||||||
| S | 0.016 |
| AARYA 7013 A1 | AWS:E7013 A1 | C | : | 0.065 | UTS(MPa) | : | 517 | A medium coated, all position, rutile typeelectrode depositing weld metal whichcontains 0.50% Mo. The electrodedisplays all the pleasing weldingcharacteristics of a rutile type, mediumcoated electrode. Suitable for welding oftubes and pipes in oil refinery and thermalprojects where high temperature strengthis necessary. Welds are of radiographicquality. | 2.50X350 | 70-100 |
| Mn | : | 0.75 | ELONGATION | : | 27% | 3.15X350/450 | 100-140 | |||
| Si | : | 0.48 | 4.00X450 | 140-180 | ||||||
| Mo | : | 0.51 | 5.00X450 | 190-240 | ||||||
| S | 0.013 |
Aarya Elect rodes have a wide range of MMAW products for various type of welding.
| TypicalWeldMetalChemistry | TypicalMechanicalProperties | Description/Application | WELDINGPARAMETERS(AC/DC+ ) | |||||||
| Size(mm) | Amp | |||||||||
| AARYA 45 | C | : | 0.048 | UTS(MPa) | : | 400 | Aarya NICI AC/DC (+) graphite coated allpositioning electrodes electrode depositing weldmetal which contains nickel and iron. Ideally suitedfor cast iron to steel welding and repair of varietiesof cast irons. The weld deposit has superior bondstrength and shows greater tolerance to impurities inthe cast irons. Welds are easily machinable. | 3.15X450 | 110-145 | |
| Mn | : | 0.22 | ELONGATION | : | 28% | 4.00X450 | 150-180 | |||
| Si | : | 0.05 | 5.00X450 | 190-230 | ||||||
Aarya Elect rodes have a wide range of MMAW products for various type of welding.
| TypicalWeldMetalChemistry | TypicalMechanicalProperties | Description/Application | WELDINGPARAMETERS(AC/DC+ ) | |||||||
| Size(mm) | Amp | |||||||||
| AARYA 250 HF | C | : | 0.22 | Hardness | : | 200 250BHN | Aarya 250 is a medium coated rutile typehardfacing electrode operating on AC/DC(-)depositing an air hardening weldmetal which hashigh degree of toughness and excellent resistance torolling sliding friction and heavy impact load.The weld deposit is machinable. | 3.15X350/450 | 110-145 | |
| Mn | : | 0.45 | 4.00X450 | 150-180 | ||||||
| Si | : | 0.37 | 5.00X450 | 190-230 | ||||||
| Cr | : | 1.90 | ||||||||
| AARYA 350 HF | C | : | 0.18 | Hardness | : | 350 450BHN | Aarya 350 A medium heavy coated, rutile typeelectrode depositing weld metal having hardness withrange of 350 450 BHN. The electrode is easy tooperate displaying pleasing welding characteristics.The weld deposit is machinable. | 3.15X350/450 | 110-145 | |
| Mn | : | 0.55 | 4.00X450 | 150-180 | ||||||
| Si | : | 0.40 | 5.00X450 | 190-230 | ||||||
| Cr | 2.50 | |||||||||
| AARYA 550 HF | C | : | 0.2.0 | Hardness | : | 500 550BHN | Aarya -550 HF is a basic coated AC-DC typeelectrodes specially designed for hardfacingapplications. Weld metal gives appx. 500-550 BHNhardness. The welds are non-machinable and airhardening type Carbon Chromium alloy which hasexcellent resistance to severe abrasion. Typicalapplication welding of crusher jaws, xcavater teeth, scraper blades etc. | 3.15X350 /450 | 110-145 | |
| Mn | : | 1.30 | 4.00X450 | 150-180 | ||||||
| Si | : | 0.90 | 5.00X450 | 190-230 | ||||||
| Cr | : | 3.50 | ||||||||
| AARYA 550 HF | C | : | 0.75 | Hardness As welded | : | 200 250BHN | Aarya Mn is a basic coated, hard facing electrodespecially design for welding of austenitic manganesesteel weld metal containing 14% Mn. The weld metalgives work hardens under impact in service andproduced excellent resistance to wear by abrasionand impact. | 3.15X350 /450 | 110-145 | |
| Mn | : | 14.0 | 4.00X450 | 150-180 | ||||||
| Si | : | 0.65 | Work Hardening | : | 500 550BHN | 5.00X450 | 190-230 |
Aarya Elect rodes have a wide range of MMAW products for various type of welding.
| Typical Weld Metal Chemistry |
Typical Mechanical Properties |
Description / Application |
WELDING PARAMETERS (AC/DC+ ) |
|||||||
| Size(mm) | Amp | |||||||||
| AARYA 250 HF | C | : | 0.22 | Hardness | : | 200 – 250 BHN |
Aarya – 250 is a medium coated rutile type hardfacing electrode operating on AC/DC(-) depositing an air hardening weldmetal which has high degree of toughness and excellent resistance to rolling sliding friction and heavy impact load. The weld deposit is machinable. |
3.15X350/450 | 110-145 | |
| Mn | : | 0.45 | 4.00X450 | 150-180 | ||||||
| Si | : | 0.37 | 5.00X450 | 190-230 | ||||||
| Cr | : | 1.90 | ||||||||
| AARYA 350 HF | C | : | 0.18 | Hardness | : | 350 – 450 BHN |
Aarya – 350 A medium – heavy coated, rutile type electrode depositing weld metal having hardness with range of 350 – 450 BHN. The electrode is easy to operate displaying pleasing welding characteristics. The weld deposit is machinable. |
3.15X350/450 | 110-145 | |
| Mn | : | 0.55 | 4.00X450 | 150-180 | ||||||
| Si | : | 0.40 | 5.00X450 | 190-230 | ||||||
| Cr | 2.50 | |||||||||
| AARYA 550 HF | C | : | 0.2.0 | Hardness | : | 500 – 550 BHN |
Aarya -550 HF is a basic coated AC-DC type electrodes specially designed for hardfacing applications. Weld metal gives appx. 500-550 BHN hardness. The welds are non-machinable and air hardening type Carbon Chromium alloy which has excellent resistance to severe abrasion. Typical application welding of crusher jaws,xcavater teeth ,scraper blades etc. |
3.15X350 /450 | 110-145 | |
| Mn | : | 1.30 | 4.00X450 | 150-180 | ||||||
| Si | : | 0.90 | 5.00X450 | 190-230 | ||||||
| Cr | : | 3.50 | ||||||||
| AARYA 550 HF | C | : | 0.75 | Hardness As welded | : | 200 – 250BHN | Aarya – Mn is a basic coated, hard facing electrode specially design for welding of austenitic manganese steel weld metal containing 14% Mn. The weld metal gives work – hardens under impact in service and produced excellent resistance to wear by abrasion and impact. |
3.15X350 /450 | 110-145 | |
| Mn | : | 14.0 | 4.00X450 | 150-180 | ||||||
| Si | : | 0.65 | Work Hardening | : | 500 – 550BHN | 5.00X450 | 190-230 |
Aarya Elect rodes have a wide range of MMAW products for various type of welding.
| TypicalWeldMetalChemistry | TypicalMechanicalProperties | Description/Application | WELDINGPARAMETERS(AC/DC+ ) | |||||||
| Size(mm) | Amp | |||||||||
| AARYA 18 | AWS:7018IS : EB 5426H3JX | C | : | 0.075 | UTS(MPa) | : | 445 | Aarya 18 basic coated hydrogencontrolled type high yield electrodes.Thedeposition efficiency exceeds 115%.Weld deposit is tough and ductile havingradiographic quality weld metal. Typicalapplication include heavy earth movingstructure, Boiler welding, bridges, thermalpower station, pressure vessels etc. | 2.50 X 350 | 70-100 |
| Mn | : | 1.05 | YS(MPa) | : | 560 | 3.15X450 | 110-150 | |||
| Si | : | 0.45 | ELONGATION | : | 27% | 4.00X450 | 140-190 | |||
| S | : | 0.016 | IMPACT AT 30C | : | 50 J | 5.00X450 | 200-250 | |||
| P | : | 0.021 | ||||||||
| AARYA 16 | AWS:7016IS : EB5424H2JX | C | : | 0.072 | UTS(MPa) | : | 440 | AAarya 16 is a heavy coated iron powdertype hydrogen controlled electrodes.Thedeposited metal in highly resistance tocracking. Typical application include high tensilesteel, railway wagons and coaches, atomic reactor, bridges, highly restrainedjoint etc. | 2.50 X 350 | 70-100 |
| Mn | : | 1.10 | YS(MPa) | : | 555 | 3.15X450 | 110-150 | |||
| Si | : | 0.40 | ELONGATION | : | 28% | 4.00X450 | 140-190 | |||
| S | : | 0.018 | IMPACT AT 30C | : | 56J | 5.00X450 | 200-250 | |||
| P | : | 0.022 |
| AARYA 16 CS | AWS:7016IS : EB5424H2JX | C | : | 0.085 | UTS(MPa) | : | 450 | Aarya 16 CS is a heavy coated ironpowder type hydrogen controlledelectrodes. The deposited metal in highlyresistance to cracking. Typical application include high tensilesteel, railway wagons and coaches, atomic reactor, bridges, highly restrainedjoint etc. | 2.50 X 350 | 70-100 |
| Mn | : | 1.25 | YS(MPa) | : | 560 | 3.15X450 | 110-150 | |||
| Si | : | 0.50 | ELONGATION | : | 27% | 4.00X450 | 140-190 | |||
| S | : | 0.018 | IMPACT AT 30C | : | 54J | 5.00X450 | 200-250 | |||
| P | : | 0.022 |
| AARYA 18 Spl | AWS:7018-1IS : EB5426H3JX | C | : | 0.055 | UTS(MPa) | : | 460 | Aarya 18 Spl is a specially designed forvery high quality welding havingunmatched in welding performance andproperties. Weld metal producedradiographic quality. Suited for welding ofheavy and rigid structure, penstock, pumpand compressor, pressure vessels etc. | 2.50 X 350 | 80-100 |
| Mn | : | 1.30 | YS(MPa) | : | 580 | 3.15X450 | 110-145 | |||
| Si | : | 0.35 | ELONGATION | : | 25% | 4.00X450 | 150-180 | |||
| S | : | 0.016 | IMPACT AT 45C | : | 52J | 5.00X450 | 190-230 |
Aarya Elect rodes have a wide range of MMAW products for various type of welding.
| Typical Weld Metal Chemistry |
Typical Mechanical Properties |
Description / Application |
WELDING PARAMETERS (AC/DC+ ) |
|||||||
| Size(mm) | Amp | |||||||||
| AARYA 18 | AWS:7018 IS : EB 5426H3JX |
C | : | 0.075 | UTS(MPa) | : | 445 | Aarya – 18 basic coated hydrogen controlled type high yield electrodes.The deposition efficiency exceeds 115%. Weld deposit is tough and ductile having radiographic quality weld metal. Typical application include heavy earth moving structure, Boiler welding, bridges, thermal power station, pressure vessels etc. |
2.50 X 350 | 70-100 |
| Mn | : | 1.05 | YS(MPa) | : | 560 | 3.15X450 | 110-150 | |||
| Si | : | 0.45 | ELONGATION | : | 27% | 4.00X450 | 140-190 | |||
| S | : | 0.016 | IMPACT AT 30C | : | 50 J | 5.00X450 | 200-250 | |||
| P | : | 0.021 | ||||||||
| AARYA 16 | AWS:7016 IS : EB5424H2JX |
C | : | 0.072 | UTS(MPa) | : | 440 | AAarya – 16 is a heavy coated iron powder type hydrogen controlled electrodes.The deposited metal in highly resistance to cracking.
Typical application include high tensile |
2.50 X 350 | 70-100 |
| Mn | : | 1.10 | YS(MPa) | : | 555 | 3.15X450 | 110-150 | |||
| Si | : | 0.40 | ELONGATION | : | 28% | 4.00X450 | 140-190 | |||
| S | : | 0.018 | IMPACT AT 30C | : | 56J | 5.00X450 | 200-250 | |||
| P | : | 0.022 |
| AARYA 16 CS | AWS:7016 IS : EB5424H2JX |
C | : | 0.085 | UTS(MPa) | : | 450 | Aarya – 16 CS is a heavy coated iron powder type hydrogen controlled electrodes. The deposited metal in highly resistance to cracking.
Typical application include high tensile |
2.50 X 350 | 70-100 |
| Mn | : | 1.25 | YS(MPa) | : | 560 | 3.15X450 | 110-150 | |||
| Si | : | 0.50 | ELONGATION | : | 27% | 4.00X450 | 140-190 | |||
| S | : | 0.018 | IMPACT AT 30C | : | 54J | 5.00X450 | 200-250 | |||
| P | : | 0.022 |
| AARYA 18 Spl | AWS:7018-1 IS : EB5426H3JX |
C | : | 0.055 | UTS(MPa) | : | 460 | Aarya – 18 Spl is a specially designed for very high quality welding having unmatched in welding performance and properties. Weld metal produced radiographic quality. Suited for welding of heavy and rigid structure, penstock, pump and compressor, pressure vessels etc. |
2.50 X 350 | 80-100 |
| Mn | : | 1.30 | YS(MPa) | : | 580 | 3.15X450 | 110-145 | |||
| Si | : | 0.35 | ELONGATION | : | 25% | 4.00X450 | 150-180 | |||
| S | : | 0.016 | IMPACT AT 45C | : | 52J | 5.00X450 | 190-230 |
Aarya Elect rodes have a wide range of MMAW products for various type of welding.
| TypicalWeldMetalChemistry | TypicalMechanicalProperties | Description/Application | WELDINGPARAMETERS(AC/DC+ ) | |||||||
| Size(mm) | Amp | |||||||||
| AARYA 13 | AWS:6013IS : ER 4211 | C | : | 0.057 | UTS(MPa) | : | 400 | Aarya 13 is a general purposeall position rutile type electrodessuitable for welding of mild steeloperates on both AC/DC(+). Ideally suited for generalfabrication, storage tanks, steelfurniture, construction equipmentetc. | 2.50 X 350 | 70-90 |
| Mn | : | 0.45 | YS(MPa) | : | 510 | 3.15X350/450 | 100-130 | |||
| Si | : | 0.25 | ELONGATION | : | 26% | 4.00X450 | 140-180 | |||
| S | : | 0.016 | IMPACT AT 0C | : | 56 J | 5.00X450 | 190-220 | |||
| P | : | 0.019 | ||||||||
| AARYA 13 S | AWS:6013IS : ER 4222x | C | : | 0.055 | UTS(MPa) | : | 410 | Aarya -13 S is a medium coatedgeneral purpose all positioningelectrodes.The electrode ischaracterized by stable andsmooth arc, low spatter havinggood deslagging.Welds are radiographic quality.Ideally suited for welding of alltypes mild steel. | 2.50 X 350 | 70-100 |
| Mn | : | 0.48 | YS(MPa) | : | 520 | 3.15X350/450 | 100-140 | |||
| Si | : | 0.28 | ELONGATION | : | 25% | 4.00X450 | 130-190 | |||
| S | : | 0.015 | IMPACT AT 0C | : | 58J | 5.00X450 | 180-220 | |||
| P | : | 0.018 |
| AARYA 13 S | AWS:6013IS : ER 4222x | C | : | 0.057 | UTS(MPa) | : | 430 | Aarya -13 SS is a heavy coatedrutile type electrodes with lowspatter, stable arc having soundand radiographic quality weldmetal.Suitable for pressure vassals, railcoaches, heavy earthmovingequipments, boiler parts, shipbuilding etc. | 2.50 X 350 | 60-100 |
| Mn | : | 0.45 | YS(MPa) | : | 525 | 3.15X450 | 110-140 | |||
| Si | : | 0.25 | ELONGATION | : | 24% | 4.00X450 | 140-200 | |||
| S | : | 0.016 | IMPACT AT 0C | : | 62J | 5.00X450 | 190-230 |
Aarya Elect rodes have a wide range of MMAW products for various type of welding
| TypicalWeldMetalChemistry | TypicalMechanicalProperties | Description/Application | WELDINGPARAMETERS(AC/DC+ ) | |||||||
| Size(mm) | Amp | |||||||||
| AARYA 310 | AWS:E 310-16 | C | : | 0.084 | UTS(MPa) | : | 605 | Aarya 310 is a rutile basedspecial purpose 25% Cr 20%Ni type stainless steel electrode.The weld metal has resistance tocorrosion. Oxidation resistance issatisfactory upto 12000C. Thiselectrode ideally suited forwelding of AISI 310 and similarcomposition of metal. | 2.50 X 350 | 60-90 |
| Mn | : | 1.76 | ELONGATION | : | 34% | 3.15X350 | 80-120 | |||
| Si | : | 0.45 | 4.00X350 | 110-150 | ||||||
| Cr | : | 30.40 | 5.00X350 | 150-200 | ||||||
| Ni | : | 21.50 | ||||||||
| S | : | 0.014 | ||||||||
| AARYA 312 | AWS:E 312-16 | C | : | 0.090 | UTS(MPa) | : | 710 | Aarya 312 is a rutile basedsemi-basic type 30% Cr 10% Nitype stainless steel electrode.Electrodes Produced versatilehigh strength with crack freejoint in carbon steel, low alloysteel including difficult to weldsteels. Ideally suited for similarcomposition base metal. | 2.50 X 350 | 60-90 |
| Mn | : | 1.76 | ELONGATION | : | 38% | 3.15X350 | 80-120 | |||
| Si | : | 0.45 | 4.00X350 | 110-150 | ||||||
| Cr | : | 30.40 | 5.00X350 | 150-200 | ||||||
| Ni | : | 9.70 | ||||||||
| S | : | 0.015 |
| AARYA 307 | AWS:E 307-16 | C | : | 0.076 | UTS(MPa) | : | 680 | Aarya 307 is specially designedfor welding of austenitic steelsand austenitic manganese steels.It is a 18% Cr 9% Ni & 6% Mntype welding electrode ideallysuited for welding of heatresistance steel, dissimilarmaterials, for buffer layer etc. | 2.50 X 350 | 80-100 |
| Mn | : | 5.70 | ELONGATION | : | 36% | 3.15X350 | 110-145 | |||
| Si | : | 0.62 | 4.00X350 | 150-180 | ||||||
| Cr | : | 19.50 | 5.00X350 | 190-230 | ||||||
| Ni | : | 9.30 | ||||||||
| S | : | 0.018 |
Mr. VIBHOR JAIN (AARYA ELECTRODES PVT LTD)
Bungalow No.2, John's Mill No.3, Jeoni Mandi , , Agra, Uttar Pradesh, India
Share us via